Carbonization and Preparation of Nitrogen-Doped Porous Carbon Materials from Zn-MOF and Its Applications.

ABSTRACT: Nitrogen-doped porous carbon (NPC) materials were successfully synthesized via a Zn-containing metal-organic framework (Zn-MOF). The resulting NPC materials are characterized using various physicochemical techniques which indicated that the NPC materials obtained at different carbonization temperatures exhibited different properties. Pristine MOF morphology and pore size are retained after carbonization at particular temperatures (600 °C-NPC600 and 800 °C-NPC800). NPC800 material shows an excellent surface area 1192 m2/g, total pore volume 0.92 cm3/g and displays a higher CO2 uptake 4.71 mmol/g at 273 k and 1 bar. Furthermore, NPC600 material displays good electrochemical sensing towards H2O2. Under optimized conditions, our sensor exhibited a wide linearity range between 100 µM and 10 mM with a detection limit of 27.5 µM.

SUBMITTER: Sivasankar K

PROVIDER: S-EPMC7013983 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Catalytic oxidative dehydrogenation of N-heterocycles with nitrogen/phosphorus co-doped porous carbon materials.

Project description:A metal-free oxidative dehydrogenation of N-heterocycles utilizing a nitrogen/phosphorus co-doped porous carbon (NPCH) catalyst is reported. The optimal material is robust against traditional poisoning agents and shows high antioxidant resistance. It exhibits good catalytic performance for the synthesis of various quinoline, indole, isoquinoline, and quinoxaline 'on-water' under air atmosphere. The active sites in the NPCH catalyst are proposed to be phosphorus and nitrogen centers within the porous carbon network.

| S-EPMC9200114 | biostudies-literature

Biomass Juncus Derived Nitrogen-Doped Porous Carbon Materials for Supercapacitor and Oxygen Reduction Reaction.

Project description:Juncus is a perennial herb aquatic plant found worldwide, with high reproductive ability in warm regions. It has three-dimensional hierarchical porous triangular networks structures composited of tubular fibers. Here, juncus derived nitrogen-doped porous carbon (NDPC) was prepared by mixing juncus and ZnCl2 through one-step pyrolysis and activation which is a low-cost, simple, and environmentally friendly method. The NDPC had hierarchical porous structures and a high specific surface area and was applied for supercapacitor and oxygen reduction reaction (ORR). The resulted NDPC-3-800 was prepared by mixing juncus with ZnCl2 at a mass ratio of 1:3 and then carbonized at 800°C, it was used as electrode material of a supercapacitor. The supercapacitor exhibited excellent specific capacitance of 290.5 F g-1 and 175.0 F g-1 in alkaline electrolyte at the current densities of 0.5 A g-1 and 50 A g-1, respectively. The supercapacitor showed good cycle stability, and the capacitance was maintained at 94.5% after 10,000 cycles. The NDPC-5-800 was prepared by mixing juncus with ZnCl2 at a mass ratio of 1:5 and then carbonized at 800°C. It exhibited outstanding ORR catalytic activity and stability attributing to their high specific surface area and abundant actives sites. The juncus can derive various materials for application in different fields.

| S-EPMC7174754 | biostudies-literature

Nitrogen-Doped Porous Carbon Materials Derived from Graphene Oxide/Melamine Resin Composites for CO2 Adsorption.

Project description:CO2 adsorption in porous carbon materials has attracted great interests for alleviating emission of post-combustion CO2. In this work, a novel nitrogen-doped porous carbon material was fabricated by carbonizing the precursor of melamine-resorcinol-formaldehyde resin/graphene oxide (MR/GO) composites with KOH as the activation agent. Detailed characterization results revealed that the fabricated MR(0.25)/GO-500 porous carbon (0.25 represented the amount of GO added in wt.% and 500 denoted activation temperature in °C) had well-defined pore size distribution, high specific surface area (1264 m2·g-1) and high nitrogen content (6.92 wt.%), which was mainly composed of the pyridinic-N and pyrrolic-N species. Batch adsorption experiments demonstrated that the fabricated MR(0.25)/GO-500 porous carbon delivered excellent CO2 adsorption ability of 5.21 mmol·g-1 at 298.15 K and 500 kPa, and such porous carbon also exhibited fast adsorption kinetics, high selectivity of CO2/N2 and good recyclability. With the inherent microstructure features of high surface area and abundant N adsorption sites species, the MR/GO-derived porous carbon materials offer a potentially promising adsorbent for practical CO2 capture.

| S-EPMC8434559 | biostudies-literature

Preparation of Activated Carbon Doped with Graphene Oxide Porous Materials and Their High Gas Adsorption Performance.

Project description:It is still a great challenge to develop a new porous carbon adsorbent with excellent separation performance and to recover low-concentration CH4 in coal mine gas. This work provides a new idea for the study of CH4 adsorption on activated carbon (AC) composites. Composite materials with microporous structures were prepared from coconut-shell activated carbon (CAC) doped with graphene oxide (GO) by a chemical activation process in this paper. The expansion and dissociation of GO at high temperatures indirectly improve the specific surface area (SSA) of the composite. The interlayer aggregation is reduced, the activation effect is improved, and a new low-cost adsorption material is prepared. The SSA of CAC-50 is more than 3000 m2·g-1. A high SSA and a narrow pore size distribution lead to a higher total adsorption capacity of CH4. The breakthrough test also confirmed that AC/GOs had a better adsorption capacity for CH4. The separation performance of the CH4/N2 mixture is not good at room temperature, which is due to the influence of a high SSA and average pore size. As a low-cost and rich material, CAC has a wide range of application prospects. The composite is a potential material for recovering low-concentration CH4 from the coal mine, which is worthy of attention. In the future, the selectivity of AC/GOs to CH4 can be increased by loading functional groups or modification.

| S-EPMC8340399 | biostudies-literature

Preparation of 2D Carbon Materials by Chemical Carbonization of Cellulosic Materials to Avoid Thermal Decomposition.

Project description:Cellulosic materials, including regenerated cellulose, are promising precursors for a variety of carbon materials. However, thermal decomposition, typically accompanying carbonization at high temperatures, hinders cellulosic materials from being efficiently carbonized (i.e., very low carbon yields). Herein, this study presents a new and efficient method for the preparation of porous 2D carbon materials from sheet-like cellulosic materials, such as papers and fabrics, involving a catalyzed chemical reaction at high temperatures without thermal decomposition. Thus, cellulosic materials are treated with sulfonic acid solutions and significantly dehydrated at high temperatures via evaporation of water. As a result, black materials are obtained at a weight near the theoretical carbon content of cellulose and remain in the carbonized materials. The as-obtained porous 2D carbon materials are flexible and suitable for a wide range of applications such as in electrodes and gas absorbents.

| S-EPMC6607140 | biostudies-literature

Upcycling of polyurethane waste by mechanochemistry: synthesis of N-doped porous carbon materials for supercapacitor applications.

Project description:We developed an upcycling process of polyurethane obtaining porous nitrogen-doped carbon materials that were applied in supercapacitor electrodes. In detail, a mechanochemical solvent-free one-pot synthesis is used and combined with a thermal treatment. Polyurethane is an ideal precursor already containing nitrogen in its backbone, yielding nitrogen-doped porous carbon materials with N content values of 1-8 wt %, high specific surface area values of up to 2150 m2·g-1 (at a N content of 1.6 wt %) and large pore volume values of up to 0.9 cm3·g-1. The materials were tested as electrodes for supercapacitors in aqueous 1 M Li2SO4 electrolyte (100 F·g-1), organic 1 M TEA-BF4 (ACN, 83 F·g-1) and EMIM-BF4 (70 F·g-1).

| S-EPMC6693373 | biostudies-literature

Green synthesis of nitrogen-doped self-assembled porous carbon-metal oxide composite towards energy and environmental applications.

Project description:Increasing environmental pollution, shortage of efficient energy conversion and storage devices and the depletion of fossil fuels have triggered the research community to look for advanced multifunctional materials suitable for different energy-related applications. Herein, we have discussed a novel and facile synthesis mechanism of such a carbon-based nanocomposite along with its energy and environmental applications. In this present work, nitrogen-doped carbon self-assembled into ordered mesoporous structure has been synthesized via an economical and environment-friendly route and its pore generating mechanism depending on the hydrogen bonding interaction has been highlighted. Incorporation of metal oxide nanoparticles in the porous carbon network has significantly improved CO2 adsorption and lithium storage capacity along with an improvement in the catalytic activity towards Oxygen Reduction Reaction (ORR). Thus our present study unveils a multifunctional material that can be used in three different fields without further modifications.

| S-EPMC6435743 | biostudies-literature

Preparation of palladated porous nitrogen-doped carbon using halloysite as porogen: disclosing its utility as a hydrogenation catalyst.

Project description:In this article, halloysite nanoclay (Hal) was used as porogen for the synthesis of nitrogen doped porous carbon material with high specific surface area and pore volume. To this purpose, polymerization of melamine and terephthalaldehyde (MT) was performed in the presence of amine-functionalized carbon coated Hal (Hal@Glu-2N) that was prepared from hydrothermal treatment of Hal and glucose. Then, the prepared nanocomposite was palladated and carbonized to afford Pd@Hal@C. To further improve the textural properties of the nanocomposite, and introduce more pores in its structure, Hal nanotubes were etched. The characterization of the resulting compound, Pd@C, and comparing it with Pd@Hal@C, showed that etching of Hal significantly increased the specific surface area and pore volume in Pd@C. Pd@C was successfully used as a heterogeneous catalyst for promoting hydrogenation of nitroarens in aqueous media using hydrogen with atmospheric pressure as a reducing agent. The comparison of the structural features and catalytic activity of the catalyst with some control catalysts, including, Pd@Hal, Pd@Hal@Glu, Pd@Hal@Glu-MT and Pd@Hal@C confirmed that nitrogen groups in C could improve the Pd anchoring and suppress its leaching, while etching of Hal and introduction of more pores could enhance the catalytic activity through facilitating the mass transfer.

| S-EPMC7005045 | biostudies-literature

MOF-derived nitrogen-doped porous carbon nanofibers with interconnected channels for high-stability Li<sup>+</sup>/Na<sup>+</sup> battery anodes.

Project description:Heteroatom-doped porous carbon materials have been widely used as anode materials for Li-ion and Na-ion batteries, however, improving the specific capacity and long-term cycling stability of ion batteries remains a major challenge. Here, we report a facile based metal-organic framework (MOFs) strategy to synthesize nitrogen-doped porous carbon nanofibers (NCNFs) with a large number of interconnected channels that can increase the contact area between the material and the electrolyte, shorten the diffusion distance between Li+/Na+ and the electrolyte, and relieve the volume expansion of the electrode material during cycling; the doping of nitrogen atoms can improve the conductivity and increase the active sites of the carbon material, can also affect the microstructure and electron distribution of the electrode material, thereby improving the electrochemical performance of the material. As expected, the obtained NCNFs-800 exhibited excellent electrochemical performance with high reversible capacity (for Li+ battery anodes: 1237 mA h g-1 at 100 mA g-1 after 200 cycles, for Na+ battery anodes: 323 mA h g-1 at 100 mA g-1 after 150 cycles) and long-term cycling stability (for Li+ battery anodes: 635 mA h g-1 at 2 A g-1 after 5000 cycles, for Na+ battery anodes: 194 mA h g-1 at 2 A g-1 after 5000 cycles).

| S-EPMC9926884 | biostudies-literature

Influence of carbonization conditions on luminescence and gene delivery properties of nitrogen-doped carbon dots.

Project description:Carbon dots (CDs) have been intensively investigated due to their unique photoluminescence (PL) properties that are improved through surface passivation with nitrogen-containing groups. Recently, gene delivery applications emerged as passivation of CDs may yield positively charged nanoparticles that can interact with negatively charged nucleic acids. However previous work in the field focused on the use of high molecular weight polyamines for CD passivation, posing the problem of the separation of nanoparticles from residual polymer that is harmful to cells. In this work, cationic CDs were prepared by pyrolysis of citric acid/bPEI600 (1/4, w/w) so unreacted low molecular weight reagents could be conveniently eliminated by extensive dialysis. Various reaction conditions and activation modes were evaluated and eleven CDs that exhibited superior solubility in water were produced. All the nanoparticles were characterized with respect to their physical, optical and PL properties and their ability to deliver plasmid DNA to mammal cells was evaluated. Despite their similar physical properties, the CDs displayed marked differences in their gene delivery efficiency. CDs produced under microwave irradiation in a domestic oven were revealed to be superior to all the other nanoparticles produced in this study and compared to the gold standard transfection reagent bPEI25k, with an optimal CD/pDNA w/w ratio that was significantly down shifted, as was the associated cytotoxicity.

| S-EPMC9060250 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data