High-Performance Ambient-Condition-Processed Polymer Solar Cells and Organic Thin-Film Transistors.

ABSTRACT: Large-scale commercial synthesis of bulk-heterojunction (BHJ) solar cell materials is very challenging and both time and energy consuming. Synthesis of π-conjugated polymers (CPs) with uniform batch-to-batch molecular weight and low dispersity is a key requirement for better reproducibility of high-efficiency polymer solar cells. Herein, a conjugated polymer (CP) PTB7-Th, well known for its high performance, has been synthesized with high molecular weight and low dispersity in a closed microwave reactor. The microwave reaction procedure is known to be more controlled and consumes less energy. The precursors were strategically reacted for different reaction time durations to obtain the optimum molecular weight. All different CPs were well characterized using 1H NMR, gel permeation chromatography (GPC), UV-vis, photoluminescence (PL), electron spin resonance (ESR), and Raman spectroscopy, whereas the film morphology was extensively studied via atomic force microscopy (AFM) and grazing incidence X-ray diffraction (GIXRD) techniques. The effect of molecular weight on a conventional BHJ solar cell with PC71BM acceptor was investigated to derive systematic structure-property relationships. The CP obtained after 35 min of reaction time and integrated into BHJ devices under ambient conditions provided the best performance with a power conversion efficiency (PCE) of 8.09%, which was quite similar to the results of CPs synthesized via a thermal route. An enhanced PCE of 8.47% was obtained for the optimized polymer (35 min microwave reaction product) when device fabrication was carried out inside a glovebox. The organic thin-film transistor (OTFT) device with the microwave-synthesized CP displayed better hole mobility (0.137 cm2 V-1 s-1) as compared to that with the thermally synthesized CP. This study also proved that the device stability and reproducibility of the microwave-synthesized CP were much better and more consistent than those of the thermally developed CP.

SUBMITTER: Garai R

PROVIDER: S-EPMC7033982 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:The key impact and significance of a multilayer polymer-based dielectric system on the remarkable photoresponse properties of zinc phthalocyanine (ZnPc)-based photosensitive organic field-effect transistors (PS-OFETs) have been systematically analyzed at various incident optical powers. A combination of inorganic aluminum oxide (Al2O3) and organic nonpolar poly(methyl methacrylate) (PMMA) is used as the bilayer dielectric configuration, whereas in the trilayer dielectric system, a bilayer polymer dielectric, consisting of PMMA, as the low-k dielectric polymer, on top of poly(vinyl alcohol) (PVA), the high-k polar dielectric, has been fabricated along with Al2O3 as the third layer. Before fabricating the OFETs, a systematic optimization of the nature of growth of the ZnPc molecules, deposited on PMMA-coated glass substrates at different substrate temperatures (T s) was performed and examined by atomic-force microscopy, field-emission scanning electron microscopy, X-ray diffraction, and Raman analysis. At 90 °C, the fabricated PS-OFETs with the Al2O3/PVA/PMMA trilayer dielectric configuration showed the best p-channel behavior, with an enhanced and remarkable photoresponsivity of R ∼ 9689.39 A W-1 compared to that of the Al2O3/PMMA bilayer dielectric system (R ∼ 2679.40 A W-1) due to the polarization of the dipoles inside the polar PVA dielectric, which increases the charge transport through the channel. The charge carrier mobility of the device also improved by one order (μh ∼ 1.3 × 10-2 cm2 V-1 s-1) compared to that of the bilayer dielectric configuration (μh ∼ 3.5 × 10-3 cm2 V-1 s-1). The observed specific detectivity (D*) and NEP values of the bilayer dielectric system were 6.01 × 1013 Jones and 2.655 × 10-17 W Hz-1/2, whereas for the trilayer dielectric system, the observed D* and NEP values were 5.13 × 1014 Jones and 1.043 × 10-17 W Hz-1/2, respectively. Additionally, the operating voltage of each of the fabricated devices was also very low (-10 V) due to the influence of the inorganic high-k Al2O3 dielectric layer. The electrical stability of all of the fabricated devices was also investigated by bias stress analysis under both light and dark conditions in vacuum. To the best of our knowledge, the photoresponsivity (R) reported here with an Al2O3/PVA/PMMA trilayer dielectric configuration is the highest reported value for thin film-based PS-OFETs, at a remarkably low operating voltage of -10 V, on low-cost glass substrates without indium tin oxide or/and Si/SiO2.

Dataset Information

High-Performance Ambient-Condition-Processed Polymer Solar Cells and Organic Thin-Film Transistors.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets