Measurement of the hysteretic thermal properties of W-doped and undoped nanocrystalline powders of VO2.

ABSTRACT: Hysteresis loops exhibited by the thermal properties of undoped and 0.8?at.% W-doped nanocrystalline powders of VO2 synthesized by means of the solution combustion method and compacted in pellets, are experimentally measured by photothermal radiometry. It is shown that: (i) the W doping reduces both the hysteresis loops of VO2 and its transition temperature up to 15?°C. (ii) The thermal diffusivity decreases (increases) until (after) the metallic domains become dominant in the VO2 insulating matrix, such that its variation across the metal-insulation transition is enhanced by 23.5% with W-0.8?at.% doping. By contrast, thermal conductivity (thermal effusivity) increases up to 45% (40%) as the metallic phase emerges in the VO2 structure due to the insulator-to-metal transition, and it enhances up to 11% (25%) in the insulator state when the local rutile phase is induced by the tungsten doping. (iii) The characteristic peak of the VO2 specific heat capacity is observed in both heating and cooling processes, such that the phase transition of the 0.8?at.% W-doped sample requires about 24% less thermal energy than the undoped one. (iv) The impact of the W doping on the four above-mentioned thermal properties of VO2 mainly shows up in its insulator phase, as a result of the distortion of the local lattice induced by the electrons of tungsten. W doping at 0.8?at.% thus enhances the VO2 capability to transport heat but diminishes its thermal switching efficiency.

SUBMITTER: Gomez-Heredia CL

PROVIDER: S-EPMC6789116 | biostudies-literature | 2019 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Measurement of the hysteretic thermal properties of W-doped and undoped nanocrystalline powders of VO2.

Gomez-Heredia C L CL Ramirez-Rincon J A JA Bhardwaj D D Rajasekar P P Tadeo I J IJ Cervantes-Lopez J L JL Ordonez-Miranda J J Ares O O Umarji A M AM Drevillon J J Joulain K K Ezzahri Y Y Alvarado-Gil J J JJ

Scientific reports 20191011 1

Hysteresis loops exhibited by the thermal properties of undoped and 0.8 at.% W-doped nanocrystalline powders of VO2 synthesized by means of the solution combustion method and compacted in pellets, are experimentally measured by photothermal radiometry. It is shown that: (i) the W doping reduces both the hysteresis loops of VO2 and its transition temperature up to 15 °C. (ii) The thermal diffusivity decreases (increases) until (after) the metallic domains become dominant in ...[more]

PMID: 31604979

Similar Datasets

Project description:Oxide based dilute magnetic semiconductor materials have been of great interest over the years due to their potential use in spintronic devices. However, the variations in the magnetic behavior of the materials have raised concerns regarding the origin of ferromagnetic properties which still needs to be explored. Manipulation of magnetic behavior in oxide based dilute magnetic semiconductors has become a challenge due to the interplay of intrinsic defects present in the material. TiO2 nanocrystals have been studied largely due to their challenging optical and magnetic properties. The present investigation studies in detail the structural, morphological, optical and magnetic behavior of non-magnetic element (Cu and Zn) doped TiO2, synthesized via a simple sol-gel technique. X-ray diffraction patterns and Raman spectra confirm the anatase phase and high resolution transmission electron microscopic results clearly indicate the formation of highly crystalline nanocrystals in all the samples with particle size ranging from 5-15 nm. Energy dispersive X-ray fluorescence spectroscopic studies reveal the compositional homogeneity of all the investigated samples. The presence of functional groups and molecular interactions were identified by Fourier transform infrared spectroscopy. Optical properties were studied through UV-visible and photoluminescence spectroscopy from which a significant reduction in band gap in Cu-doped TiO2 nanocrystals was found. X-ray photoelectron spectra confirm the presence of Ti3+, Cu2+, Cu+ and Zn2+ in Cu and Zn-doped TiO2 samples. The concept of bound magnetic polarons associated with the vacancy defects at both Ti, Cu, Zn and oxygen sites is used to explain the induced weak ferromagnetic behavior in undoped, Cu and Zn-doped TiO2 at room temperature. The overlapping of bound magnetic polarons could be the source of ferromagnetism irrespective of the non-magnetic nature of the dopant ion. The concentration of bound magnetic polarons is estimated using a Langevin fit and a detailed understanding of the variation of defect mediated magnetic properties is established with the help of PL analysis. A significant reduction in bandgap along with enhanced magnetization observed in the Cu-doped TiO2 material makes it suitable as a potential candidate for spintronics and magneto-optics applications. Room temperature magnetic properties of the Zn doped sample show a diamagnetic tail which is explained based on the defect centers and oxidation states of dopant ions present in the sample which is further verified with the help of XPS results.

Dataset Information

Measurement of the hysteretic thermal properties of W-doped and undoped nanocrystalline powders of VO2.

Publications

Measurement of the hysteretic thermal properties of W-doped and undoped nanocrystalline powders of VO<sub>2</sub>.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets