A Novel Inherently Flame-Retardant Composite Based on Zinc Alginate/Nano-Cu2O.

ABSTRACT: A novel flame-retardant composite material based on zinc alginate (ZnAlg) and nano-cuprous oxide (Cu2O) was prepared through a simple, eco-friendly freeze-drying process and a sol-gel method. The composites were characterized and their combustion and flammability behavior were tested. The composites had high thermal stability and achieved nearly non-flammability with a limiting oxygen index (LOI) of 58. The results show remarkable improvement of flame-retardant properties in the ZnAlg/Cu2O composites, compared to ZnAlg. Furthermore, the pyrolysis behavior was determined by pyrolysis-gas chromatography-mass spectrometry (Py-GC-MS) and the flame-retardant mechanism was proposed based on the combined experimental results. The prepared composites show promising application prospects in building materials and the textile industry.

SUBMITTER: Xu P

PROVIDER: S-EPMC6835664 | biostudies-literature | 2019 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

A Novel Inherently Flame-Retardant Composite Based on Zinc Alginate/Nano-Cu<sub>2</sub>O.

Xu Peng P Shao Peiyuan P Zhang Qing Q Cheng Wen W Li Zichao Z Li Qun Q

Polymers 20190927 10

A novel flame-retardant composite material based on zinc alginate (ZnAlg) and nano-cuprous oxide (Cu<sub>2</sub>O) was prepared through a simple, eco-friendly freeze-drying process and a sol-gel method. The composites were characterized and their combustion and flammability behavior were tested. The composites had high thermal stability and achieved nearly non-flammability with a limiting oxygen index (LOI) of 58. The results show remarkable improvement of flame-retardant properties in the ZnAlg ...[more]

PMID: 31569681

Similar Datasets

Suppression of Smoldering of Calcium Alginate Flame-Retardant Paper by Flame-Retardant Polyamide-66.

Project description:Calcium alginate (Ca-Alg) fibers are renewable fibers obtained from the ocean with essential flame retardancy, which have recently been applied as components of flame-retardant paper. However, the application of Ca-Alg fibers is limited because of their tendency to smolder. Therefore, composites papers were fabricated by blending using flame-retardant polyamide-66 (FR-PA), with a 5 wt% content of phosphorous flame retardant, which will form molten carbon during combustion. When the FR-PA content is 30% of the composite paper, FR-PA forms a compact carbon layer on the surface of the Ca-Alg fibers during combustion, which isolates the mass/heat transfer and effectively suppresses the smoldering of Ca-Alg. This consists of a condensed flame retardant mechanism. Furthermore, the combustion and thermal degradation behavior of paper were analyzed by cone calorimetry (CONE), TG and TG-IR. Ca-Alg in the composite paper decomposed and released CO2 before ignition, which delayed the ignition time. Simultaneously, the FR-PA contained in the composite paper effectively inhibited the combustion of volatile combustibles in the gas phase. Overall, FR-PA and Ca-Alg improve the thermal stability of the composite paper in different temperature regions under air atmosphere. Ca-Alg reduces the formation of aromatic products and NH3 in the composite paper under N2 atmosphere. Ca-Alg-based paper with excellent flame retardancy was successfully prepared.

| S-EPMC7866267 | biostudies-literature

A Novel Self-Assembled Graphene-Based Flame Retardant: Synthesis and Flame Retardant Performance in PLA.

Project description:In this study, a novel flame retardant (PMrG) was developed by self-assembling melamine and phytic acid (PA) onto rGO, and then applying it to the improvement of the flame resistance of PLA. PMrG simultaneously decreases the peak heat release rate (pHRR) and the total heat release (THR) of the composite during combustion, and enhances the LOI value and the time to ignition (TTI), thus significantly improving the flame retardancy of the composite. The flame retardant mechanism of the PMrG is also investigated. On one hand, the dehydration of PA and the decomposition of melamine in PMrG generate non-flammable volatiles, such as H2O and NH3, which dilute the oxygen concentration around the combustion front of the composite. On the other hand, the rGO, melamine, and PA components in PMrG create a synergistic effect in promoting the formation of a compact char layer during the combustion, which plays a barrier role and effectively suppresses the release of heat and smoke. In addition, the PMrGs in PLA exert a positive effect on the crystallization of the PLA matrix, thus playing the role of nucleation agent.

| S-EPMC8659536 | biostudies-literature

In Situ Nanofibrillar Polypropylene-Based Composite Microcellular Foams with Enhanced Mechanical and Flame-Retardant Performances.

Project description:With the increasing demand for plastic components, the development of lightweight, high strength and functionalized polypropylene (PP) from a cost-effective and environmentally friendly process is critical for resource conservation. In situ fibrillation (INF) and supercritical CO2 (scCO2) foaming technology were combined in this work to fabricate PP foams. Polyethylene terephthalate (PET) and poly(diaryloxyphosphazene)(PDPP) particles were applied to fabricate in situ fibrillated PP/PET/PDPP composite foams with enhanced mechanical properties and favorable flame-retardant performance. The existence of PET nanofibrils with a diameter of 270 nm were uniformly dispersed in PP matrix and served multiple roles by tuning melt viscoelasticity for improving microcellular foaming behavior, enhancing crystallization of PP matrix and contributing to improving the uniformity of PDPP's dispersion in INF composite. Compared to pure PP foam, PP/PET(F)/PDPP foam exhibited refined cellular structures, thus the cell size of PP/PET(F)/PDPP foam was decreased from 69 to 23 μm, and the cell density increased from 5.4 × 106 to 1.8 × 108 cells/cm3. Furthermore, PP/PET(F)/PDPP foam showed remarkable mechanical properties, including a 975% increase in compressive stress, which was attributed to the physical entangled PET nanofibrils and refined cellular structure. Moreover, the presence of PET nanofibrils also improved the intrinsic flame-retardant nature of PDPP. The synergistical effect of the PET nanofibrillar network and low loading of PDPP additives inhibited the combustion process. These gathered advantages of PP/PET(F)/PDPP foam make it promising for lightweight, strong, and fire-retardant polymeric foams.

| S-EPMC10056583 | biostudies-literature

Sustainable, heat-resistant and flame-retardant cellulose-based composite separator for high-performance lithium ion battery.

Project description:A sustainable, heat-resistant and flame-retardant cellulose-based composite nonwoven has been successfully fabricated and explored its potential application for promising separator of high-performance lithium ion battery. It was demonstrated that this flame-retardant cellulose-based composite separator possessed good flame retardancy, superior heat tolerance and proper mechanical strength. As compared to the commercialized polypropylene (PP) separator, such composite separator presented improved electrolyte uptake, better interface stability and enhanced ionic conductivity. In addition, the lithium cobalt oxide (LiCoO2)/graphite cell using this composite separator exhibited better rate capability and cycling retention than that for PP separator owing to its facile ion transport and excellent interfacial compatibility. Furthermore, the lithium iron phosphate (LiFePO4)/lithium cell with such composite separator delivered stable cycling performance and thermal dimensional stability even at an elevated temperature of 120°C. All these fascinating characteristics would boost the application of this composite separator for high-performance lithium ion battery.

| S-EPMC3909895 | biostudies-literature

Bio-Based Bisbenzoxazines with Flame Retardant Linker.

Project description:This work explores the strategy of incorporating a highly substituted reactive flame retardant into a benzoxazine moiety. For this purpose, a DOPO-based flame retardant received a chain extension via reaction with ethylene carbonate. It was then reacted with phloretic acid to obtain a diphenol end-capped molecule, and further reacted with furfurylamine and paraformaldehyde to obtain a benzoxazine monomer via a Mannich-like ring closure reaction. This four-step synthesis yielded a partly bio-based halogen-free flame retardant benzoxazine monomer (DOPO-PA-fa). The successful synthesis was proven via NMR, IR and MS analysis. The polymerization behavior was monitored by DSC and rheological analysis both showing the polymerization starts at 200 °C to yield pDOPO-PA-fa. pDOPO-PA-fa has a significant thermal stability with a residual mass of 30% at 800 °C under ambient atmosphere. Furthermore, it reached a V-0 rating against small flames and an OI of 35%. Blended with other benzoxazines, it significantly improves their thermal stability and fire resistance. It emphasizes its potential as flame retardant agent.

| S-EPMC8707438 | biostudies-literature

Development of a Flame Retardant and an Organohalogen Flame Retardant Chemical Inventory

Project description:There have been many attempts to compile comprehensive lists of flame retardants. However, this goal has proven challenging due to the heterogeneity of compounds that can be used as flame retardants coupled with changes in formulation chemistry over time. Flame retardants have been the focus of many recent existing hazard, exposure, and risk assessments. These assessments have been class-based or for individual chemical substances. Here, diverse sets of publicly available data sources from governmental organizations and the open literature were compiled to develop an inventory of chemicals used as flame retardants and organohalogen flame retardants. The chemical substances from these data sources were mapped to appropriate chemical identifiers via manual curation and deduplicated. Despite different data sources containing a large number of overlapping chemical substances, compiling information from multiple data sources was found to increase the breadth of potential flame retardant chemistries. The flame retardant and organohalogen flame retardant inventories were developed as a resource for scientists interested in better understanding properties of flame retardant and organohalogen flame retardant classes. Measurement(s)chemical use informationTechnology Type(s)manual and automated literature collection

| S-EPMC9192637 | biostudies-literature

Influence of Zinc Oxide Nanoparticles and Char Forming Agent Polymer on Flame Retardancy of Intumescent Flame Retardant Coatings.

Project description:Zinc oxide nanoparticles (ZnO NPs) were synthesized by a precipitation method, and a new charring-foaming agent (CFA) N-ethanolamine triazine-piperazine, melamine polymer (ETPMP) was synthesized via nucleophilic substitution reaction by using cyanuric chloride, ethanolamine, piperazine, and melamine as precursor molecules. FTIR and energy-dispersive X-ray spectroscopy (EDS) studies were employed to characterize and confirm the synthesized ETPMP structure. New intumescent flame retardant epoxy coating compositions were prepared by adding ammonium polyphosphate (APP), ETPMP, and ZnO NPs into an epoxy resin. APP and ETPMP were fixed in a 2:1 w/w ratio and used as an intumescent flame-retardant (IFR) system. ZnO NPs were loaded as a synergistic agent in different amounts into the IFR coating system. The synergistic effects of ZnO NPs on IFR coatings were systematically evaluated by limited oxygen index (LOI) tests, vertical burning tests (UL-94 V), TGA, cone calorimeter tests, and SEM. The obtained results revealed that a small amount of ZnO NPs significantly increased the LOI values of the IFR coating and these coatings had a V-0 ratings in UL-94 V tests. From the TGA data, it is clear that the addition of ZnO NPs could change the thermal degradation behaviors of coatings with increasing char residue percentage at high temperatures. Cone calorimeter data reported that ZnO NPs could decrease the combustion parameters including peak heat release rates (PHRRs), and total heat release (THR) rates. The SEM results showed that ZnO NPs could enhance the strength and the compactness of the intumescent char, which restricted the flow of heat and oxygen.

| S-EPMC7022803 | biostudies-literature

Biorenewable Polyelectrolyte Nanocoating for Flame-Retardant Cotton-Based Paper.

Project description:Cotton-based raw paper, made of 100% cellulose, is used to make humidity-sensing, cottonid for bio-architecture applications. Despite its renewability and excellent mechanical properties, it is inherently flammable. In an effort to reduce its flammability, thin films of fully renewable and environmentally benign polyelectrolytes, chitosan (CH) and phytic acid (PA), were deposited on raw paper via layer-by-layer (LbL) assembly. Only four bilayers (BL) of the CH/PA coating are required to achieve self-extinguishing behavior, with a 69% reduction in peak heat release rate measured by microscale combustion calorimetry. These results demonstrate that this renewable intumescent LbL-assembled film provides an effective flame-retardant treatment for these environmentally friendly, climate-adaptive construction materials and could potentially be used to protect many cellulosic materials.

| S-EPMC9476518 | biostudies-literature

Synergistic Flame Retardant Effect of an Intumescent Flame Retardant Containing Boron and Magnesium Hydroxide.

Project description:In this study, to develop an organic/inorganic synergistic flame retardant and to reduce the dosage and cost of flame retardants, organic/inorganic synergistic flame retardants, hexakis(4-boronic acid-phenoxy)-cyclophosphazene (CP-6B), and magnesium hydroxide (MH) were chosen. The flame retardant properties of CP-6B/MH in epoxy resin (EP) were discussed. EP/CP-6B/MH had better flame retardancy and heat resistance compared with EP/CP-6B and EP/MH. A limiting oxygen index of EP/3.0%CP-6B/0.5%MH of 31.9% was achieved, and vertical burning V-0 rating was achieved. Compared with EP, the cone calorimeter dates of EP/CP-6B/MH decreased. CP-6B/MH inhibited combustion and did little to damage mechanical properties. Besides, the flame retardant mechanism was studied by scanning electron microscopy, energy-dispersive X-ray spectroscopy, X-ray diffraction, Fourier transform infrared spectroscopy, and pyrolysis-gas chromatography-mass spectrometry. CP-6B/MH exerted good synergistic effects.

| S-EPMC6648587 | biostudies-literature

A Novel Flame-Retardant, Smoke-Suppressing, and Superhydrophobic Transparent Bamboo.

Project description:Silica glass, known for its brittleness, weight, and non-biodegradable nature, faces challenges in finding suitable alternatives. Transparent wood, made by infusing polymers into wood, shows promise but is hindered by limited availability of wood in China and fire risks associated with its use. This study explores the potential of utilizing bamboo, which has a shorter growth cycle, as a valuable resource for developing flame-retardant, smoke-suppressing, and superhydrophobic transparent bamboo. A 3-layered flame-retardant barrier, composed of a top silane layer, an intermediate layer of SiO2 formed through hydrolysis-condensation of Na2SiO3 on the surface, and an inner layer of Na2SiO3, has been confirmed to be effective in reducing heat release, slowing flame spread, and inhibiting the release of combustible volatiles, toxic smoke, and CO. Compared to natural bamboo and other congeneric transparent products, the transparent bamboo displays remarkable superiority, with the majority of parameters being notably lower by an entire order of magnitude. It achieves a long ignition time of 116 s, low total heat release (0.7 MJ/m2), low total smoke production (0.063 m2), and low peak CO concentration (0.008 kg/kg). Moreover, when used as a substrate for perovskite solar cells, the transparent bamboo displays the potential to act as a light management layer, leading to a marked efficiency enhancement of 15.29%. The excellent features of transparent bamboo make it an enticing choice for future advancements in flame-retardant glasses and optical devices.

| S-EPMC10865110 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data