Altering spacer material affects bone regeneration in the Masquelet technique in a rat femoral defect.

ABSTRACT: The Masquelet technique depends on pre-development of a foreign-body membrane to support bone regeneration with grafts over three times larger than the traditional maximum. To date, the procedure has always used spacers made of bone cement, which is the polymer polymethyl methacrylate (PMMA), to induce the foreign-body membrane. This study sought to compare (i) morphology, factor expression, and cellularity in membranes formed by PMMA, titanium, and polyvinyl alcohol sponge (PVA) spacers in the Masquelet milieu and (ii) subsequent bone regeneration in the same groups. Ten-week-old, male Sprague-Dawley rats were given an externally stabilized, 6?mm femur defect, and a pre-made spacer of PMMA, titanium, or PVA was implanted. All animals were given 4 weeks to form a membrane, and those receiving an isograft were given 10 weeks post-implantation to union. All samples were scanned with microCT to measure phase 1 and phase 2 bone formation. Membrane samples were processed for histology to measure membrane morphology, cellularity, and expression of the factors BMP2, TGF?, VEGF, and IL6. PMMA and titanium spacers created almost identical membranes and phase 1 bone. PVA spacers were uniformly infiltrated with tissue and cells and did not form a distinct membrane. There were no quantitative differences in phase 2 bone formation. However, PMMA induced membranes supported functional union in 6 of 7 samples while a majority of titanium and PVA groups failed to achieve the same. Spacer material can alter the membrane enough to disrupt phase 2 bone formation. The membrane's role in bone regeneration is likely more than just as a physical barrier. © 2018 Orthopaedic Research Society. Published by Wiley Periodicals, Inc. J Orthop Res.

SUBMITTER: McBride-Gagyi S

PROVIDER: S-EPMC6785358 | biostudies-literature | 2018 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Altering spacer material affects bone regeneration in the Masquelet technique in a rat femoral defect.

McBride-Gagyi Sarah S Toth Zacharie Z Kim Daniel D Ip Victoria V Evans Emily E Watson John Tracy JT Nicolaou Daemeon D

Journal of orthopaedic research : official publication of the Orthopaedic Research Society 20180209

The Masquelet technique depends on pre-development of a foreign-body membrane to support bone regeneration with grafts over three times larger than the traditional maximum. To date, the procedure has always used spacers made of bone cement, which is the polymer polymethyl methacrylate (PMMA), to induce the foreign-body membrane. This study sought to compare (i) morphology, factor expression, and cellularity in membranes formed by PMMA, titanium, and polyvinyl alcohol sponge (PVA) spacers in the ...[more]

PMID: 29424019

Similar Datasets

Project description:BackgroundThe Masquelet-induced-membrane technique is a commonly used method for treating segmental bone defects. However, there are no established clinical standards for management of the induced membrane before grafting.Questions/purposesTwo clinically based theories were tested in a chronic caprine tibial defect model: (1) a textured spacer that increases the induced-membrane surface area will increase bone regeneration; and (2) surgical scraping to remove a thin tissue layer of the inner induced-membrane surface will enhance bone formation.MethodsThirty-two skeletally mature female goats were assigned to four groups: smooth spacer with or without membrane scraping and textured spacer with or without membrane scraping. During an initial surgical procedure (unilateral, left tibia), a defect was created excising bone (5 cm), periosteum (9 cm), and muscle (10 g). Segments initially were stabilized with an intramedullary rod and an antibiotic-impregnated polymethylmethacrylate spacer with a smooth or textured surface. Four weeks later, the spacer was removed and the induced-membrane was either scraped or left intact before bone grafting. Bone formation was assessed using micro-CT (total bone volume in 2.5-cm central defect region) as the primary outcome; radiographs and histologic analysis as secondary outcomes, with the reviewer blinded to the treatment groups of the samples being assessed 12 weeks after grafting. All statistical tests were performed using a linear mixed effects model approach.ResultsMicro-CT analysis showed greater bone formation in defects with scraped induced membrane (mean, 3034.5 mm3; median, 1928.0 mm3; quartile [Q]1-Q3, 273.3-2921.1 mm3) compared with defects with intact induced membrane (mean, 1709.5 mm3; median, 473.8 mm3; Q1-Q3, 132.2-1272.3 mm3; p = 0.034). There was no difference in bone formation between textured spacers (mean, 2405.5 mm3; median, 772.7 mm3; Q1-Q3, 195.9-2743.8 mm3) and smooth spacers (mean, 2473.2 mm3; median, 1143.6 mm3; Q1-Q3, 230.2-451.1 mm3; p = 0.917).ConclusionsScraping the induced-membrane surface to remove the innermost layer of the induced-membrane increased bone regeneration. A textured spacer that increased the induced-membrane surface area had no effect on bone regeneration.Clinical relevanceScraping the induced membrane during the second stage of the Masquelet technique may be a rapid and simple means of improving healing of segmental bone defects, which needs to be confirmed clinically.

Dataset Information

Altering spacer material affects bone regeneration in the Masquelet technique in a rat femoral defect.

Publications

Altering spacer material affects bone regeneration in the Masquelet technique in a rat femoral defect.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets