ABSTRACT: In this study, the potentiometric arrayed glucose biosensors, which were based on zinc oxide (ZnO) or aluminum-doped zinc oxide (AZO) sensing membranes, were fabricated by using screen-printing technology and a sputtering system, and graphene oxide (GO) and Nafion-glucose oxidase (GOx) were used to modify sensing membranes by using the drop-coating method. Next, the material properties were characterized by using a Raman spectrometer, a field-emission scanning electron microscope (FE-SEM), and a scanning probe microscope (SPM). The sensing characteristics of the glucose biosensors were measured by using the voltage-time (V-T) measurement system. Finally, electrochemical impedance spectroscopy (EIS) was conducted to analyze their charge transfer abilities. The results indicated that the average sensitivity of the glucose biosensor based on Nafion-GOx/GO/AZO was apparently higher than that of the glucose biosensor based on Nafion-GOx/GO/ZnO. In addition, the glucose biosensor based on Nafion-GOx/GO/AZO exhibited an excellent average sensitivity of 15.44 mV/mM and linearity of 0.997 over a narrow range of glucose concentration range, a response time of 26 s, a limit of detection (LOD) of 1.89 mM, and good reproducibility. In terms of the reversibility and stability, the hysteresis voltages (VH) were 3.96 mV and 2.42 mV. Additionally, the glucose biosensor also showed good anti-inference ability and reproducibility. According to these results, it is demonstrated that AZO is a promising material, which could be used to develop a reliable, simple, and low-cost potentiometric glucose biosensor.

SUBMITTER: Chou JC

PROVIDER: S-EPMC7071120 | biostudies-literature | 2020 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

A Facile Fabrication of a Potentiometric Arrayed Glucose Biosensor Based on Nafion-GOx/GO/AZO.

Chou Jung-Chuan JC Lin Si-Hong SH Lai Tsu-Yang TY Kuo Po-Yu PY Lai Chih-Hsien CH Nien Yu-Hsun YH Su Tzu-Yu TY

Sensors (Basel, Switzerland) 20200211 4

In this study, the potentiometric arrayed glucose biosensors, which were based on zinc oxide (ZnO) or aluminum-doped zinc oxide (AZO) sensing membranes, were fabricated by using screen-printing technology and a sputtering system, and graphene oxide (GO) and Nafion-glucose oxidase (GOx) were used to modify sensing membranes by using the drop-coating method. Next, the material properties were characterized by using a Raman spectrometer, a field-emission scanning electron microscope (FE-SEM), and a ...[more]

PMID: 32054014

Similar Datasets

Project description:In recent years, LC resonant sensors have gained widespread attention for their extensive applications in industries such as pharmaceutical storage and food transportation. A wireless passive sensor with a good sensing performance is proposed based on a GO/CNT-OH/Nafion nanocomposite. The sensor was fabricated via inkjet printing technology, and the surface morphology of the GO/CNT-OH/Nafion nanocomposite was characterized by SEM measurement. It is found that the MWCNTs support the GO layer and the hydrophobic chains of Nafion interact with the hydrophobic layer of GO, resulting in a larger cavity and hydrophilic surface of the entire material. This structure well reflects the fact that the mixing of MWCNTs and Nafion provides the entire material with a stronger water absorption. The experimental study shows that the proposed humidity sensor has a frequency variation of 103 kHz/%RH at low humidity (30-60% RH) and a sensitivity of 931 kHz/%RH at high humidity (60-95% RH), while the sensitivity value from 30-95% RH is 547 kHz/% RH. The response time and recovery time are 110 s and 115 s, respectively. In addition, the tests showed that the GO/CNT-OH/Nafion nanocomposite applied to the humidity sensor had a maximum humidity hysteresis of about 3% RH at 30-95% RH, the resonant frequency remained basically unchanged after 50 h of testing, and the whole sensor possessed a good stability. After conducting several repeated experiments, it was found that the resonant frequency error of the whole sensor was low and did not affect the overall sensing test, which proved the reproducible preparation of the sensor. Finally, the humidity-sensing mechanism of the proposed sensor was analyzed in this paper, and it was found that GO enhanced the hygroscopic properties of GO/CNT-OH/Nafion nanocomposite when it was supported by MWCNT-OH and included uniformly dispersed Nafion. Therefore, our proposed humidity sensor is suitable for humidity detection above 30% RH in both sealed and open environments.

Dataset Information

A Facile Fabrication of a Potentiometric Arrayed Glucose Biosensor Based on Nafion-GOx/GO/AZO.

Publications

A Facile Fabrication of a Potentiometric Arrayed Glucose Biosensor Based on Nafion-GOx/GO/AZO.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets