Anhydrous Phase B: Transmission Electron Microscope Characterization and Elastic Properties.

ABSTRACT: Anhydrous phase B and stishovite formed directly from olivine in experiments at 14 GPa and 1400 °CThe structure of anhydrous phase B is determined ab initio from precession electron diffraction tomography in transmission electron microscopyElastic and seismic properties of anhydrous phase B are calculated.

SUBMITTER: Addad A

PROVIDER: S-EPMC6853247 | biostudies-literature | 2019 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Anhydrous Phase B: Transmission Electron Microscope Characterization and Elastic Properties.

Addad A A Carrez P P Cordier P P Jacob D D Karato S-I SI Mohiuddin A A Mussi A A Nzogang B C BC Roussel P P Tommasi A A

Geochemistry, geophysics, geosystems : G(3) 20190814 8

Anhydrous phase B and stishovite formed directly from olivine in experiments at 14 GPa and 1400 °CThe structure of anhydrous phase B is determined ab initio from precession electron diffraction tomography in transmission electron microscopyElastic and seismic properties of anhydrous phase B are calculated. ...[more]

PMID: 31762710

Similar Datasets

Isotope analysis in the transmission electron microscope.

Project description:The Ångström-sized probe of the scanning transmission electron microscope can visualize and collect spectra from single atoms. This can unambiguously resolve the chemical structure of materials, but not their isotopic composition. Here we differentiate between two isotopes of the same element by quantifying how likely the energetic imaging electrons are to eject atoms. First, we measure the displacement probability in graphene grown from either 12C or 13C and describe the process using a quantum mechanical model of lattice vibrations coupled with density functional theory simulations. We then test our spatial resolution in a mixed sample by ejecting individual atoms from nanoscale areas spanning an interface region that is far from atomically sharp, mapping the isotope concentration with a precision better than 20%. Although we use a scanning instrument, our method may be applicable to any atomic resolution transmission electron microscope and to other low-dimensional materials.

| S-EPMC5476802 | biostudies-literature

In situ electronic characterization of graphene nanoconstrictions fabricated in a transmission electron microscope.

Project description:We report electronic measurements on high-quality graphene nanoconstrictions (GNCs) fabricated in a transmission electron microscope (TEM), and the first measurements on GNC conductance with an accurate measurement of constriction width down to 1 nm. To create the GNCs, freely suspended graphene ribbons were fabricated using few-layer graphene grown by chemical vapor deposition. The ribbons were loaded into the TEM, and a current-annealing procedure was used to clean the material and improve its electronic characteristics. The TEM beam was then used to sculpt GNCs to a series of desired widths in the range 1-700 nm; after each sculpting step, the sample was imaged by TEM and its electronic properties were measured in situ. GNC conductance was found to be remarkably high, comparable to that of exfoliated graphene samples of similar size. The GNC conductance varied with width approximately as G(w)=(e2/h)w0.75, where w is the constriction width in nanometers. GNCs support current densities greater than 120 ?A/nm2, 2 orders of magnitude higher than that which has been previously reported for graphene nanoribbons and 2000 times higher than that reported for copper.

| S-EPMC3382988 | biostudies-literature

Attosecond metrology in a continuous-beam transmission electron microscope.

Project description:Electron microscopy can visualize the structure of complex materials with atomic and subatomic resolution, but investigations of reaction dynamics and light-matter interaction call for time resolution as well, ideally on a level below the oscillation period of light. Here, we report the use of the optical cycles of a continuous-wave laser to bunch the electron beam inside a transmission electron microscope into electron pulses that are shorter than half a cycle of light. The pulses arrive at the target at almost the full average brightness of the electron source and in synchrony to the optical cycles, providing attosecond time resolution of spectroscopic features. The necessary modifications are simple and can turn almost any electron microscope into an attosecond instrument that may be useful for visualizing the inner workings of light-matter interaction on the basis of the atoms and the cycles of light.

| S-EPMC7673721 | biostudies-literature

Comparing Scanning Electron Microscope and Transmission Electron Microscope Grain Mapping Techniques Applied to Well-Defined and Highly Irregular Nanoparticles.

Project description:Investigating how grain structure affects the functional properties of nanoparticles requires a robust method for nanoscale grain mapping. In this study, we directly compare the grain mapping ability of transmission Kikuchi diffraction (TKD) in a scanning electron microscope to automated crystal orientation mapping (ACOM) in a transmission electron microscope across multiple nanoparticle materials. Analysis of well-defined Au, ZnO, and ZnSe nanoparticles showed that the grain orientations and GB geometries obtained by TKD are accurate and match those obtained by ACOM. For more complex polycrystalline Cu nanostructures, TKD provided an interpretable grain map whereas ACOM, with or without precession electron diffraction, yielded speckled, uninterpretable maps with orientation errors. Acquisition times for TKD were generally shorter than those for ACOM. Our results validate the use of TKD for characterizing grain orientation and grain boundary distributions in nanoparticles, providing a framework for the broader exploration of how microstructure influences nanoparticle properties.

| S-EPMC7033971 | biostudies-literature

Iterative stable alignment and clustering of 2D transmission electron microscope images.

Project description:Identification of homogeneous subsets of images in a macromolecular electron microscopy (EM) image data set is a critical step in single-particle analysis. The task is handled by iterative algorithms, whose performance is compromised by the compounded limitations of image alignment and K-means clustering. Here we describe an approach, iterative stable alignment and clustering (ISAC) that, relying on a new clustering method and on the concepts of stability and reproducibility, can extract validated, homogeneous subsets of images. ISAC requires only a small number of simple parameters and, with minimal human intervention, can eliminate bias from two-dimensional image clustering and maximize the quality of group averages that can be used for ab initio three-dimensional structural determination and analysis of macromolecular conformational variability. Repeated testing of the stability and reproducibility of a solution within ISAC eliminates heterogeneous or incorrect classes and introduces critical validation to the process of EM image clustering.

| S-EPMC3426367 | biostudies-literature

In-Situ Stretching Patterned Graphene Nanoribbons in the Transmission Electron Microscope.

Project description:The mechanical response of patterned graphene nanoribbons (GNRs) with a width less than 100 nm was studied in-situ using quantitative tensile testing in a transmission electron microscope (TEM). A high degree of crystallinity was confirmed for patterned nanoribbons before and after the in-situ experiment by selected area electron diffraction (SAED) patterns. However, the maximum local true strain of the nanoribbons was determined to be only about 3%. The simultaneously recorded low-loss electron energy loss spectrum (EELS) on the stretched nanoribbons did not reveal any bandgap opening. Density Functional Based Tight Binding (DFTB) simulation was conducted to predict a feasible bandgap opening as a function of width in GNRs at low strain. The bandgap of unstrained armchair graphene nanoribbons (AGNRs) vanished for a width of about 14.75 nm, and this critical width was reduced to 11.21 nm for a strain level of 2.2%. The measured low tensile failure strain may limit the practical capability of tuning the bandgap of patterned graphene nanostructures by strain engineering, and therefore, it should be considered in bandgap design for graphene-based electronic devices by strain engineering.

| S-EPMC5428052 | biostudies-literature

Fine Structure in Multi-Phase Zr₈Ni21-Zr₇Ni10-Zr₂Ni₇ Alloy Revealed by Transmission Electron Microscope.

Project description:The microstructure of an annealed alloy with a Zr₈Ni21 composition was studied by both scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The presence of three phases, Zr₈Ni21, Zr₂Ni₇, and Zr₇Ni10, was confirmed by SEM/X-ray energy dispersive spectroscopy compositional mapping and TEM electron diffraction. Distribution of the phases and their morphology can be linked to a multi-phase structure formed by a sequence of reactions: (1) L → Zr₂Ni₇ + L'; (2) peritectic Zr₂Ni₇ + L' → Zr₂Ni₇ + Zr₈Ni21 + L"; (3) eutectic L" → Zr₈Ni21 + Zr₇Ni10. The effect of annealing at 960 °C, which was intended to convert a cast structure into a single-phase Zr₈Ni21 structure, was only moderate and the resulting alloy was still multi-phased. TEM and crystallographic analysis of the Zr₂Ni₇ phase show a high density of planar (001) defects that were explained as low-energy boundaries between rotational variants and stacking faults. The crystallographic features arise from the pseudo-hexagonal structure of Zr₂Ni₇. This highly defective Zr₂Ni₇ phase was identified as the source of the broad X-ray diffraction peaks at around 38.4° and 44.6° when a Cu-K was used as the radiation source.

| S-EPMC5455659 | biostudies-other

In Situ Quantitative Tensile Testing of Antigorite in a Transmission Electron Microscope.

Project description:The determination of the mechanical properties of serpentinites is essential toward the understanding of the mechanics of faulting and subduction. Here we present the first in situ tensile tests on antigorite in a transmission electron microscope. A push-to-pull deformation device is used to perform quantitative tensile tests, during which force and displacement are measured, while the evolving microstructure is imaged with the microscope. The experiments have been performed at room temperature on 2 × 1 × 0.2 ?m3 beams prepared by focused ion beam. The specimens are not single crystals despite their small sizes. Orientation mapping indicated that several grains were well oriented for plastic slip. However, no dislocation activity has been observed even though the engineering tensile stress went up to 700 MPa. We show also that antigorite does not exhibit a purely elastic-brittle behavior since, despite the presence of defects, the specimens accumulate permanent deformation and did not fail within the elastic regime. Instead, we observe that strain localizes at grain boundaries. All observations concur to show that under these experimental conditions, grain boundary sliding is the dominant deformation mechanism. This study sheds a new light on the mechanical properties of antigorite and calls for further studies on the structure and properties of grain boundaries in antigorite and more generally in phyllosilicates.

| S-EPMC7375155 | biostudies-literature

Depth sectioning with the aberration-corrected scanning transmission electron microscope.

Project description:The ability to correct the aberrations of the probe-forming lens in the scanning transmission electron microscope provides not only a significant improvement in transverse resolution but in addition brings depth resolution at the nanometer scale. Aberration correction therefore opens up the possibility of 3D imaging by optical sectioning. Here we develop a definition for the depth resolution for scanning transmission electron microscope depth sectioning and present initial results from this method. Objects such as catalytic metal clusters and single atoms on various support materials are imaged in three dimensions with a resolution of several nanometers. Effective focal depth is determined by statistical analysis and the contributing factors are discussed. Finally, current challenges and future capabilities available through new instruments are discussed.

| S-EPMC1413870 | biostudies-other

Transmission electron microscope evidence of telocytes in canine dura mater.

Project description:Telocytes (TCs) are a novel type of interstitial cells present in a wide variety of organs and tissues (www.telocytes.com). Telocytes are identified morphologically by a small cell body and specific long prolongations (telopodes) alternating thin segments (podomers) with dilations (podoms). The presence of TCs in rat meninges has been identified in previous research. We here present further evidence that TCs existed in canine dura mater, closed to capillary and surrounded by a great deal of collagen fibres under transmission electron microscope.

| S-EPMC4717856 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data