Determining surface chemical composition of silver nanoparticles during sulfidation by monitoring the ligand shell.

ABSTRACT: Evaluating the surface and core compositions of transforming nanoparticles (NP) represents a significant measurement challenge but is necessary for predicting performance in applied systems and their toxicity in natural environments. Here, we use X-ray photoelectron spectroscopy (XPS) and attenuated total reflectance Fourier transform infrared (ATR-FTIR) spectroscopy to characterize both the surface and core ofpolyvinyl pyrollidone-silver nanoparticles in the presence of two Suwannee River fulvic acid (FA) standards and humic acid (HA) during sulfidation, the predominant transformation pathway in environmental systems. Only by using data from both spectroscopic methods was a clear relationship established between AgNP core composition and FA affinity established, where concomitant loss of FA was observed with Ag2S formation. Using XPS to measure AgNP surface composition, overlapping trends from XPS on FA I desorption from the AgNP surface as function of surface sulfidation were observed with FA II in the ATR-FTIR measurements. The reproducibility of the changing heterogeneous coating as a function of AgNP sulfidation provided a transferable method to determine the extent of Ag sulfidation without further need for the high resolution, high cost measurement tools that underpinned validation of the method. The relationship was not observed for HA, where a lower affinity to the AgNP surface was observed, suggesting distinct binding to the NP.

SUBMITTER: Pettibone JM

PROVIDER: S-EPMC6759992 | biostudies-literature | 2018

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Determining surface chemical composition of silver nanoparticles during sulfidation by monitoring the ligand shell.

Pettibone John M JM Gorham Justin M JM Liu Jingyu J

Journal of nanoparticle research : an interdisciplinary forum for nanoscale science and technology 20180101

Evaluating the surface and core compositions of transforming nanoparticles (NP) represents a significant measurement challenge but is necessary for predicting performance in applied systems and their toxicity in natural environments. Here, we use X-ray photoelectron spectroscopy (XPS) and attenuated total reflectance Fourier transform infrared (ATR-FTIR) spectroscopy to characterize both the surface and core ofpolyvinyl pyrollidone-silver nanoparticles in the presence of two Suwannee River fulvi ...[more]

PMID: 31555056

Similar Datasets

Project description:Understanding the structure transformation of engineered nanomaterials (ENMs) is a grand measurement challenge, which impacts many aspects of ENMs applications, such as their efficacy, safety, and environmental consequence. To address the significant knowledge gap regarding the fundamental kinetic rate and extent of ENM transformation in the environment, we present a comprehensive and mechanistic structural investigation of the transformation, aggregation, and dissolution behavior of a polyvinylpyrrolidone-coated silver nanoparticle (AgNP) suspension upon sulfidation in moderately reduced hard water with fulvic acid and dissolved Na2S. This reaction is among the most prevalent and industrially and environmentally relevant ENMs transformation. Using ex situ transmission electron microscopy (TEM) and both in situ and ex situ synchrotron-based small angle X-ray scattering (SAXS) and X-ray diffraction (XRD), we find that sulfidation of faceted AgNPs strongly depends on the crystallographic orientation of the facets, with nanometer-scale passivation layers developed on {111} and {100} facets and continuous nucleation and growth on {110} facets. Nanobeam electron diffraction and atomic resolution imaging show Ag and Ag2S domains both possess a high degree of crystalline order, contradicting amorphous structures as previously reported. In situ SAXS/XRD allowed simultaneous determination of the morphological changes and extent of sulfidation of AgNPs. SAXS/XRD results strongly indicate sulfidation follows first-order reaction kinetics without any aggregation. Aided by their size monodispersity, for the first time, using direct, in situ morphology and atomic-structure probes whose results mutually corroborate, we unequivocally determined the sulfidation rate constant of AgNPs under an environmentally relevant condition (~0.013 min-1 for 68 nm diameter AgNPs). A rigorous analysis of the long-term sulfidation product of the AgNPs under different S/Ag ratios using ex situ SAXS/XRD clearly demonstrates that the silver mass in the original AgNP and transformed Ag/Ag2S NP is preserved. This result has important environmental implications, strongly suggesting that Ag+ ions, a known highly effective antimicrobial agent, are not leached into the solution during sulfidation of AgNPs. The combined nondestructive methodology can be extended to unfold the structure transformation pathway and kinetics in a broad range of ENM systems.

Dataset Information

Determining surface chemical composition of silver nanoparticles during sulfidation by monitoring the ligand shell.

Publications

Determining surface chemical composition of silver nanoparticles during sulfidation by monitoring the ligand shell.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets