Enhanced visible-light photocatalytic activity of anatase-rutile mixed-phase nano-size powder given by high-temperature heat treatment.

ABSTRACT: Nano-size EVONIK AEROXIDE® P25 titanium dioxide, TiO2, powder was heat-treated at temperatures, 700-900°C, in air. An X-ray diffraction study showed that the P25 powder is composed of approximately 20 and approximately 80 mass% of rutile and anatase phases, respectively. It was also shown that the transformation from anatase to rutile induced by high-temperature heat treatment was almost completed at 750°C, whereas a small amount (less than 3 mass%) of anatase phase was still left even in the powder heat-treated at 900°C. The transformation behaviour was consistent with results obtained by Raman scattering spectroscopy. Raman experiments also indicated that high-temperature heating induced the formation of oxide ion vacancies. Powders were dispersed in methyl orange (MO) aqueous solution, and the bleach rate of MO was measured to evaluate photocatalytic activity under ultraviolet (UV)- and visible-light irradiation. After the heat treatment, the UV-light photocatalytic performance sharply deteriorated. Interestingly, visible-light photocatalytic activity was enhanced by high-temperature heating and reached the highest performance for an 800°C-heated sample, indicating that the P25 powder obtained high visible-light photocatalytic performance after heat treatment. Even after 900°C heat treatment, the photocatalytic performance was higher than that of as-received powder. Enhancement of photocatalytic activities was discussed in relation to visible light absorption and charge carrier transfer.

SUBMITTER: Ishigaki T

PROVIDER: S-EPMC7029928 | biostudies-literature | 2020 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Enhanced visible-light photocatalytic activity of anatase-rutile mixed-phase nano-size powder given by high-temperature heat treatment.

Ishigaki Takamasa T Nakada Yusuke Y Tarutani Naoki N Uchikoshi Tetsuo T Tsujimoto Yoshihiro Y Isobe Masaaki M Ogata Hironori H Zhang Chenning C Hao Dong D

Royal Society open science 20200115 1

Nano-size EVONIK AEROXIDE<sup>®</sup> P25 titanium dioxide, TiO<sub>2</sub>, powder was heat-treated at temperatures, 700-900°C, in air. An X-ray diffraction study showed that the P25 powder is composed of approximately 20 and approximately 80 mass% of rutile and anatase phases, respectively. It was also shown that the transformation from anatase to rutile induced by high-temperature heat treatment was almost completed at 750°C, whereas a small amount (less than 3 mass%) of anatase phase was sti ...[more]

PMID: 32218970

Similar Datasets

Project description:Titanium dioxide is an ubiquitous photocatalyst in water-cleaning technologies, being presently the most promising tools to resolve the global issue of sewage treatment. In this framework, titanium dioxide-graphene nanocomposites are discussed as promising visible-light activated photocatalysts but little is hitherto known about the surface and interface chemistry bridging the metal oxide and carbon phases. In an attempt to spotlight this overlooked issue, we herein designed two different hybrid nanocomposites through covalent grafting and growth of titanium dioxide clusters on graphene oxide and on phosphorylated graphene oxide, which affords GO@TiO2 and PGO@TiO2, respectively. While anatase could be selectively harvested on the surface of GO@TiO2, biphasic anatase-rutile nucleates could be obtained on PGO@TiO2. Thermal annealing treatments improve the metal oxide crystallization and further remove oxygenated groups from the surface of graphene. The interfacial stability of these photocatalysts was also investigated under irradiation, with the graphene support being sensitive to the proximal presence of titanium dioxide. The resulting nanocomposites were also assessed for methylene blue removal through adsorption and photocatalysis. Regardless of their composition, superior photoactivity was noticed for the nanocomposites compared to commercially available degussa that display marginal visible-light photoactivity (11% removal). Within our study, PGO@TiO2-500 stands as the most active catalyst, allowing nearly quantitative removal of the pollutant from water. The superior performance of PGO@TiO2-500 can be explained by the highest stability reached through P-O-Ti bonding, its improved crystallinity, and the reduction of the graphene surface during thermal treatment. On a whole, this study provides a blueprint for comparing semiconducting metal oxide grown on tuneable surface-interfacial graphene environments and highlights the utility of surface-engineering graphene sheets to access efficient visible-light oxidation photocatalysts.

Dataset Information

Enhanced visible-light photocatalytic activity of anatase-rutile mixed-phase nano-size powder given by high-temperature heat treatment.

Publications

Enhanced visible-light photocatalytic activity of anatase-rutile mixed-phase nano-size powder given by high-temperature heat treatment.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets