Keratin/Hydrotalcites Hybrid Sponges as Promising Adsorbents for Cationic and Anionic Dyes.

ABSTRACT: In this work, keratin sponges were prepared by freeze-drying method and tested for adsorption of Azure A and Methyl Orange dyes. The obtained materials showed a porosity of 99.92% and a mean pore size dimension of about 91 ?m. The use of oxidized sucrose with a heating treatment at 150°C was demonstrated to be a useful crosslinking procedure alternative to the conventional glutaraldehyde. Keratin sponges showed a maximum adsorption capacity of 0.063 and of 0.037 mmol/g for Azure A and Methyl Orange, respectively. The absorption of the cationic dye Azure A onto keratin sponges was better described by Freundlich model while the isotherm adsorption of the anionic Methyl Orange was found to correlate with both Langmuir and Freundlich models. The mean free energies evaluated by using the D-R model indicated a physisorption of Methyl Orange and a chemisorptions of Azure A onto keratin sponges. Finally, the functionalization of keratin sponges with Zn Al hydrotalcites nanoparticles did not affect the adsorption performances of the adsorbent toward the cationic dye Azure A, while it improved those toward the anionic Methyl Orange, increasing the related removal efficiencies from 43 to 96%. Collectively, the reported data indicates that the combination of keratin with hydrotalcites nanoparticles is a good strategy to obtain more functional adsorbent materials of potential interest for water treatment and purification.

SUBMITTER: Posati T

PROVIDER: S-EPMC7047220 | biostudies-literature | 2020

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Keratin/Hydrotalcites Hybrid Sponges as Promising Adsorbents for Cationic and Anionic Dyes.

Posati Tamara T Listwan Arthur A Sotgiu Giovanna G Torreggiani Armida A Zamboni Roberto R Aluigi Annalisa A

Frontiers in bioengineering and biotechnology 20200221

In this work, keratin sponges were prepared by freeze-drying method and tested for adsorption of Azure A and Methyl Orange dyes. The obtained materials showed a porosity of 99.92% and a mean pore size dimension of about 91 μm. The use of oxidized sucrose with a heating treatment at 150°C was demonstrated to be a useful crosslinking procedure alternative to the conventional glutaraldehyde. Keratin sponges showed a maximum adsorption capacity of 0.063 and of 0.037 mmol/g for Azure A and Methyl Ora ...[more]

PMID: 32154225

Similar Datasets

Project description:Amongst many chemical pollutants that cause environmental pollution, the presence of organic dyes in water resources can cause substantial health issues. Thus, owing to their mutagenicity and their adverse effects on human health, environment, and animals, they must be removed from industrial wastewater. In this study, UiO-66 metal-organic framework, as well as composite nanoparticles with carbonaceous materials such as MWCNTs-COOH and graphene oxide (GO) with different molar ratios (2.9 and 5.8 wt.%), were synthesized through solvothermal method since carbonaceous materials are an emerging material that demonstrates improvement in the properties of adsorbents. Then, the synthesized materials were utilized as a solid adsorbent for removing four different dyes including; anionic methyl red (MR), anionic methyl orange (MO), cationic methylene blue (MB), and cationic malachite green (MG) prepared from distilled water. The properties of prepared adsorbents were characterized via X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), field emission scanning electron microscopy (FESEM), Photoluminescence spectroscopy (PL), Brunauer-Emmett-Teller (BET), as well as surface area analyzer and energy dispersive spectroscopy (EDS-MAP). Further, the influences of various factors including initial concentrations of the dyes and adsorption process time on adsorption of dyes were investigated. Adsorption experiments indicated that synthesized adsorbents exhibited the highest adsorption efficiency towards MR and MO dyes. Moreover, the experimental adsorption results revealed that MWCNTs-UiO-66 nanocomposites could adsorb 98% of MR and MO as well as 72% of MB and 46% of MG. Furthermore, the kinetic and stability of the materials over time were investigated. To reach a clear picture, adsorption experiments demonstrated that the amount of dye uptake on adsorbents was enhanced by increasing the contact time as well as uptake of materials with time were stable for both cationic and anionic dyes. The MR, MO, and MB adsorption isotherms were fitted with the Langmuir and Freundlich models. The Langmuir showed the highest agreement in these dyes and MWCNTs-UiO-66 (2.9 and 5.8 wt.%) exhibited a maximum adsorption capacity of 105.26 mg/g for MR, while the MG isotherm was in line with the Langmuir model.

Project description:Silica-supported hierarchical graphitic carbon sheltering cobalt nanoparticles Co-HGC@SiO2 (1) were prepared by pyrolysis at 850 °C of [Co(phen)(H2O)4]SO4·2H2O complex with silica in the presence of pyrene as a carbon source under nitrogen atmosphere. Nanocomposites (2) and (3) were obtained by acid treatment of (1) with HCl and HF acid, respectively. The nanocomposites showed rough hierarchical carbon microstructures over silica support decorated with irregular cobalt nanospheres and nanorods 50 to 200 nm in diameter. The nanoparticles consist of graphitic shells and cobalt cores. SEM, EDAX and TEM elemental mapping indicate a noticeable loss of cobalt in the case of (2) and loss of cobalt and silica in the case of (3) with an increase in porosity. Nanocomposite (3) showed the highest BET surface area 217.5 m2g-1. Raman spectrum shows defect D-band and graphitic G-band as expected in carbon nanostructures. PXRD reveals the presence of cobalt(0) nanoparticles. XPS indicates the presence of Co(II) oxides and the successful doping of nitrogen in the nanocomposites. Moreover, TEM elemental mapping provides information about the abundance of Si, Co, C, N and S elements in zones. Nanocomposite (1) showed maximum uptake capacity of 192.3 and 224.5 mg/g for crystal violet CV and methyl orange MO dyes, respectively. Nanocomposite (2) showed a capacity of 94.1 and 225.5 mg/g for CV and MO dyes, respectively. Nanocomposite (4) obtained after treatment of (1) with crystal violet proved successful adsorption of CV. Co-HGC (5) prepared without addition of silica has a capacity for CV equal to 192 mg/g, while it is 769.2 mg/g with MO. Electrostatics and π-π interactions of graphite and cobalt species in the nanocomposites with aromatic rings of cationic and anionic dyes are responsible for the adsorption. Yan et al. was the best model to describe column kinetics. The thomas column adsorption model showed that the maximum uptake capacity of (1) was 44.42 mg/g for CV and 32.62 mg/g for MO. for a column packed with 0.5 gm of (1) and dye concentration of 100 mg/L at a flow rate of 1 mL/min. The column was recycled three times with no noticeable clogging or degradation of nanocomposites. Thus, Co-HGC@SiO2 adsorbents can be used efficiently to treat water contaminated with cationic and anionic dyes.

Dataset Information

Keratin/Hydrotalcites Hybrid Sponges as Promising Adsorbents for Cationic and Anionic Dyes.

Publications

Keratin/Hydrotalcites Hybrid Sponges as Promising Adsorbents for Cationic and Anionic Dyes.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets