Coupling of kenaf Biochar and Magnetic BiFeO3 onto Cross-linked Chitosan for Enhancing Separation Performance and Cr(VI) Ions Removal Efficiency.

ABSTRACT: Cr(VI) contamination has posed great threat to both the ecosystem and human health for its carcinogenic and mutagenic nature. A highly effective adsorbent for the removal of Cr(VI) was prepared and its adsorption mechanism was thoroughly discussed in this study. In detail, magnetic BiFeO3 and kenaf biochar were loaded on cross-linked chitosan to obtain chitosan-kenaf biochar@BiFeO3 (CKB) for improving adsorption capacity towards Cr(VI). The adsorption process of Cr(VI) onto CKB was evaluated as a function of the pH, the existence of competing ions, the initial concentration of Cr(VI) and contact time. The results show that CKB exhibits the highest adsorption capacity under the optimal pH 2.0. The presence of competing ions such as Ca2+, NO3-, SO42-, and Cl- decreases the adsorption capacity; among them, Ca2+ and NO3- show the greatest hindrance. By studying the effect of initial Cr(VI) concentration on the adsorption capacity, it was found that CKB in the solution was enough to remove Cr(VI) for all treatments (10-200 mg/L). The adsorption experimental data were well fitted with pseudo-first-order model, suggesting that chemisorption is not the dominant rate-limiting step. Freundlich isotherm model can better explain the adsorption process, indicating a non-ideal adsorption towards Cr(VI) on a heterogeneous surface of CKB. A 25-1 Fractional Factorial Design (FFD) showed that pH and initial concentration of Cr(VI) have significant influence on Cr(VI) adsorption in our reaction system. In general, excellent adsorption efficiency of CKB indicates that it may be a good candidate for the remediation of Cr(VI)-contaminating wastewater.

SUBMITTER: Zhou D

PROVIDER: S-EPMC7037466 | biostudies-literature | 2020 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Coupling of kenaf Biochar and Magnetic BiFeO3 onto Cross-linked Chitosan for Enhancing Separation Performance and Cr(VI) Ions Removal Efficiency.

Zhou Daixi D Xie Guangyu G Hu Xinjiang X Cai Xiaoxi X Zhao Yunlin Y Hu Xi X Jin Qi Q Fu Xiaohua X Tan Xiaofei X Liang Chong C Lai Kaiqi K Wang Hui H Tang Chunfang C

International journal of environmental research and public health 20200127 3

Cr(VI) contamination has posed great threat to both the ecosystem and human health for its carcinogenic and mutagenic nature. A highly effective adsorbent for the removal of Cr(VI) was prepared and its adsorption mechanism was thoroughly discussed in this study. In detail, magnetic BiFeO3 and kenaf biochar were loaded on cross-linked chitosan to obtain chitosan-kenaf biochar@BiFeO3 (CKB) for improving adsorption capacity towards Cr(VI). The adsorption process of Cr(VI) onto ...[more]

PMID: 32012702

Similar Datasets

Project description:Heavy metal ions in water refer to significant risks to the biological system due to their high toxicity. Therefore, the decontamination of water polluted by heavy metal ions attracts significant interest of researchers. Adsorption by nanomaterials has been a widely used technique for removing heavy metal ions from water. Chitosan was extracted from shrimp shellfish and mixed with laboratory-prepared AgNPs/GO in the ratio of 3 : 1. A series of tests evaluates the best condition of pH, amount of adsorbent, retention time, stirring speed, temp, and initial concentration. The research was conducted under various conditions. Langmuir, Freundlich, Tempkin, and Dubinin-Radushkevich isotherms were also tested. Also, the column adsorption experiment was carried out on industrial wastewater at different flow rates and column bed heights. The optimal values of the contact time, pH, and adsorbent dose of Cr(vi) were found to be 80 min, 4, and 0.1 g 100 mL-1, respectively, at room temperature (30 °C), agitation at 150 rpm, and initial concentration of 50 ppm. On the other hand, the optimal value of contact time, pH, and adsorbent dose of Fe(iii) were found to be 30 min, 6, and 0.02 g 100 mL-1, respectively, at room temp (30 °C) with a stirring speed of 250 rpm and an initial concentration of 40 ppm. For Cr(vi) and Fe(iii), equilibrium studies show that the data fit the Freundlich isotherm well (correlation coefficient, R 2 = 0.98) (III). A link between the pseudo-second order active model and data fitting the pseudo-first order active models were made. Within the intraparticle diffusion model, there are four stages that the mechanism must go through before it is at equilibrium. The adsorbent was tested in an industrial adsorbent column. This test proves that the nanocomposite's adsorption capacity can be restored by washing it with 0.1 M HCl, as shown by the periodicity test. After four cycles, the amount of Cr(vi) adsorbed on AgNPs/GO/chitosan was just 20%, which is insufficient for further adsorption experiments. Cr(vi) removal rates (%R) decreased slightly.

Dataset Information

Coupling of kenaf Biochar and Magnetic BiFeO3 onto Cross-linked Chitosan for Enhancing Separation Performance and Cr(VI) Ions Removal Efficiency.

Publications

Coupling of kenaf Biochar and Magnetic BiFeO<sub>3</sub> onto Cross-linked Chitosan for Enhancing Separation Performance and Cr(VI) Ions Removal Efficiency.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets