Effects of Al-Si Coating and Zn Coating on the Hydrogen Uptake and Embrittlement of Ultra-High Strength Press-Hardened Steel.

ABSTRACT: Press-hardened steel (PHS), used for automotive safety-related structure parts, is sensitive to hydrogen embrittlement due to its martensitic microstructure. Hydrogen is introduced in PHS during the hot press forming (HPF) process, by an atmospheric corrosion process. In this study, the hydrogen embrittlement behavior of uncoated, aluminized, and galvanized PHSs was investigated. The Al-10%Si coating promoted the absorption of diffusible hydrogen at elevated temperature during the HPF while the reacted coating layer prevented the absorbed hydrogen from out-diffusing through the reacted coating surface layer at room temperature. Therefore, the aluminized PHS showed a greater sensitivity to both the hydrogen uptake and the resultant embrittlement, as compared to the uncoated and galvanized PHSs. Use of galvanized PHS for HPF application reduces the risk of hydrogen embrittlement, since the Zn coating effectively prevents the hydrogen uptake. The greater embrittlement resistance of the galvanized PHS is possibly due to the inhibition of the hydrogen generation reaction by the surface ZnO oxide layer and the low rate of hydrogen transport through the liquid Zn phase.

SUBMITTER: Jo KR

PROVIDER: S-EPMC6774365 | biostudies-literature | 2019

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Effects of Al-Si Coating and Zn Coating on the Hydrogen Uptake and Embrittlement of Ultra-High Strength Press-Hardened Steel.

Jo Kyoung Rae KR Cho Lawrence L Sulistiyo Dimas H DH Seo Eun Jung EJ Kim Seong Woo SW De Cooman Bruno C BC

Surface & coatings technology 20190101

Press-hardened steel (PHS), used for automotive safety-related structure parts, is sensitive to hydrogen embrittlement due to its martensitic microstructure. Hydrogen is introduced in PHS during the hot press forming (HPF) process, by an atmospheric corrosion process. In this study, the hydrogen embrittlement behavior of uncoated, aluminized, and galvanized PHSs was investigated. The Al-10%Si coating promoted the absorption of diffusible hydrogen at elevated temperature during the HPF while the ...[more]

PMID: 31579346

Similar Datasets

Project description:In this study, we aimed to process the biomimetic function surface by designing a prototype for modeling the pits on a dung beetle body and the abdomen of a desert viper, and by using high speed milling and controlling the ratio of row spacing to feed rate. Firstly, we conducted three-dimensional parametric modeling and static analysis of the bionic functional surface using 3D modeling software UGNX (12.0, SIEMENS AG, Munich, Germany) and finite element analysis software ABAQUS (2018, Dassault, Providence, RI, USA). Then, the analysis results were imported into the fatigue life analysis software nCode (2018, HBM United Kingdom Ltd., South Yorkshire, UK) to simulate the fatigue characteristics of different bionic pit morphology models. Per the simulated tensile fatigue testing machine, the result shows that the minimum fatigue life value of the quadrilateral pit surface of the simulated dung beetle is one and four times higher than the hexagonal pit morphology and the irregular pit morphology, respectively, whereas the maximum fatigue damage is lower by one and five orders of magnitude, respectively. The quadrilateral pit surface on the biomimetic dung beetle body has better fatigue resistance, which can considerably improve the fatigue damage distribution state and the fatigue life of hardened steel die surfaces. The influential regulation of milling parameters on fatigue performance was studied and the results show that the fatigue resistance of the model is optimal when milling parameters are: row spacing of 0.4 mm, loading space of 0.2 mm, and milling depth of 0.3 mm. The quadrilateral dimensions formed by milling are highly similar to those of a dung beetle body proving that a certain reduction in milling process depth can increase the structural fatigue resistance. From the perspective of fatigue crack growth analysis, the quadrilateral dimples on the surface of the dung beetle improve fatigue crack growth inhibition and fatigue resistance.

Dataset Information

Effects of Al-Si Coating and Zn Coating on the Hydrogen Uptake and Embrittlement of Ultra-High Strength Press-Hardened Steel.

Publications

Effects of Al-Si Coating and Zn Coating on the Hydrogen Uptake and Embrittlement of Ultra-High Strength Press-Hardened Steel.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets