A Facile and Green Synthesis of a MoO2-Reduced Graphene Oxide Aerogel for Energy Storage Devices.

ABSTRACT: A simple, low cost, and "green" method of hydrothermal synthesis, based on the addition of l-ascorbic acid (l-AA) as a reducing agent, is presented in order to obtain reduced graphene oxide (rGO) and hybrid rGO-MoO2 aerogels for the fabrication of supercapacitors. The resulting high degree of chemical reduction of graphene oxide (GO), confirmed by X-Ray Photoelectron Spectroscopy (XPS) analysis, is shown to produce a better electrical double layer (EDL) capacitance, as shown by cyclic voltammetric (CV) measurements. Moreover, a good reduction yield of the carbonaceous 3D-scaffold seems to be achievable even when the precursor of molybdenum oxide is added to the pristine slurry in order to get the hybrid rGO-MoO2 compound. The pseudocapacitance contribution from the resulting embedded MoO2 microstructures, was then studied by means of CV and electrochemical impedance spectroscopy (EIS). The oxidation state of the molybdenum in the MoO2 particles embedded in the rGO aerogel was deeply studied by means of XPS analysis and valuable information on the electrochemical behavior, according to the involved redox reactions, was obtained. Finally, the increased stability of the aerogels prepared with l-AA, after charge-discharge cycling, was demonstrated and confirmed by means of Field Emission Scanning Electron Microscopy (FESEM) characterization.

SUBMITTER: Serrapede M

PROVIDER: S-EPMC7040781 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Green preparation of reduced graphene oxide for sensing and energy storage applications.

Project description:Preparation of graphene from chemical reduction of graphene oxide (GO) is recognized as one of the most promising methods for large-scale and low-cost production of graphene-based materials. This study reports a new, green, and efficient reducing agent (caffeic acid/CA) for GO reduction. The CA-reduced GO (CA-rGO) shows a high C/O ratio (7.15) that is among the best rGOs prepared with green reducing reagents. Electronic gas sensors and supercapacitors have been fabricated with the CA-rGO and show good performance, which demonstrates the potential of CA-rGO for sensing and energy storage applications.

| S-EPMC3986759 | biostudies-literature

Charge storage mechanisms of manganese oxide nanosheets and N-doped reduced graphene oxide aerogel for high-performance asymmetric supercapacitors.

Project description:Although manganese oxide- and graphene-based supercapacitors have been widely studied, their charge storage mechanisms are not yet fully investigated. In this work, we have studied the charge storage mechanisms of K-birnassite MnO2 nanosheets and N-doped reduced graphene oxide aerogel (N-rGOae) using an in situ X-ray absorption spectroscopy (XAS) and an electrochemical quart crystal microbalance (EQCM). The oxidation number of Mn at the MnO2 electrode is +3.01 at 0?V vs. SCE for the charging process and gets oxidized to +3.12 at +0.8?V vs. SCE and then reduced back to +3.01 at 0?V vs. SCE for the discharging process. The mass change of solvated ions, inserted to the layers of MnO2 during the charging process is 7.4??g?cm-2. Whilst, the mass change of the solvated ions at the N-rGOae electrode is 8.4??g?cm-2. An asymmetric supercapacitor of MnO2//N-rGOae (CR2016) provides a maximum specific capacitance of ca. 467?F?g-1 at 1?A?g-1, a maximum specific power of 39?kW?kg-1 and a specific energy of 40?Wh?kg-1 with a wide working potential of 1.6?V and 93.2% capacity retention after 7,500 cycles. The MnO2//N-rGOae supercapacitor may be practically used in high power and energy applications.

| S-EPMC5114613 | biostudies-literature

Development of hybrid materials based on sponge supported reduced graphene oxide and transition metal hydroxides for hybrid energy storage devices.

Project description:Earnest efforts have been taken to design hybrid energy storage devices using hybrid electrodes based on capacitive (rGO) and pseudocapacitive (Ni(OH)2 and Co(OH)2) materials deposited on the skeleton of 3D macroporous (indicate sponge material) sponge support. Conducting framework was formed by coating rGO on macroporous sponge on which subsequent deposition of Ni(OH)2 and Co(OH)2 was carried out. The synergetic combination of rGO and Ni(OH)2 or Co(OH)2) provides dual charge-storing mechanisms whereas 3D framework of sponge allows excellent accessibility of electrolyte to hybrid electrodes. Moreover, to further increase the energy density, hybrid devices have been fabricated with SP@rGO@Ni or SP@rGO@Co and SP@rGO as positive and negative electrodes, respectively. These hybrid devices operate with extended operating voltage windows and achieve remarkable electrochemical supercapacitive properties which make them truly promising energy storage devices for commercial production.

| S-EPMC4258650 | biostudies-literature

3D Printed Graphene Based Energy Storage Devices.

Project description:3D printing technology provides a unique platform for rapid prototyping of numerous applications due to its ability to produce low cost 3D printed platforms. Herein, a graphene-based polylactic acid filament (graphene/PLA) has been 3D printed to fabricate a range of 3D disc electrode (3DE) configurations using a conventional RepRap fused deposition moulding (FDM) 3D printer, which requires no further modification/ex-situ curing step. To provide proof-of-concept, these 3D printed electrode architectures are characterised both electrochemically and physicochemically and are advantageously applied as freestanding anodes within Li-ion batteries and as solid-state supercapacitors. These freestanding anodes neglect the requirement for a current collector, thus offering a simplistic and cheaper alternative to traditional Li-ion based setups. Additionally, the ability of these devices' to electrochemically produce hydrogen via the hydrogen evolution reaction (HER) as an alternative to currently utilised platinum based electrodes (with in electrolysers) is also performed. The 3DE demonstrates an unexpectedly high catalytic activity towards the HER (-0.46 V vs. SCE) upon the 1000th cycle, such potential is the closest observed to the desired value of platinum at (-0.25 V vs. SCE). We subsequently suggest that 3D printing of graphene-based conductive filaments allows for the simple fabrication of energy storage devices with bespoke and conceptual designs to be realised.

| S-EPMC5361393 | biostudies-literature

Facile Synthesis of Sn/Nitrogen-Doped Reduced Graphene Oxide Nanocomposites with Superb Lithium Storage Properties.

Project description:Sn/Nitrogen-doped reduced graphene oxide (Sn@N-G) composites have been successfully synthesized via a facile method for lithium-ion batteries. Compared with the Sn or Sn/graphene anodes, the Sn@N-G anode exhibits a superb rate capability of 535 mAh g-1 at 2C and cycling stability up to 300 cycles at 0.5C. The improved lithium-storage performance of Sn@N-G anode could be ascribed to the effective graphene wrapping, which accommodates the large volume change of Sn during the charge-discharge process, while the nitrogen doping increases the electronic conductivity of graphene, as well as provides a large number of active sites as reservoirs for Li+ storage.

| S-EPMC6723252 | biostudies-literature

Facile Green Approach for Developing Electrochemically Reduced Graphene Oxide-Embedded Platinum Nanoparticles for Ultrasensitive Detection of Nitric Oxide.

Project description:Nitric oxide (NO) plays a crucial and important role in cellular physiology and also acts as a signaling molecule for cancer in humans. However, conventional detection methods have their own limitations in the detection of NO at low concentrations because of its high reactivity and low lifetime. Herein, we report a strategy to fabricate Pt nanoparticle-decorated electrochemically reduced graphene oxide (erGO)-modified glassy carbon electrode (GCE) with efficiency to detect NO at a low concentration. For this study, Pt@erGO/GCE was fabricated by employing two different sequential methods [first GO reduction followed by Pt electrodeposition (SQ-I) and Pt electrodeposition followed by GO reduction (SQ-II)]. It was interesting to note that the electrocatalytic current response for SQ-I (184 μA) was ∼15 and ∼3 folds higher than those of the bare GCE (11.7 μA) and SQ-II (61.5 μA). The higher current response was mainly attributed to a higher diffusion coefficient and electrochemically active surface area. The proposed SQ-I electrode exhibited a considerably low LOD of 52 nM (S/N = 3) in a linear range of 0.25-40 μM with a short response time (0.7 s). In addition, the practical analytical applicability of the proposed sensor was also verified.

| S-EPMC8014916 | biostudies-literature

Synthesis of Polypyrrole/Reduced Graphene Oxide Hybrids via Hydrothermal Treatment for Energy Storage Applications.

Project description:Herein, we propose hydrothermal treatment as a facile and environmentally friendly approach for the synthesis of polypyrrole/reduced graphene oxide hybrids. A series of self-assembled hybrid materials with different component mass ratios of conductive polymer to graphene oxide was prepared. The morphology, porous structure, chemical composition and electrochemical performance of the synthesized hybrids as electrode materials for supercapacitors were investigated. Nitrogen sorption analysis at 77 K revealed significant changes in the textural development of the synthesized materials, presenting specific surface areas ranging from 25 to 199 m2 g-1. The combination of the pseudocapacitive polypyrrole and robust graphene material resulted in hybrids with excellent electrochemical properties, which achieved specific capacitances as high as 198 F g-1 at a current density of 20 A g-1 and retained up to 92% of their initial capacitance after 3000 charge-discharge cycles. We found that a suitable morphology and chemical composition are key factors that determine the electrochemical properties of polypyrrole/reduced graphene oxide hybrid materials.

| S-EPMC7287821 | biostudies-literature

3D free-standing nitrogen-doped reduced graphene oxide aerogel as anode material for sodium ion batteries with enhanced sodium storage.

Project description:Sodium ion batteries have drawn extensive attentions for large-scale energy storage to replace lithium ion batteries primarily due to the natural abundance of sodium resource and low cost, but their energy density and electrochemical performance are hindered by the sluggish diffusion kinetics of sodium ion. Herein, free-standing nitrogen-doped graphene aerogel has been fabricated via hydrothermal reaction as the potential anode material for sodium ion batteries. The three dimensional porous network structure of the graphene aerogel provides sufficient interstitial space for sodium ion accommodation, allowing fast and reversible ion intercalation/de-intercalation. The nitrogen doping could introduce defects on the graphene sheets, making the feasible transport of large-sized sodium ion. Benefiting from the effective structure and nitrogen doping, the obtained material demonstrates high reversible capacities, good cycling performance (287.9 mA h g-1 after 200 cycles at a current density of 100 mA g-1), especially superior rate capability (151.9 mA h g-1 at a high current density of 5 A g-1).

| S-EPMC5501838 | biostudies-literature

Ultra-Light Reduced Graphene Oxide Based Aerogel/Foam Absorber of Microwave Radiation.

Project description:We present the polarization-dependent highly absorptive in Ka-band composition of conventional polyurethane foam filled with in situ synthesized aerogel coated by reduced graphene oxide (rGO). The rGO-based aerogel was in situ prepared into the open-cell polyurethane foam (PUF) skeleton through a bidirectional freeze-drying process. The aerogel is composed of the flat lamellas stacks, possessing the anisotropic structure and unique electromagnetic properties. Further improvement of the electromagnetic shielding ability was possible by the rGO coating introduction as a coupling layer between PUF and rGO-based aerogel. This enhances the overall conductivity of the resulting composites: 1.41 + 3.33i S/m vs. 0.9 + 2.45i S/m for PUF loaded with in situ synthesized aerogel without rGO coating.With this mechanically robust plane easy to process coating one could achieve -20 dB by power with the record light structure (0.0462 g/cm²). That could compete in view of the weight per cm² even with graphene-based absorbers comprising either dielectric matching elements or back metal reflectors, or both.

| S-EPMC6356501 | biostudies-literature

3D hierarchical porous graphene aerogel with tunable meso-pores on graphene nanosheets for high-performance energy storage.

Project description:New and novel 3D hierarchical porous graphene aerogels (HPGA) with uniform and tunable meso-pores (e.g., 21 and 53 nm) on graphene nanosheets (GNS) were prepared by a hydrothermal self-assembly process and an in-situ carbothermal reaction. The size and distribution of the meso-pores on the individual GNS were uniform and could be tuned by controlling the sizes of the Co3O4 NPs used in the hydrothermal reaction. This unique architecture of HPGA prevents the stacking of GNS and promises more electrochemically active sites that enhance the electrochemical storage level significantly. HPGA, as a lithium-ion battery anode, exhibited superior electrochemical performance, including a high reversible specific capacity of 1100 mAh/g at a current density of 0.1 A/g, outstanding cycling stability and excellent rate performance. Even at a large current density of 20 A/g, the reversible capacity was retained at 300 mAh/g, which is larger than that of most porous carbon-based anodes reported, suggesting it to be a promising candidate for energy storage. The proposed 3D HPGA is expected to provide an important platform that can promote the development of 3D topological porous systems in a range of energy storage and generation fields.

| S-EPMC4585608 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data