Neutron Total Scattering Studies of Group II Titanates (ATiO3, A2+ = Mg, Ca, Sr, Ba).

ABSTRACT: Neutron total scattering measurements were conducted on MgTiO3, CaTiO3, SrTiO3, and BaTiO3 to simultaneously investigate the local and average structure of these materials. The local structures of MgTiO3, CaTiO3, and SrTiO3 were well modelled using the refined average structural models: trigonal R[Formula: see text], orthorhombic Pbnm, and cubic Pm[Formula: see text]m respectively. However the local structure for BaTiO3, at both temperatures where the average structure is orthorhombic Amm2 and tetragonal P4mm, was best described by the rhombohedral R3m model. Only the R3m model was able to account for the observed displacement of titanium in the [111] direction. Furthermore, box-car type refinements were conducted. These refinements show that the coherence length of the rhombohedral distortion is around 10?Å, at larger r-ranges the local distortions become misaligned and average out to Amm2 and P4mm.

SUBMITTER: Culbertson CM

PROVIDER: S-EPMC7048731 | biostudies-literature | 2020 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Neutron Total Scattering Studies of Group II Titanates (ATiO3, A2+ = Mg, Ca, Sr, Ba).

Culbertson Charles M CM Flak Alexander T AT Yatskin Michael M Cheong Paul H-Y PH Cann David P DP Dolgos Michelle R MR

Scientific reports 20200228 1

Neutron total scattering measurements were conducted on MgTiO3, CaTiO3, SrTiO3, and BaTiO3 to simultaneously investigate the local and average structure of these materials. The local structures of MgTiO3, CaTiO3, and SrTiO3 were well modelled using the refined average structural models: trigonal R[Formula: see text], orthorhombic Pbnm, and cubic Pm[Formula: see text]m respectively. However the local structure for BaTiO< ...[more]

PMID: 32111857

Similar Datasets

Limits of Cation Solubility in AMg₂Sb₂ (A = Mg, Ca, Sr, Ba) Alloys.

Project description:A M 2 X 2 compounds that crystallize in the CaAl 2 Si 2 structure type have emerged as a promising class of n- and p-type thermoelectric materials. Alloying on the cation (A) site is a frequently used approach to optimize the thermoelectric transport properties of A M 2 X 2 compounds, and complete solid solubility has been reported for many combinations of cations. In the present study, we investigate the phase stability of the AMg 2 Sb 2 system with mixed occupancy of Mg, Ca, Sr, or Ba on the cation (A) site. We show that the small ionic radius of Mg 2 + leads to limited solubility when alloyed with larger cations such as Sr or Ba. Phase separation observed in such cases indicates a eutectic-like phase diagram. By combining these results with prior alloying studies, we establish an upper limit for cation radius mismatch in A M 2 X 2 alloys to provide general guidance for future alloying and doping studies.

| S-EPMC6416610 | biostudies-literature

Groundwater discharge impacts marine isotope budgets of Li, Mg, Ca, Sr, and Ba.

Project description:Groundwater-derived solute fluxes to the ocean have long been assumed static and subordinate to riverine fluxes, if not neglected entirely, in marine isotope budgets. Here we present concentration and isotope data for Li, Mg, Ca, Sr, and Ba in coastal groundwaters to constrain the importance of groundwater discharge in mediating the magnitude and isotopic composition of terrestrially derived solute fluxes to the ocean. Data were extrapolated globally using three independent volumetric estimates of groundwater discharge to coastal waters, from which we estimate that groundwater-derived solute fluxes represent, at a minimum, 5% of riverine fluxes for Li, Mg, Ca, Sr, and Ba. The isotopic compositions of the groundwater-derived Mg, Ca, and Sr fluxes are distinct from global riverine averages, while Li and Ba fluxes are isotopically indistinguishable from rivers. These differences reflect a strong dependence on coastal lithology that should be considered a priority for parameterization in Earth-system models.

| S-EPMC7794541 | biostudies-literature

Bare and ligand protected planar hexacoordinate silicon in SiSb3M3 + (M = Ca, Sr, Ba) clusters.

Project description:The occurrence of planar hexacoordination is very rare in main group elements. We report here a class of clusters containing a planar hexacoordinate silicon (phSi) atom with the formula SiSb3M3 + (M = Ca, Sr, Ba), which have D 3h (1A1') symmetry in their global minimum structure. The unique ability of heavier alkaline-earth atoms to use their vacant d atomic orbitals in bonding effectively stabilizes the peripheral ring and is responsible for covalent interaction with the Si center. Although the interaction between Si and Sb is significantly stronger than the Si-M one, sizable stabilization energies (-27.4 to -35.4 kcal mol-1) also originated from the combined electrostatic and covalent attraction between Si and M centers. The lighter homologues, SiE3M3 + (E = N, P, As; M = Ca, Sr, Ba) clusters, also possess similar D 3h symmetric structures as the global minima. However, the repulsive electrostatic interaction between Si and M dominates over covalent attraction making the Si-M contacts repulsive in nature. Most interestingly, the planarity of the phSi core and the attractive nature of all the six contacts of phSi are maintained in N-heterocyclic carbene (NHC) and benzene (Bz) bound SiSb3M3(NHC)6 + and SiSb3M3(Bz)6 + (M = Ca, Sr, Ba) complexes. Therefore, bare and ligand-protected SiSb3M3 + clusters are suitable candidates for gas-phase detection and large-scale synthesis, respectively.

| S-EPMC9278486 | biostudies-literature

Alkaline-Earth Metal Effects on Physical Properties of Ferromagnetic AVO3 (A = Ba, Sr, Ca, and Mg): Density Functional Theory Insights.

Project description:The effects of alkaline-earth metals on electronic, optical, thermodynamic, and physical properties of ferromagnetic AVO3 (A = Ba, Sr, Ca, and Mg) have been investigated by first-principles calculations within the GGA+U formalism based on density functional theory. The optimized structural parameters are in good agreement with the available experimental results that evaluate the reliability of our calculations. The cell and mechanical stability is discussed using the formation energy and Born stability criteria, respectively. The mechanical behaviors of AVO3 are discussed on the basis of the results of elastic constants, elastic moduli, Peierls stress, and Vickers hardness. The nature of the ductile-brittle transition of AVO3 compounds was confirmed by the values of Pugh's ratio, Poisson's ratio, and Cauchy pressure. The electronic band structures, as well as density of states, reveal the half-metallic behavior of BaVO3 and SrVO3. However, CaVO3 and MgVO3 exhibit spin-gapless and magnetic semiconductor characteristics, respectively. The microscopic origin of the transition from the half-metallic to semiconductor nature of AVO3 is rationalized using electronic properties. The presence of covalent, ionic, and metallic bonds in AVO3 compounds is found by the analysis of bonding properties. The single-band nature of half-metallic AVO3 is seen by observing hole-like Fermi surfaces in this study. Furthermore, the various thermodynamic and optical properties are calculated and analyzed. The refractive index suggests that AVO3 could be a potential candidate for applications to high-density optical data storage devices.

| S-EPMC9219064 | biostudies-literature

First Principles Study of the Photoelectric Properties of Alkaline Earth Metal (Be/Mg/Ca/Sr/Ba)-Doped Monolayers of MoS2.

Project description:The energy band structure, density of states, and optical properties of monolayers of MoS2 doped with alkaline earth metals (Be/Mg/Ca/Sr/Ba) are systematically studied based on first principles. The results indicate that all the doped systems have a great potential to be formed and structurally stable. In comparison to monolayer MoS2, doping alkaline earth metals results in lattice distortions in the doped system. Therefore, the recombination of photogenerated hole-electron pairs is suppressed effectively. Simultaneously, the introduction of dopants reduces the band gap of the systems while creating impurity levels. Hence, the likelihood of electron transfer from the valence to the conduction band is enhanced, which means a reduction in the energy required for such a transfer. Moreover, doping monolayer MoS2 with alkaline earth metals increases the static dielectric constant and enhances its polarizability. Notably, the Sr-MoS2 system exhibits the highest value of static permittivity, demonstrating the strongest polarization capability. The doped systems exhibit a red-shifted absorption spectrum in the low-energy region. Consequently, the Be/Mg/Ca-MoS2 systems demonstrate superior visible absorption properties and a favorable band gap, indicating their potential as photo-catalysts for water splitting.

| S-EPMC10458419 | biostudies-literature

Na6MCl8 rock-salt compounds with M = Mg, Ca, Ba, Zn, Sr as components for solid-state sodium ion batteries.

Project description:We investigate a new series of rock-salt type structures, Na6MCl8 with M = Mg, Ca, Ba, Zn and Sr using advanced atomistic simulations. Calculated results show a direct relationship between the size of the M2+ cation and lattice parameters as well as the defect formation energy variation. The NaCl Schottky defect type is highly favourable, and the Na6BaCl8 structure possesses the lowest values of defect formation energies. These structures are predicted to be mechanically stable and ductile, implying their compatibility with possible use as electrodes/electrolytes. The Na6MCl8 structures exhibit semiconductor characteristics with an energy gap ranging between 4.1-4.6 eV, which differs from the previous value of Na6MgCl8. A 3D migration pathway is identified in each rock-salt structure. Despite the small variation of the Na diffusivity and conductivity at 250 K within the structures considered, the Na6BaCl8 is characterized by the highest conductivity at 250 K, while the Na6MgCl8 structure has the highest conductivity and diffusivity values. The outstanding properties predicted for a Na ion battery suggest future development of synthetic strategies for their actual preparation.

| S-EPMC11228939 | biostudies-literature

Effects of Mg, Ca, Sr, and Ba Dopants on the Performance of La2O3 Catalysts for the Oxidative Coupling of Methane.

Project description:Oxidative coupling of methane (OCM) is a reaction to directly convert methane into high value-added hydrocarbons (C2+) such as ethylene and ethane using molecular oxygen and a catalyst. This work investigated lanthanum oxide catalysts for OCM, which were promoted with alkaline-earth metal oxides (Mg, Ca, Sr, and Ba) and prepared by the solution-mixing method. The synthesized catalysts were characterized using X-ray powder diffraction, CO2-programmed desorption, and X-ray photoelectron spectroscopy. The comparative performance of each promoter showed that promising lanthanum-loaded alkaline-earth metal oxide catalysts were La-Sr and La-Ba. In contrast, the combination of La with Ca or Mg did not lead to a clear improvement of C2+ yield. The most promising LaSr50 catalyst exhibited the highest C2+ yield of 17.2%, with a 56.0% C2+ selectivity and a 30.9% CH4 conversion. Catalyst characterization indicated that their activity was strongly associated with moderate basic sites and surface-adsorbed oxygen species of O2 -. Moreover, the catalyst was stable over 25 h at a reactor temperature of 700 °C.

| S-EPMC8771708 | biostudies-literature

Crystal Growth from Anhydrous HF Solutions of M2+ (M = Ca, Sr, Ba) and [AuF6]-, Not Only Simple M(AuF6)2 Salts.

Project description:Crystal growth from anhydrous HF solutions of M2+ (M = Ca, Sr, Ba) and [AuF6]- (molar ratio 1:2) gave [Ca(HF)2](AuF6)2, [Sr(HF)](AuF6)2, and Ba[Ba(HF)]6(AuF6)14. [Ca(HF)2](AuF6)2 exhibits a layered structure in which [Ca(HF)2]2+ cations are connected by AuF6 units, while the crystal structure of Ba[Ba(HF)]6(AuF6)14 exhibits a complex three-dimensional (3-D) network consisting of Ba2+ and [Ba(HF)2]2+ cations bridged by AuF6 groups. These results indicate that the previously reported M(AuF6)2 (M = Ca, Sr, Ba) compounds, prepared in the anhydrous HF, do not in fact correspond to this chemical formula. When the initial M2+/[AuF6]- ratio was 1:1, single crystals of [M(HF)](H3F4)(AuF6) were grown for M = Sr. The crystal structure consists of a 3-D framework formed by [Sr(HF)]2+ cations associated with [AuF6]- and [H3F4]- anions. The latter exhibits a Z-shaped conformation, which has not been observed before. Single crystals of M(BF4)(AuF6) (M = Sr, Ba) were grown when a small amount of BF3 was present during crystallization. Sr(BF4)(AuF6) crystallizes in two modifications. A high-temperature α-phase (293 K) crystallized in an orthorhombic unit cell, and a low-temperature β-phase (150 K) crystallized in a monoclinic unit cell. For Ba(BF4)(AuF6), only an orthorhombic modification was observed in the range 80-230 K. An attempt to grow crystals of Ca(BF4)(AuF6) failed. Instead, crystals of [Ca(HF)](BF4)2 were grown and the crystal structure was determined. During prolonged crystallization of [AuF]6- salts, moisture can penetrate through the walls of the crystallization vessel. This can lead to partial reduction of Au(V) to A(III) and the formation of [AuF4]- byproducts, as shown by the single-crystal growth of [Ba(HF)]4(AuF4)(AuF6)7. Its crystal structure consists of [Ba(HF)]2+ cations connected by AuF6 octahedra and square-planar AuF4 units. The crystal structure of the minor product [O2]2[Sr(HF)]5[AuF6]12·HF was also determined.

| S-EPMC9377525 | biostudies-literature

Nitridic Analogs of Micas AESi3 P4 N10 (NH)2 (AE=Mg, Mg0.94 Ca0.06 , Ca, Sr).

Project description:We present the first nitridic analogs of micas, namely AESi3 P4 N10 (NH)2 (AE=Mg, Mg0.94 Ca0.06 , Ca, Sr), which were synthesized under high-pressure high-temperature conditions at 1400 °C and 8 GPa from the refractory nitrides P3 N5 and Si3 N4 , the respective alkaline earth amides, implementing NH4 F as a mineralizer. The crystal structure was elucidated by single-crystal diffraction with microfocused synchrotron radiation, energy-dispersive X-ray spectroscopic (EDX) mapping with atomic resolution, powder X-ray diffraction, and solid-state NMR. The structures consist of typical tetrahedra-octahedra-tetrahedra (T-O-T) layers with P occupying T and Si occupying O layers, realizing the rare motif of sixfold coordinated silicon atoms in nitrides. The presence of H, as an imide group forming the SiN4 (NH)2 octahedra, is confirmed by SCXRD, MAS-NMR, and IR spectroscopy. Eu2+ -doped samples show tunable narrow-band emission from deep blue to cyan (451-492 nm).

| S-EPMC9300002 | biostudies-literature

Highly Luminous N3--Substituted Li2MSiO4-δN2/3δ:Eu2+ (M = Ca, Sr, and Ba) for White NUV Light-Emitting Diodes.

Project description:The N3--substituted Li2MSiO4:Eu2+ (M = Ca, Sr, and Ba) phosphors were systematically prepared and analyzed. Secondary-ion mass spectroscopy measurements revealed that the average N3- contents are 0.003 for Ca, 0.009 for Sr, and 0.032 for Ba. Furthermore, the N3- incorporation in the host lattices was corroborated by infrared and X-ray photoelectron spectroscopies. From the photoluminescence spectra of Li2MSiO4:Eu2+ (M = Ca, Sr, and Ba) phosphors before and after N3- doping, it was verified that the enhanced emission intensity of the phosphors is most likely due to the N3- doping. In Li2MSiO4:Eu2+ (M = Ca, Sr, and Ba) phosphors, the maximum wavelengths of the emission band were red-shifted in the order Ca < Ba < Sr, which is not consistent with the trend of crystal field splitting: Ba < Sr < Ca. This discrepancy was clearly explained by electron-electron repulsions among polyhedra, LiO4-MO n , SiO4-MO n , and MO n -M'O n associated with structural difference in the host lattices. Therefore, the energy levels associated with the 4f65d energy levels of Eu2+ are definitely established in the following order: Li2CaSiO4:Eu2+ > Li2BaSiO4:Eu2+ > Li2SrSiO4:Eu2+. Furthermore, using the Williamson-Hall (W-H) method, the determined structural strains of Li2MSiO4:Eu2+ (M = Ca, Sr, and Ba) phosphors revealed that the increased compressive strain after N3- doping induces the enhanced emission intensity of these phosphors. White light-emitting diodes made by three N3--doped phosphors and a 365 nm emitting InGaN chip showed the (0.333, 0.373) color coordinate and high color-rendering index (R a = 83). These phosphor materials may provide a platform for development of new efficient phosphors in solid-state lighting field.

| S-EPMC6648572 | biostudies-literature