Visualization of aquaionic splitting via iron corrosion.

ABSTRACT: We report a water decomposition mode called 'Aquaionic Splitting (AiS)' by means of iron corrosion in aqueous solution. In this paper, we investigated the phenomenon by controlling the reaction between iron and water. A pseudo-sacrificial protection method with oil paint was employed to select the anode and cathode formation locations that govern iron corrosion. Then, the AiS reaction was visualized by using BTB solution, whose colour corresponds to pH, to produce colour patterning that corresponds to the aquaion distribution. It has become clear that water can be selectively separated into protons and hydroxide ions by corrosion control treatment. In this vein, the diffusion coefficient of protons was estimated by using the colour patterning of BTB solution that accompanies iron corrosion, and aquaion distribution was then computer simulated by solving the diffusion equation.

SUBMITTER: Murakami S

PROVIDER: S-EPMC6997388 | biostudies-literature | 2020 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Visualization of aquaionic splitting via iron corrosion.

Murakami Shuntaro S Zhang Lihua L Watanabe Seiichi S

Scientific reports 20200203 1

We report a water decomposition mode called 'Aquaionic Splitting (AiS)' by means of iron corrosion in aqueous solution. In this paper, we investigated the phenomenon by controlling the reaction between iron and water. A pseudo-sacrificial protection method with oil paint was employed to select the anode and cathode formation locations that govern iron corrosion. Then, the AiS reaction was visualized by using BTB solution, whose colour corresponds to pH, to produce colour patterning that correspo ...[more]

PMID: 32015420

Similar Datasets

Project description:The concept that anaerobic microorganisms can directly accept electrons from Fe(0) has been controversial because direct metal-microbe electron transfer has previously only been indirectly inferred. Fe(0) oxidation was studied with Geobacter sulfurreducens strain ACL, an autotrophic strain that was previously shown to grow with electrons derived from a graphite cathode as the sole electron donor. Strain ACL grew with Fe(0) as the sole electron donor and fumarate as the electron acceptor. However, it appeared that at least a portion of the electron transfer was via H2 produced nonenzymatically from the oxidation of Fe(0) to Fe(II). H2, which accumulated in abiotic controls, was consumed during the growth of strain ACL, the cells were predominately planktonic, and genes for the uptake hydrogenase were highly expressed. Strain ACLHF was constructed to prevent growth on H2 or formate by deleting the genes for the uptake of hydrogenase and formate dehydrogenases from strain ACL. Strain ACLHF also grew with Fe(0) as the sole electron donor, but H2 accumulated in the culture, and cells heavily colonized Fe(0) surfaces with no visible planktonic growth. Transcriptomics suggested that the outer surface c-type cytochromes OmcS and OmcZ were important during growth of strain ACLHF on Fe(0). Strain ACLHF did not grow on Fe(0) if the gene for either of these cytochromes was deleted. The specific attachment of strain ACLHF to Fe(0), coupled with requirements for known extracellular electrical contacts, suggest that direct metal-microbe electron transfer is the most likely option for Fe(0) serving as an electron donor.IMPORTANCE The anaerobic corrosion of iron structures is expensive to repair and can be a safety and environmental concern. It has been known for over 100 years that the presence of anaerobic respiratory microorganisms can accelerate iron corrosion. Multiple studies have suggested that there are sulfate reducers, methanogens, and acetogens that can directly accept electrons from Fe(0) to support sulfate or carbon dioxide reduction. However, all of the strains studied can also use H2 as an electron donor for growth, which is known to be abiotically produced from Fe(0). Furthermore, no proteins definitely shown to function as extracellular electrical contacts with Fe(0) were identified. The studies described here demonstrate that direct electron transfer from Fe(0) can support anaerobic respiration. They also map out a simple genetic approach to the study of iron corrosion mechanisms in other microorganisms. A better understanding of how microorganisms promote iron corrosion is expected to lead to the development of strategies that can help reduce adverse impacts from this process.

Project description:Abstract Metal corrosion is important in the fields of biomedicine as well as construction and transportation etc. While most corrosion occurs inhomogeneously, there is so far no satisfactory parameter to characterize corrosion inhomogeneity. Herein, we employ the Poisson raindrop question to model the corrosion process and derive an equation to relate corrosion coverage and corrosion mass. The resultant equation is named coverage-mass equation, abbreviated as C-M equation. We also suggest corrosion mass at 50% coverage, termed as half-coverage mass Mcorro50%, as an inhomogeneity parameter to quantify corrosion inhomogeneity. The equation is confirmed and the half-coverage mass Mcorro50% is justified in our experiments of iron corrosion in five aqueous media, normal saline, phosphate-buffered saline, Hank’s solution, deionized water and artificial seawater, where the former three ones are biomimetic and very important in studies of biomedical materials. The half-coverage mass Mcorro50% is proved to be more comprehensive and mathematically convergent than the traditional pitting factor. Iron corrosion is detected using visual observation, scanning electron microscopy with a build-in energy dispersive spectrometer, inductive coupled plasma emission spectrometry and electrochemical measurements. Both rates and inhomogeneity extents of iron corrosion are compared among the five aqueous media. The factors underlying the medium effects on corrosion rate and inhomogeneity are discussed and interpreted. Corrosion rates of iron in the five media differ about 7-fold, and half-coverage mass values differ about 300 000-fold. The fastest corrosion and the most significant inhomogeneity occur both in biomimetic media, but not the same one. The new equation (C-M equation) and the new quantity (half-coverage mass) are stimulating for dealing with a dynamic and stochastic process with global inhomogeneity including but not limited to metal corrosion. The findings are particularly meaningful for research and development of next-generation biodegradable materials. Graphical Abstract

Project description:Currently, sulfate-reducing bacteria (SRB) is regarded as the main culprit of microbiologically influenced corrosion (MIC), mainly due to the low reported corrosion rates of other microorganisms. For example, the highest reported corrosion rate for methanogens is 0.065 mm/yr. However, by investigating methanogen-induced microbiologically influenced corrosion (Mi-MIC) using an in-house developed versatile multiport flow test column, extremely high corrosion rates were observed. We analyzed a large set of carbon steel beads, which were sectionally embedded into the test columns as substrates for iron-utilizing methanogen Methanobacterium IM1. After 14 days of operation using glass beads as fillers for section separation, the highest average corrosion rate of Methanobacterium IM1 was 0.2 mm/yr, which doubled that of Desulfovibrio ferrophilus IS5 and Desulfovibrio alaskensis 16109 investigated at the same conditions. At the most corroded region, nearly 80% of the beads lost 1% of their initial weight (fast-corrosion), resulting in an average corrosion rate of 0.2 mm/yr for Methanobacterium IM1-treated columns. When sand was used as filler material to mimic sediment conditions, average corrosion rates for Methanobacterium IM1 increased to 0.3 mm/yr (maximum 0.52 mm/yr) with over 83% of the beads having corrosion rates above 0.3 mm/yr. Scanning electron images of metal coupons extracted from the column showed methanogenic cells were clustered close to the metal surface. Methanobacterium IM1 is a hydrogenotrophic methanogen with higher affinity to metal than H2. Unlike SRB, Methanobacterium IM1 is not restricted to the availability of sulfate concentration in the environment. Thus, the use of the multiport flow column provided a new insight on the corrosion potential of methanogens, particularly in dynamic conditions, that offers new opportunities for monitoring and development of mitigation strategies. Overall, this study shows (1) under certain conditions methanogenic archaea can cause higher corrosion than SRB, (2) specific quantifications, i.e., maximum, average, and minimum corrosion rates can be determined, and (3) that spatial statistical evaluations of MIC can be carried out.

Dataset Information

Visualization of aquaionic splitting via iron corrosion.

Publications

Visualization of aquaionic splitting via iron corrosion.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets