Thin-film composite membrane breaking the trade-off between conductivity and selectivity for a flow battery.

ABSTRACT: A membrane with both high ion conductivity and selectivity is critical to high power density and low-cost flow batteries, which are of great importance for the wide application of renewable energies. The trade-off between ion selectivity and conductivity is a bottleneck of ion conductive membranes. In this paper, a thin-film composite membrane with ultrathin polyamide selective layer is found to break the trade-off between ion selectivity and conductivity, and dramatically improve the power density of a flow battery. As a result, a vanadium flow battery with a thin-film composite membrane achieves energy efficiency higher than 80% at a current density of 260 mA cm^-2, which is the highest ever reported to the best of our knowledge. Combining experiments and theoretical calculation, we propose that the high performance is attributed to the proton transfer via Grotthuss mechanism and Vehicle mechanism in sub-1 nm pores of the ultrathin polyamide selective layer.

SUBMITTER: Dai Q

PROVIDER: S-EPMC6946707 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Oily Wastewater Treatment Using Polyamide Thin Film Composite Membrane Technology.

Project description:In this study, polyamide (PA) thin film composite (TFC) reverse osmosis (RO) membrane filtration was used in edible oil wastewater emulsion treatment. The PA-TFC membrane was characterized using mechanical, thermal, chemical, and physical tests. Surface morphology and cross-sections of TFCs were characterized using SEM. The effects of edible oil concentrations, average droplets size, and contact angle on separation efficiency and flux were studied in detail. Purification performance was enhanced using activated carbon as a pre-treatment unit. The performance of the RO unit was assessed by chemical oxygen demand (COD) removal and permeate flux. Oil concentration in wastewater varied between 3000 mg/L and 6000 mg/L. Oily wastewater showed a higher contact angle (62.9°) than de-ionized water (33°). Experimental results showed that the presence of activated carbon increases the permeation COD removal from 94% to 99%. The RO membrane filtration coupled with an activated carbon unit of oily wastewater is a convenient hybrid technique for removal of high-concentration edible oil wastewater emulsion up to 99%. Using activated carbon as an adsorption pre-treatment unit improved the permeate flux from 34 L/m2hr to 75 L/m2hr.

| S-EPMC7281104 | biostudies-literature

Breaking of Thermopower-Conductivity Trade-Off in LaTiO<sub>3</sub> Film around Mott Insulator to Metal Transition.

Project description:Introducing artificial strain in epitaxial thin films is an effective strategy to alter electronic structures of transition metal oxides (TMOs) and to induce novel phenomena and functionalities not realized in bulk crystals. This study reports a breaking of the conventional trade-off relation in thermopower (S)-conductivity (σ) and demonstrates a 2 orders of magnitude enhancement of power factor (PF) in compressively strained LaTiO3 (LTO) films. By varying substrates and reducing film thickness down to 4 nm, the out-of-plane to the in-plane lattice parameter ratio is controlled from 0.992 (tensile strain) to 1.034 (compressive strain). This tuning induces the electronic structure change from a Mott insulator to a metal and leads to a 103 -fold increase in σ up to 2920 S cm-1 . Concomitantly, the sign of S inverts from positive to negative, and both σ and S increase and break the trade-off relation between them in the n-type region. As a result, the PF (=S2 σ) is significantly enhanced to 300 µW m- 1 K-2 , which is 102 times larger than that of bulk LTO. Present results propose epitaxial strain as a means to finely tune strongly correlated TMOs close to their Mott transition, and thus to harness the hidden large thermoelectric PF.

| S-EPMC8655177 | biostudies-literature

Thin Film Composite Polyamide Reverse Osmosis Membrane Technology towards a Circular Economy.

Project description:It is estimated that Reverse Osmosis (RO) desalination will produce, by 2025, more than 2,000,000 end-of-life membranes annually worldwide. This review examines the implementation of circular economy principles in RO technology through a comprehensive analysis of the RO membrane life cycle (manufacturing, usage, and end-of-life management). Future RO design should incorporate a biobased composition (biopolymers, recycled materials, and green solvents), improve the durability of the membranes (fouling and chlorine resistance), and facilitate the recyclability of the modules. Moreover, proper membrane maintenance at the usage phase, attained through the implementation of feed pre-treatment, early fouling detection, and membrane cleaning methods can help extend the service time of RO elements. Currently, end-of-life membranes are dumped in landfills, which is contrary to the waste hierarchy. This review analyses up to now developed alternative valorisation routes of end-of-life RO membranes, including reuse, direct and indirect recycling, and energy recovery, placing a special focus on emerging indirect recycling strategies. Lastly, Life Cycle Assessment is presented as a holistic methodology to evaluate the environmental and economic burdens of membrane recycling strategies. According to the European Commission's objectives set through the Green Deal, future perspectives indicate that end-of-life membrane valorisation strategies will keep gaining increasing interest in the upcoming years.

| S-EPMC9502371 | biostudies-literature

Poly(Homopiperazine-Amide) Thin-Film Composite Membrane for Nanofiltration of Heavy Metal Ions.

Project description:The development of membrane-based technologies for the treatment of wastewater streams and resources containing heavy metal ions is in high demand. Among various technologies, nanofiltration (NF) membranes are attractive choices, and the continuous development of novel materials to improve the state-of-the-art NF membranes is highly desired. Here, we report on the synthesis of poly(homopiperazine-amide) thin-film composite (HTFC)-NF membranes, using homopiperazine (HP) as a monomer. The surface charge, hydrophilicity, morphology, cross-linking density, water permeation, solute rejection, and antifouling properties of the fabricated NF membranes were evaluated. The fabricated HTFC NF membranes demonstrated water permeability of 7.0 ± 0.3 L/(m2 h bar) and rejected Na2SO4, MgSO4, and NaCl with rejection values of 97.0 ± 0.6, 97.4 ± 0.5, and 23.3 ± 0.6%, respectively. The membranes exhibit high rejection values of 98.1 ± 0.3 and 96.3 ± 0.4% for Pb2+ and Cd2+ ions, respectively. The fouling experiment with humic acid followed by cross-flow washing of the membranes indicates that a flux recovery ratio (FRR) of 96.9 ± 0.4% can be obtained.

| S-EPMC7659160 | biostudies-literature

Tuning the Ion-Selectivity of Thin-Film Composite Nanofiltration Membranes by Molecular Layer Deposition of Alucone.

Project description:This work addresses a key challenge of tailoring the ion selectivity of a thin-film composite nanofiltration membrane to a specific application, such as water softening, without altering the water permeability. We modified the active surface of a commercial NF270 membrane by molecular layer deposition (MLD) of ethylene glycol-Al (EG-alucone). With increasing deposition cycles, we found that the MLD precursors first infiltrated and deposited in the active layer of NF270, then inflated the active layer, and finally deposited on the surface as a distinct EG-alucone layer. The deposition process changed the morphology of the membrane active layer and decreased the overall density of its fixed negative charge by embedding the positively charged EG-alucone. Filtration experiments revealed that these modifications affected the ion separation properties of the membrane without significantly hindering the water permeability. Specifically, the permeation of Na+ increased relative to that of Mg2+, as indicated by the permselectivity of Na+ salts over Mg2+ salts. The changes in permselectivities with an increasing number of MLD cycles were rationalized using the dielectric, steric, and electrostatic ion exclusion mechanisms, which are related to the membrane material, pore size, and fixed charge, respectively. These relations open a path for the rational design of nanofiltration membranes with tailored selectivity by tuning the properties of the MLD layer. Filtration results of natural brackish groundwater using the MLD modified membranes agreed with the single salt experiments. As a result, water hardness was 26% lower for the permeate obtained using the MLD-modified membranes, which were found stable even during a 24 h filtration run. These results highlight the practical potential of this approach in enhancing water softening efficiency.

| S-EPMC7735666 | biostudies-literature

An Economical Composite Membrane with High Ion Selectivity for Vanadium Flow Batteries.

Project description:The ion exchange membrane of the Nafion series widely used in vanadium flow batteries (VFBs) is characterized by its high cost and high vanadium permeability, which limit the further commercialization of VFBs. Herein, a thin composite membrane enabled by a low-cost microporous polyethylene (PE) substrate and perfluorosulfonic acid (PFSA) resin is proposed to reduce the cost of the membrane. Meanwhile, the rigid PE substrate limits the swelling of the composite membrane, which effectively reduces the penetration of vanadium ions and improves the ion selectivity of the composite membrane. Benefiting from such a rational design, a VFB assembled with the PE/PFSA composite membrane exhibited a higher coulombic efficiency (CE ≈ 96.8%) compared with commercial Nafion212 at 200 mA cm-2. Significantly, the energy efficiency maintained stability within 200 cycles with a slow decay rate. In practical terms, the thin PE/PFSA composite membrane with low cost and high ion selectivity can make an ideal membrane candidate in VFBs.

| S-EPMC10057319 | biostudies-literature

Modification of Polyamide-Urethane (PAUt) Thin Film Composite Membrane for Improving the Reverse Osmosis Performance.

Project description:In the current study, the poly (amide-urethane) (PAUt) membranes were successfully fabricated by interfacial polymerization of m-phenylenediamine (MPD) and 5-choroformyloxyisophaloyl chloride (CFIC) on the polysulfone substrates. Two modification methods based on layer-by-layer assembly were applied to modify the PAUt membrane surface to achieve antifouling property: 1. Chitosan (CS) was directly self-assembled on the PAUt membrane (i.e., PAUt-CS); and 2. polydimethyl diallyl ammonium chloride (PDDA), polystyrene sulfonate (PSS), and CS were successively self-assembled on the membrane surface (i.e., PAUt-PDDA/PSS/CS). The resultant membranes were symmetrically characterized by Attenuated Total Reflection Fourier Transform Infrared Spectroscopy (ATR-FTIR), X-ray Photoelectron Spectroscopy (XPS), Scanning Electron Microscopy (SEM), Atomic Force Microscopy (AFM) and Contact Angle Meter (CAM), respectively. The results indicated that the modified membranes had much smoother and more hydrophilic surfaces as compared to the nascent PAUt membrane. Meanwhile, the modified membranes exhibited better reverse osmosis performance in terms of water permeability and salt rejection. After the modified membranes were fouled by lake water, the PAUt-PDDA/PSS/CS membrane presented the best antifouling performance among the three types of membranes. Combining the reverse osmosis performance with the anti-fouling property obviously, the PAUt-PDDA/PSS/CS membrane behaved as a promising candidate to be used in real applications.

| S-EPMC6415036 | biostudies-literature

Organic Nanobowls Modified Thin Film Composite Membrane for Enhanced Purification Performance toward Different Water Resources.

Project description:The structure and composition of nanofillers have a significant influence on polyamide nanofiltration (NF) membranes. In this work, an asymmetric organic nanobowl containing a concave cavity was synthesized and incorporated into a polyamide layer to prepare thin film nanocomposite (TFN) membranes via an interfacial polymerization process. Benefiting from the hydrophilicity, hollow cavity and charge property of the compatible organic nanobowls, the separation performance of the developed TFN membrane was significantly improved. The corresponding water fluxes increased to 119.44 ± 5.56, 141.82 ± 3.24 and 130.27 ± 2.05 L/(m2·h) toward Na2SO4, MgCl2 and NaCl solutions, respectively, with higher rejections, compared with the control thin film composite (TFC) and commercial (CM) membranes. Besides this, the modified TFN membrane presented a satisfying purification performance toward tap water, municipal effluent and heavy metal wastewater. More importantly, a better antifouling property of the TFN membrane than TFC and CM membranes was achieved with the assistance of organic nanobowls. These results indicate that the separation performance of the TFN membrane can be elevated by the incorporation of organic nanobowls.

| S-EPMC8151631 | biostudies-literature

Harnessing Thin-Film Continuous-Flow Assembly Lines.

Project description:Inspired by nature's ability to construct complex molecules through sequential synthetic transformations, an assembly line synthesis of ?-aminophosphonates has been developed. In this approach, simple starting materials are continuously fed through a thin-film reactor where the intermediates accrue molecular complexity as they progress through the flow system. Flow chemistry allows rapid multistep transformations to occur via reaction compartmentalization, an approach not amenable to using conventional flasks. Thin film processing can also access facile in situ solvent exchange to drive reaction efficiency, and through this method, ?-aminophosphonate synthesis requires only 443?s residence time to produce 3.22?g?h(-1) . Assembly-line synthesis allows unprecedented reaction flexibility and processing efficiency.

| S-EPMC5562431 | biostudies-literature

Thin-Film Composite Membrane with Porous Interlayer Composed of Dendritic Mesoporous Silica Nanoparticles for Enhanced Nanofiltration.

Project description:Positively charged nanofiltration (NF) membranes show great potential in the fields of water treatment and resource recovery. However, this kind of NF membrane usually suffers from relatively low water permeance. Herein, a positively charged NF membrane with a porous interlayer is developed, where the interlayer is formed by assembling dendritic mesoporous silica nanoparticles (DMSNs) after the formation of a polyamide layer. This post-assembly strategy avoids the adverse effect of the interlayer on the formation of positively charged NF membranes. The porous DMSN interlayer provides abundant connected channels for water transport, thus endowing the NF membrane with enhanced water permeance. A series of DMSNs with different sizes was synthesized, and their influence on membrane formation and membrane performance was systematically investigated. The optimized membrane exhibits a CaCl2 rejection rate of 95.2% and a water flux of 133.6 L·h-1·m-2, which is 1.6 times that of the control group without an interlayer. This work represents an approach to the fabrication of a positively charged NF membrane with porous interlayers for high-efficiency cation rejection.

| S-EPMC10574978 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data