A Process Optimization and Performance Study of Environmentally Friendly Waste Newspaper/Polypropylene Film Layered Composites.

ABSTRACT: Waste newspaper are currently used in a single way and have low utilization rates. In this paper, the optimal process of preparing environmentally friendly layered composites by using waste newspaper combined with polypropylene film lamination was studied. The effects of hot-pressing temperature, hot-pressing time and paper content on the properties of the composites were analyzed. The results showed that under the process conditions of hot-pressing temperature 180 °C, compression time 20 min and paper content 66.7%, the obtained composite material had a flexural strength of 126 MPa, a tensile strength of 95 MPa, an impact strength of 5.3 kJ/m2 and a water absorption thickness expansion ratio of 3.2%. Tensile performance increased by 164% compared to the original waste newspaper. Compared to our previous work, the hot processing time had been cut in half and costs were lower. In terms of creep properties, the unrecoverable strain rate was reduced by 57.5% compared to pure polypropylene. The results show that the material can maintain excellent flexural strength, tensile strength and water absorption performance while making good use of waste newspaper.

SUBMITTER: Guan N

PROVIDER: S-EPMC7013860 | biostudies-literature | 2020 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

A Process Optimization and Performance Study of Environmentally Friendly Waste Newspaper/Polypropylene Film Layered Composites.

Guan Neng N Hu Chuanshuang C Guan Litao L Zhang Weiwei W Yun Hong H Hu Xiaojing X

Materials (Basel, Switzerland) 20200116 2

Waste newspaper are currently used in a single way and have low utilization rates. In this paper, the optimal process of preparing environmentally friendly layered composites by using waste newspaper combined with polypropylene film lamination was studied. The effects of hot-pressing temperature, hot-pressing time and paper content on the properties of the composites were analyzed. The results showed that under the process conditions of hot-pressing temperature 180 °C, compression time 20 min an ...[more]

PMID: 31963115

Similar Datasets

Project description:This work focuses on the manufacturing and characterization of highly environmentally friendly lightweight sandwich structures based on polylactide (PLA) honeycomb cores and PLA-flax fabric laminate skins or facings. PLA honeycombs were manufactured using PLA sheets with different thicknesses ranging from 50 to 500 μm. The PLA sheets were shaped into semi-hexagonal profiles by hot-compression molding. After this stage, the different semi-hexagonal sheets were bonded together to give hexagonal panels. The skins were manufactured by hot-compression molding by stacking two Biotex flax/PLA fabrics with 40 wt% PLA fibers. The combined use of temperature (200 °C), pressure, and time (2 min) allowed PLA fibers to melt, flow, and fully embed the flax fabrics, thus leading to thin composite laminates to be used as skins. Sandwich structures were finally obtained by bonding the PLA honeycomb core with the PLA-flax skins using an epoxy adhesive. A thin PLA nonwoven was previously attached to the external hexagonal PLA core, to promote mechanical interlock between the core and the skins. The influence of the honeycomb core thickness on the final flexural and compression properties was analyzed. The obtained results indicate that the core thickness has a great influence on the flexural properties, which increases with core thickness; nevertheless, as expected, the bonding between the PLA honeycomb core and the skins is critical. Excellent results have been obtained with 10 and 20 mm thickness honeycombs with a core shear of about 0.60 and facing bending stresses of 31-33 MPa, which can be considered as candidates for technical applications. The ultimate load to the sample weight ratio reached values of 141.5 N·g-1 for composites with 20 mm thick PLA honeycombs, which is comparable to other technical composite sandwich structures. The bonding between the core and the skins is critical as poor adhesion does not allow load transfer and, while the procedure showed in this research gives interesting results, new developments are necessary to obtain standard properties on sandwich structures.

Dataset Information

A Process Optimization and Performance Study of Environmentally Friendly Waste Newspaper/Polypropylene Film Layered Composites.

Publications

A Process Optimization and Performance Study of Environmentally Friendly Waste Newspaper/Polypropylene Film Layered Composites.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets