Melt-Electrospun Polyethylene Nanofiber Obtained from Polyethylene/Polyvinyl Butyral Blend Film.

ABSTRACT: We prepared low-density polyethylene (LDPE) nanofiber, a few hundred nanometers in diameter, using polyvinyl butyral (PVB) and a laser melt-electrospinning (M-ESP) device. We blended PVB with LDPE via an internal melt mixer, removed the PVB after M-ESP by ethanol treatment, and studied the influence of PVB on fiber diameter. A substantial diameter reduction with improved crystallinity of LDPE fiber was observed with increased PVB content in the blend. PVB inclusion also increased the polarity of the LDPE/PVB blend, resulting in better spinnability. The removal of PVB from LDPE/PVB blend fiber caused a massive drop in the LDPE fiber diameter, due to fiber splitting, particularly in PVB-rich samples. Fourier transform infrared (FTIR) spectroscopy of fibers confirmed that the prepared nanofiber was the same as pure LDPE fiber.

SUBMITTER: Zakaria M

PROVIDER: S-EPMC7077628 | biostudies-literature | 2020 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Melt-Electrospun Polyethylene Nanofiber Obtained from Polyethylene/Polyvinyl Butyral Blend Film.

Zakaria Mohammad M Shibahara Kanta K Nakane Koji K

Polymers 20200216 2

We prepared low-density polyethylene (LDPE) nanofiber, a few hundred nanometers in diameter, using polyvinyl butyral (PVB) and a laser melt-electrospinning (M-ESP) device. We blended PVB with LDPE via an internal melt mixer, removed the PVB after M-ESP by ethanol treatment, and studied the influence of PVB on fiber diameter. A substantial diameter reduction with improved crystallinity of LDPE fiber was observed with increased PVB content in the blend. PVB inclusion also increased the polarity of ...[more]

PMID: 32079096

Similar Datasets

Project description:BackgroundHere, electrospun fibers based on a blend of polycaprolactone (PCL), poly(ethylene glycol) (PEG), and gelatin methacryloyl (GelMA) were developed. The careful choice of this polymer combination allowed for the preparation of a biomaterial that preserved the mechanical strength of PCL, while at the same time improving the hydrophilicity of the blended material and human osteoblast maturation.MethodsThe morphology, chemical structure, wettability, and mechanical properties before and after UV photocrosslinking were evaluated. Furthermore, human osteoblasts (hFOB) were cultivated for up to 21 days on the scaffolds, and their potential to upregulate cell proliferation, alkaline phosphatase (ALP) activity, and calcium deposition were investigated.ResultsContact angle measurement results showed that the developed scaffolds presented hydrophilic properties after PEG and GelMA incorporation before (25°) and after UV photocross-linking (69°) compared to pure PCL (149°). PCL:PEG:GelMA-UV displayed a slight increase in mechanical strength (elastic modulus ~37 MPa) over PCL alone (~33 MPa). Normally, an increase in strength of fibers leads to a decrease in elongation at break, due to the material becoming less deformable and stiffer, thus leading to breaks at low strain. This behavior was observed by comparing PCL (elongation at break ~106%) and PCL:PEG:GelMA-UV (~50%). Moreover, increases in ALP activity (10-fold at day 14) and calcium deposition (1.3-fold at day 21) by hFOBs were detected after PEG and GelMA incorporation after UV photocross-linking compared to pure PCL. Ultrathin and hydrophilic fibers were obtained after PEG and GelMA incorporation after UV photocrosslinking, but the strength of PCL was maintained. Interestingly, those ultrathin fiber characteristics improved hFOB functions.ConclusionThese findings appear promising for the use of these electrospun scaffolds, based on the combination of polymers used here for numerous orthopedic applications.

Dataset Information

Melt-Electrospun Polyethylene Nanofiber Obtained from Polyethylene/Polyvinyl Butyral Blend Film.

Publications

Melt-Electrospun Polyethylene Nanofiber Obtained from Polyethylene/Polyvinyl Butyral Blend Film.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets