Nanohydroxyapatite Reinforced Chitosan Composite Hydrogel with Tunable Mechanical and Biological Properties for Cartilage Regeneration.

ABSTRACT: With the continuous quest of developing hydrogel for cartilage regeneration with superior mechanobiological properties are still becoming a challenge. Chitosan (CS) hydrogels are the promising implant materials due to an analogous character of the soft tissue; however, their low mechanical strength and durability together with its lack of integrity with surrounding tissues hinder the load-bearing application. This can be solved by developing a composite chitosan hydrogel reinforced with Hydroxyapatite Nanorods (HANr). The objective of this work is to develop and characterize (physically, chemically, mechanically and biologically) the composite hydrogels loaded with different concentration of hydroxyapatite nanorod. The concentration of hydroxyapatite in the composite hydrogel was optimized and it was found that, reinforcement modifies the hydrogel network by promoting the secondary crosslinking. The compression strength could reach 1.62?±?0.02?MPa with a significant deformation of 32% and exhibits time-dependent, rapid self-recoverable and fatigue resistant behavior based on the cyclic loading-unloading compression test. The storage modulus value can reach nearly 10 kPa which is needed for the proposed application. Besides, composite hydrogels show an excellent antimicrobial activity against Escherichia coli, Staphylococcus aureus bacteria's and Candida albicans fungi and their cytocompatibility towards L929 mouse fibroblasts provide a potential pathway to developing a composite hydrogel for cartilage regeneration.

SUBMITTER: Kumar BYS

PROVIDER: S-EPMC6828803 | biostudies-literature | 2019 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Nanohydroxyapatite Reinforced Chitosan Composite Hydrogel with Tunable Mechanical and Biological Properties for Cartilage Regeneration.

Kumar B Y Santosh BYS Isloor Arun M AM Kumar G C Mohan GCM Inamuddin Asiri Abdullah M AM

Scientific reports 20191104 1

With the continuous quest of developing hydrogel for cartilage regeneration with superior mechanobiological properties are still becoming a challenge. Chitosan (CS) hydrogels are the promising implant materials due to an analogous character of the soft tissue; however, their low mechanical strength and durability together with its lack of integrity with surrounding tissues hinder the load-bearing application. This can be solved by developing a composite chitosan hydrogel reinforced with Hydroxya ...[more]

PMID: 31685836

Similar Datasets

Project description:BackgroundThe regeneration of lost/damaged support tissue in the periodontium, including the alveolar bone, periodontal ligament, and cementum, is an ambitious purpose of periodontal regenerative therapy and might effectively reduce periodontitis-caused tooth loss. Guided tissue regeneration (GTR) is a technique currently used in dentistry for periodontal surgery, which allows osseous regeneration prior to soft tissue migration into the area of interest. Calcium phosphate-based bone grafts (mostly Tricalcium Phosphate or Hydroxyapatite) are bio ceramics that show the greatest similarity to the mineral found in the bone. Thereby, giving calcium-phosphate excellent biocompatibility, biodegradability and osteoconductivity. The aim of the study is to fabricate hydroxyapatite reinforced polymeric hydrogel membrane for regeneration.Materials and methodPure alginate fabrication was done by cross linking sodium alginate with calcium chloride. Hydroxyapatite (HAP) alginate (Alg) was formulated by adding nanoparticles to the alginate mixture, which was then cross-linked with calcium chloride to formulate a HAP alginate polymeric membrane. The Fourier-transform infrared spectroscopy (FT-IR), Scanning Electron Microscope (SEM), and biocompatibility tests were performed to analyse the membrane characteristics.ResultsFabricated Hydroxyapatite- alginate (Hap- Alg) membrane has longer durability, because of strong crystal structure which in turn might take a longer time to regenerate. The membrane was found to be biocompatible and HAp induces faster mineralisation which in turn will increase the tissue regeneration rate of the membrane.ConclusionThe findings of our study suggests that the HAP-Alg hydro gel membrane is highly durable and hemocompatible and it has faster mineralisation capability thus making it superior from the clinically available membranes for GTR. Further analyses needs to be conducted to evaluate the potential of this membrane to be used for regeneration.

Project description:Articular cartilage has limited capacity for regeneration and when damaged cannot be repaired with currently available metallic or synthetic implants. We aim to bioengineer a microfibre-reinforced hydrogel that can capture the zonal depth-dependent mechanical properties of native cartilage, and simultaneously support neo-cartilage formation. With this goal, a sophisticated bi-layered microfibre architecture, combining a densely distributed crossed fibre mat (superficial tangential zone, STZ) and a uniform box structure (middle and deep zone, MDZ), was successfully manufactured via melt electrospinning and combined with a gelatin-methacrylamide hydrogel. The inclusion of a thin STZ layer greatly increased the composite construct's peak modulus under both incongruent (3.2-fold) and congruent (2.1-fold) loading, as compared to hydrogels reinforced with only a uniform MDZ structure. Notably, the stress relaxation response of the bi-layered composite construct was comparable to the tested native cartilage tissue. Furthermore, similar production of sulphated glycosaminoglycans and collagen II was observed for the novel composite constructs cultured under mechanical conditioning w/o TGF-ß1 supplementation and in static conditions w/TGF-ß1 supplementation, which confirmed the capability of the novel composite construct to support neo-cartilage formation upon mechanical stimulation. To conclude, these results are an important step towards the design and manufacture of biomechanically competent implants for cartilage regeneration. STATEMENT OF SIGNIFICANCE: Damage to articular cartilage results in severe pain and joint disfunction that cannot be treated with currently available implants. This study presents a sophisticated bioengineered bi-layered fibre reinforced cell-laden hydrogel that can approximate the functional mechanical properties of native cartilage. For the first time, the importance of incorporating a viable superficial tangential zone (STZ) - like structure to improve the load-bearing properties of bioengineered constructs, particularly when in-congruent surfaces are compressed, is demonstrated. The present work also provides new insights for the development of implants that are able to promote and guide new cartilaginous tissue formation upon physiologically relevant mechanical stimulation.

Dataset Information

Nanohydroxyapatite Reinforced Chitosan Composite Hydrogel with Tunable Mechanical and Biological Properties for Cartilage Regeneration.

Publications

Nanohydroxyapatite Reinforced Chitosan Composite Hydrogel with Tunable Mechanical and Biological Properties for Cartilage Regeneration.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets