Combination of polyethylene glycol impregnation and paraffin heat treatment to protect round bamboo from cracking.

ABSTRACT: Round bamboo has drawn more and more attention in architecture, decoration and recreational products. Splitting brings some safety problems, which shorten the service life of round bamboo. In this paper, three schemes were adopted as follows to solve the problem: round bamboo was impregnated in polyethylene glycol (PEG)-1000 solution alone, heat treatment in paraffin alone or treated with the combination of PEG impregnation and paraffin heat treatment (PEG-PH). The treated bamboo was exposed outdoors for 26 weeks to evaluate the development of cracks. Results showed as follows: the initial split of PEG-PH-treated bamboo appeared after 22 weeks, while that of the controls after 2 weeks, the total length of cracks was 2271.31 and 873.5 mm for the control and PEG-PH-treated bamboo, respectively. To reveal the reasons for reduced cracks, scanning electron micrograph (SEM) was employed to observe the microstructure of bamboo; besides, hydrophobicity of bamboo was characterized by the water contact angle. PEG can swell the cell wall and the better hydrophobicity of round bamboo could be achieved after PEG-PH treatment. Therefore, the combination of PEG immersion and paraffin heating is an effective and practicable method in bamboo treatment, especially for round bamboo with high moisture content.

SUBMITTER: Rao J

PROVIDER: S-EPMC6894564 | biostudies-literature | 2019 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Combination of polyethylene glycol impregnation and paraffin heat treatment to protect round bamboo from cracking.

Rao Jin J Jiang Jun J Prosper Nayebare Kakwara NK Yang Xiushu X Liu Tingsong T Cai Wei W Wang Hui H Sun Fangli F

Royal Society open science 20191106 11

Round bamboo has drawn more and more attention in architecture, decoration and recreational products. Splitting brings some safety problems, which shorten the service life of round bamboo. In this paper, three schemes were adopted as follows to solve the problem: round bamboo was impregnated in polyethylene glycol (PEG)-1000 solution alone, heat treatment in paraffin alone or treated with the combination of PEG impregnation and paraffin heat treatment (PEG-PH). The treated bamboo was exposed out ...[more]

PMID: 31827815

Similar Datasets

Project description:In this paper, Moso bamboo (Phyllostachys heterocycle) before and after heat treatment were used as raw materials to prepare transparent bamboo (TB). In an acidic environment, the lignin contained in the bamboo material was removed to obtain a bamboo template, and an epoxy resin similar to the cellulose refractive index was used for vacuum impregnation into the bamboo template to obtain a transparent bamboo material. The purpose of this study was to compare the physical and chemical properties of TB and original bamboo and the differences between TBs before and after heat treatment, taken from different parts of bamboo, in order to explore the performance advantages and disadvantages of TB as a new material. The Fourier transform infrared spectroscopy analysis (FTIR), scanning electron microscope testing (SEM), three elements analysis, light transmittance testing, and mechanical strength testing were used to study the molecular composition, microstructure, chemical composition, light transmittance, and tensile strength of the TB samples. The results showed that the lignin content of the delignified bamboo templates was greatly reduced. In addition, the SEM images showed that a large amount of epoxy resin (type E51 and type B210 curing agent) was covered on the cross-section surface and pores of the TB samples. The FTIR showed that the epoxy molecular groups appeared on the TB, and the delignified bamboo template and the resin had a good synergy effect. According to the light transmittance testing, the original bamboo samples hardly contained light transmittance under visible light. The transmittance of transparent inner bamboo (TIB) and transparent heat-treated inner bamboo (THIB) could reach about 11%, and the transmittance of transparent outer bamboo (TOB) and transparent heat-treated outer bamboo (THOB) was about 2%. The light transmittance had been significantly improved when compared with the original bamboo samples. The transmittances of the TB samples before and after heat treatment in different parts of bamboo were different. In the visible light irradiation range, the light transmittances of TB samples were as follows: TIB > THIB and THOB > TOB. Meanwhile, the tensile strength of TB was reduced, especially for TOB and THOB. In addition, TB has a wide range of raw materials, and the preparation process is environmentally friendly. It can be used for decorative materials in homes, buildings, etc., and has a great application potential.

Dataset Information

Combination of polyethylene glycol impregnation and paraffin heat treatment to protect round bamboo from cracking.

Publications

Combination of polyethylene glycol impregnation and paraffin heat treatment to protect round bamboo from cracking.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets