Photocatalytic inactivation of Escherischia coli under UV light irradiation using large surface area anatase TiO2 quantum dots.

ABSTRACT: In this study, high specific surface areas (SSAs) of anatase titanium dioxide (TiO2) quantum dots (QDs) were successfully synthesized through a novel one-step microwave-hydrothermal method in rapid synthesis time (20 min) without further heat treatment. XRD analysis and HR-TEM images showed that the as-prepared TiO2 QDs of approximately 2 nm size have high crystallinity with anatase phase. Optical properties showed that the energy band gap (E g) of as-prepared TiO2 QDs was 3.60 eV, which is higher than the standard TiO2 band gap, which might be due to the quantum size effect. Raman studies showed shifting and broadening of the peaks of TiO2 QDs due to the reduction of the crystallite size. The obtained Brunauer-Emmett-Teller specific surface area (381 m2 g-1) of TiO2 QDs is greater than the surface area (181 m2 g-1) of commercial TiO2 nanoparticles. The photocatalytic activities of TiO2 QDs were conducted by the inactivation of Escherischia coli under ultraviolet light irradiation and compared with commercially available anatase TiO2 nanoparticles. The photocatalytic inactivation ability of E. coli was estimated to be 91% at 60 µg ml-1 for TiO2 QDs, which is superior to the commercial TiO2 nanoparticles. Hence, the present study provides new insight into the rapid synthesis of TiO2 QDs without any annealing treatment to increase the absorbance of ultraviolet light for superior photocatalytic inactivation ability of E. coli.

SUBMITTER: Ahmed F

PROVIDER: S-EPMC6936290 | biostudies-literature | 2019 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Photocatalytic inactivation of Escherischia coli under UV light irradiation using large surface area anatase TiO2 quantum dots.

Ahmed Faheem F Awada Chawki C Ansari Sajid Ali SA Aljaafari Abdullah A Alshoaibi Adil A

Royal Society open science 20191204 12

In this study, high specific surface areas (SSAs) of anatase titanium dioxide (TiO2) quantum dots (QDs) were successfully synthesized through a novel one-step microwave-hydrothermal method in rapid synthesis time (20 min) without further heat treatment. XRD analysis and HR-TEM images showed that the as-prepared TiO2 QDs of approximately 2 nm size have high crystallinity with anatase phase. Optical properties showed that the energy band gap (E g) of as-prep ...[more]

PMID: 31903213

Similar Datasets

Project description:Background purposePhotocatalytic water splitting for hydrogen evolution is a potential way to solve many energy and environmental issues. Developing visible-light-active photocatalysts to efficiently utilize sunlight and finding proper ways to improve photocatalytic activity for H2 evolution have always been hot topics for research. This study attempts to expand the use of sunlight and to enhance the photocatalytic activity of TiO2 by N doping and Au loading.MethodsAu/N-doped TiO2 photocatalysts were synthesized and successfully used for photocatalytic water splitting for H2 evolution under irradiation of UV and UV-vis light, respectively. The samples were characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), UV-vis diffuse reflectance spectroscopy (DRS), photoluminescence spectroscopy (PL), and photoelectrochemical characterizations.ResultsDRS displayed an extension of light absorption into the visible region by doping of N and depositing with Au, respectively. PL analysis indicated electron-hole recombination due to N doping and an efficient inhibition of electron-hole recombination due to the loaded Au particles. Under the irradiation of UV light, the photocatalytic hydrogen production rate of the as-synthesized samples followed the order Au/TiO2 > Au/N-doped TiO2 > TiO2 > N-doped TiO2. While under irradiation of UV-vis light, the N-TiO2 and Au/N-TiO2 samples show higher H2 evolution than their corresponding nitrogen-free samples (TiO2 and Au/TiO2). This inconsistent result could be attributed to the doping of N and the surface plasmonic resonance (SPR) effect of Au particles extending the visible light absorption. The photoelectrochemical characterizations further indicated the enhancement of the visible light response of Au/N-doped TiO2.ConclusionComparative studies have shown that a combination of nitrogen doping and Au loading enhanced the visible light response of TiO2 and increased the utilization of solar energy, greatly boosting the photocatalytic activity for hydrogen production under UV-vis light.

Dataset Information

Photocatalytic inactivation of Escherischia coli under UV light irradiation using large surface area anatase TiO2 quantum dots.

Publications

Photocatalytic inactivation of <i>Escherischia coli</i> under UV light irradiation using large surface area anatase TiO<sub>2</sub> quantum dots.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets