Amino-Functionalized Lead Phthalocyanine-Modified Benzoxazine Resin: Curing Kinetics, Thermal, and Mechanical Properties.

ABSTRACT: Phenol-diaminodiphenylmethane-based benzoxazine (P-ddm)/phthalocyanine copolymer was prepared by using P-ddm resin as matrix and 3,10,17,24-tetra-aminoethoxy lead phthalocyanine (APbPc) as additive. Fourier-transform infrared (FTIR), differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA), and thermogravimetric analysis (TGA) were used to investigate the curing behavior, curing kinetics, dynamic mechanical properties, thermal stability, and impact strength of the prepared copolymers. The kinetic parameters for the P-ddm/APbPc blend curing processes were examined by utilizing the iso-conversional, Flynn-Wall-Ozawa, and Málek methods. The P-ddm/APbPc blends exhibit two typical curing processes, and DSC results confirmed that the blending of APbPc monomer can effectively reduce the curing temperature of P-ddm resin. The autocatalytic models also described the non-isothermal curing reaction rate well, and the appropriate kinetic parameters of the curing process were obtained. The DMA and impact strength experiments proved that the blending of APbPc monomer can significantly improve the toughness and stiffness of P-ddm resin, the highest enhancements were observed on 25 wt.% addition of APbPc, the recorded values for the storage modulus and impact strength were 1003 MPa and 3.60 kJ/m² higher, respectively, while a decline of 24.6 °C was observed in the glass transition temperature values. TGA curves indicated that the cured copolymers also exhibit excellent thermal stabilities.

SUBMITTER: Zu LW

PROVIDER: S-EPMC6918423 | biostudies-literature | 2019 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Amino-Functionalized Lead Phthalocyanine-Modified Benzoxazine Resin: Curing Kinetics, Thermal, and Mechanical Properties.

Zu Li-Wu LW Gao Bao-Chang BC Pan Zhong-Cheng ZC Wang Jun J Dayo Abdul Qadeer AQ Liu Wen-Bin WB

Polymers 20191111 11

Phenol-diaminodiphenylmethane-based benzoxazine (P-ddm)/phthalocyanine copolymer was prepared by using P-ddm resin as matrix and 3,10,17,24-tetra-aminoethoxy lead phthalocyanine (APbPc) as additive. Fourier-transform infrared (FTIR), differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA), and thermogravimetric analysis (TGA) were used to investigate the curing behavior, curing kinetics, dynamic mechanical properties, thermal stability, and impact strength of the prepared copo ...[more]

PMID: 31717916

Similar Datasets

Project description:A novel organic-inorganic hybrid containing allyl benzoxazine and polyhedral oligomeric silsesquioxane (POSS) was synthesized by the thiol-ene (click) reaction. The benzoxazine (BOZ)-containing POSS (SPOSS-BOZ) copolymerized with benzoxazine/epoxy resin was used to prepare composites of SPOSS-PBZ-E nanocomposites(NPs). The polymerization behavior was monitored by FTIR and non-isothermal differential scanning calorimetry (DSC), which showed that the composites had completely cured with multiple polymerization mechanisms according to the oxazine ring-opening and epoxy resin (EP) polymerization. The thermal properties of the organic-inorganic polybenzoxazine (PBZ) nanocomposites were analyzed by DSC and thermogravimetric analysis (TGA). Furthermore, the X-ray diffraction analysis and the scanning electron microscopy (SEM) micrographs of the SPOSS-PBZ-E nanocomposites indicated that SPOSS was chemically incorporated into the hybrid nanocomposites in the size range of 80-200 nm. The flame retardancy of the benzoxazine epoxy resin composites was investigated by limiting oxygen index (LOI), UL 94 vertical burn test, and cone calorimeter tests. When the amount of SPOSS reached 10% or more, the vertical burning rating of the curing system arrived at V-1, and when the SPOSS-BOZ content reached 20 wt %, the thermal stability and flame retardancy of the material were both improved. Moreover, in the cone calorimeter testing, the addition of SPOSS-BOZ hindered the decomposition of the composites and led to a reduction in the peak heat release rate (pHRR), the average heat release rate (aHRR), and the total heat release (THR) values by about 20%, 25%, and 25%, respectively. The morphologies of the chars were also studied by SEM and energy dispersive X-ray spectroscopy (EDX), and the flame-retardant mechanism of POSS was mainly a condensed-phase flame retardant. The ceramic layer was formed by the enrichment of silicon on the char surface. When there are enough POSS nanoparticles, it can effectively protect the combustion of internal polymers.

Dataset Information

Amino-Functionalized Lead Phthalocyanine-Modified Benzoxazine Resin: Curing Kinetics, Thermal, and Mechanical Properties.

Publications

Amino-Functionalized Lead Phthalocyanine-Modified Benzoxazine Resin: Curing Kinetics, Thermal, and Mechanical Properties.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets