Preparation of Scalable Silica-Coated Iron Oxide Nanoparticles for Nanowarming.

ABSTRACT: Cryopreservation technology allows long-term banking of biological systems. However, a major challenge to cryopreserving organs remains in the rewarming of large volumes (>3 mL), where mechanical stress and ice formation during convective warming cause severe damage. Nanowarming technology presents a promising solution to rewarm organs rapidly and uniformly via inductive heating of magnetic nanoparticles (IONPs) preloaded by perfusion into the organ vasculature. This use requires the IONPs to be produced at scale, heat quickly, be nontoxic, remain stable in cryoprotective agents (CPAs), and be washed out easily after nanowarming. Nanowarming of cells and blood vessels using a mesoporous silica-coated iron oxide nanoparticle (msIONP) in VS55, a common CPA, has been previously demonstrated. However, production of msIONPs is a lengthy, multistep process and provides only mg Fe per batch. Here, a new microporous silica-coated iron oxide nanoparticle (sIONP) that can be produced in as little as 1 d while scaling up to 1.4 g Fe per batch is presented. sIONP high heating, biocompatibility, and stability in VS55 is also verified, and the ability to perfusion load and washout sIONPs from a rat kidney as evidenced by advanced imaging and ICP-OES is demonstrated.

SUBMITTER: Gao Z

PROVIDER: S-EPMC7029634 | biostudies-literature | 2020 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Preparation of Scalable Silica-Coated Iron Oxide Nanoparticles for Nanowarming.

Gao Zhe Z Ring Hattie L HL Sharma Anirudh A Namsrai Baterdene B Tran Nam N Finger Erik B EB Garwood Michael M Haynes Christy L CL Bischof John C JC

Advanced science (Weinheim, Baden-Wurttemberg, Germany) 20200107 4

Cryopreservation technology allows long-term banking of biological systems. However, a major challenge to cryopreserving organs remains in the rewarming of large volumes (>3 mL), where mechanical stress and ice formation during convective warming cause severe damage. Nanowarming technology presents a promising solution to rewarm organs rapidly and uniformly via inductive heating of magnetic nanoparticles (IONPs) preloaded by perfusion into the organ vasculature. This use requires the IONPs to be ...[more]

PMID: 32099753

Similar Datasets

Project description:New preservation technologies may allow for organ banking similar to blood and biomaterial banking approaches. Using cryoprotective agents (CPAs), aqueous solutions with organic components such as DMSO, propylene glycol, and added salts and sugars, organs can be used to vitrify and store organs at -140 °C. When needed, these organs can be rewarmed in a rapid and uniform manner if CPAs are supplemented with iron oxide nanoparticles (IONPs) in an applied radiofrequency field. Speed and uniformity of warming are both IONP concentration and CPA suspension dependent. Here we present a coating method of small molecule phosphonate linker (PLink) and biocompatible polymer (i.e. polyethylene glycol PEG) that tunes stability and increases the maximum allowable concentration of IONPs in CPA suspension. PLink contains a phosphonate 'anchor' for high irreversible binding to iron oxide and a carboxylic acid 'handle' for ligand attachment. PLink-PEG removes and replaces the initial coating layer of commercially available IONPs (EMG1200 (hydrophobic) and EMG308 (hydrophilic) Ferrotec, Inc., increasing colloidal stability and decreasing aggregation in both water and CPAs, (verified with dynamic light scattering) from minutes (uncoated) to up to 6 days. Heating properties of EMG1200, specific absorption rate (SAR), measured using an applied field of 360 kHz and 20 kA m-1, increased from 20 to 180 W per g Fe with increasing PLink-PEG5000. PEG replacing the initially hydrophobic coating decreased aggregation in water and CPA, consistent with earlier studies on heating performance. Furthermore, although the size is minimized at 0.20 mol PEG per g Fe, heating is not maximized until concentrations above 0.43 mol PEG per g Fe on EMG1200. SAR on hydrophilic EMG308 was preserved at 400 W per g Fe regardless of the amount of PLink added to the core. Herein concentrations of IONP in VS55 (common CPA) significantly above our previous capabilities, sIONP at 10 mg Fe per mL, was reached, 25 mg Fe per mL of 308-PEG5000 and 60 mg Fe per mL of 1200-PEG5000, approaching stock EMG308 in water, 60 mg Fe per mL. Furthermore, at these concentrations cryopreserved Human dermal fibroblast cells were successfully nanowarmed (at applied fields described above), with higher viability as compared to convective rewarming in a water bath and heating rate close to 200 °C min-1, 2.5 times faster than our current system. Using PLink as the coating method allowed for higher concentrations of IONPs to be successfully suspended in CPA without affecting the heating ability. Additionally, the model ligand, PEG, allowed for increased stability over time in nanowarming experiments.

Dataset Information

Preparation of Scalable Silica-Coated Iron Oxide Nanoparticles for Nanowarming.

Publications

Preparation of Scalable Silica-Coated Iron Oxide Nanoparticles for Nanowarming.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets