Hydrophobically Coated Superparamagnetic Iron Oxides Nanoparticles Incorporated into Polymer-Based Nanocapsules Dispersed in Water.

ABSTRACT: This paper reports the characterization of iron oxide magnetic nanoparticles obtained via the thermal decomposition of an organometallic precursor, which were then loaded into nanocapsules prepared via the emulsification process in the presence of an amphiphilic derivative of chitosan. The applied synthetic method led to the formation of a hydrophobic layer on the surface of nanoparticles that enabled their loading in the hydrophobic liquid inside of the polymer-based capsules. The average diameter of nanoparticles was determined to be equal to 15 nm, and they were thoroughly characterized using X-ray diffraction (XRD), magnetometry, and Mössbauer spectroscopy. A core-shell structure consisting of a wüstite core and maghemite-like shell was revealed, resulting in an exchange bias effect and a considerable magnetocrystalline anisotropy at low temperatures and a superparamagnetic behavior at room temperature. Importantly, superparamagnetic behavior was observed for the aqueous dispersion of the nanocapsules loaded with the superparamagnetic nanoparticles, and the dispersion was shown to be very stable (at least 48 weeks). The results were analyzed and discussed with respect to the potential future applications of these nanoparticles and nanocapsules based on biopolymers as platforms designed for the magnetically navigated transport of encapsulated hydrophobic substances.

SUBMITTER: Gumieniczek-Chlopek E

PROVIDER: S-EPMC7085046 | biostudies-literature | 2020 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Hydrophobically Coated Superparamagnetic Iron Oxides Nanoparticles Incorporated into Polymer-Based Nanocapsules Dispersed in Water.

Gumieniczek-Chłopek Elżbieta E Odrobińska Joanna J Strączek Tomasz T Radziszewska Agnieszka A Zapotoczny Szczepan S Kapusta Czesław C

Materials (Basel, Switzerland) 20200309 5

This paper reports the characterization of iron oxide magnetic nanoparticles obtained via the thermal decomposition of an organometallic precursor, which were then loaded into nanocapsules prepared via the emulsification process in the presence of an amphiphilic derivative of chitosan. The applied synthetic method led to the formation of a hydrophobic layer on the surface of nanoparticles that enabled their loading in the hydrophobic liquid inside of the polymer-based capsules. The average diame ...[more]

PMID: 32182749

Similar Datasets

Project description:BackgroundEngineered inorganic nanoparticles (NPs) are essential components in the development of nanotechnologies. For applications in nanomedicine, particles need to be functionalized to ensure a good dispersibility in biological fluids. In many cases however, functionalization is not sufficient: the particles become either coated by a corona of serum proteins or precipitate out of the solvent. We show that by changing the coating of magnetic iron oxide NPs using poly-L-lysine (PLL) polymer the colloidal stability of the dispersion is improved in aqueous solutions including water, phosphate buffered saline (PBS), PBS with 10% fetal bovine serum (FBS) and cell culture medium, and the internalization of the NPs toward living mammalian cells is profoundly affected.MethodsA multifunctional magnetic NP is designed to perform a near-infrared (NIR)-responsive remote control photothermal ablation for the treatment of breast cancer. In contrast to the previously reported studies of gold (Au) magnetic (Fe3O4) core-shell NPs, a Janus-like nanostructure is synthesized with Fe3O4 NPs decorated with Au resulting in an approximate size of 60 nm mean diameter. The surface of trisoctahedral Au-Fe3O4 NPs was coated with a positively charged polymer, PLL to deliver the NPs inside cells. The PLL-Au-Fe3O4 NPs were characterized by transmission electron microscopy (TEM), XRD, FT-IR and dynamic light scattering (DLS). The unique properties of both Au surface plasmon resonance and superparamagnetic moment result in a multimodal platform for use as a nanothermal ablator and also as a magnetic resonance imaging (MRI) contrast agent, respectively. Taking advantage of the photothermal therapy, PLL-Au-Fe3O4 NPs were incubated with BT-474 and MDA-MB-231 breast cancer cells, investigated for the cytotoxicity and intracellular uptake, and remotely triggered by a NIR laser of ~ 808 nm (1 W/cm2 for 10 min).ResultsThe PLL coating increased the colloidal stability and robustness of Au-Fe3O4 NPs (PLL-Au-Fe3O4) in biological media including cell culture medium, PBS and PBS with 10% fetal bovine serum. It is revealed that no significant (< 10%) cytotoxicity was induced by PLL-Au-Fe3O4 NPs itself in BT-474 and MDA-MB-231 cells at concentrations up to 100 μg/ml. Brightfield microscopy, fluorescence microscopy and TEM showed significant uptake of PLL-Au-Fe3O4 NPs by BT-474 and MDA-MB-231 cells. The cells exhibited 40 and 60% inhibition in BT-474 and MDA-MB-231 cell growth, respectively following the internalized NPs were triggered by a photothermal laser using 100 μg/ml PLL-Au-Fe3O4 NPs. The control cells treated with NPs but without laser showed < 10% cell death compared to no laser treatment control CONCLUSION: Combined together, the results demonstrate a new polymer gold superparamagnetic nanostructure that integrates both diagnostics function and photothermal ablation of tumors into a single multimodal nanoplatform exhibiting a significant cancer cell death.

Project description:Superparamagnetic iron oxide nanoparticles (SPIONs) have been widely utilized for the diagnosis and therapy of specific diseases, as magnetic resonance imaging (MRI) contrast agents and drug-delivery carriers, due to their easy transportation to targeted areas by an external magnetic field. For such biomedical applications, SPIONs must have multifunctional characteristics, including optimized size and modified surface. However, the biofunctionality and biocompatibility of SPIONs with various surface functional groups of different sizes have yet to be elucidated clearly. Therefore, it is important to carefully monitor the cytotoxicity and genotoxicity of SPIONs that are surfaced-modified with various functional groups of different sizes. In this study, we evaluated SPIONs with diameters of approximately 10 nm and 100~150 nm, containing different surface functional groups. SPIONs were covered with -O? groups, so-called bare SPIONs. Following this, they were modified with three different functional groups--hydroxyl (-OH), carboxylic (-COOH), and amine (-NH?) groups--by coating their surfaces with tetraethyl orthosilicate (TEOS), (3-aminopropyl)trimethoxysilane (APTMS), TEOS-APTMS, or citrate, which imparted different surface charges and sizes to the particles. The effects of SPIONs coated with these functional groups on mitochondrial activity, intracellular accumulation of reactive oxygen species, membrane integrity, and DNA stability in L-929 fibroblasts were determined by water-soluble tetrazolium, 2',7'-dichlorodihydrofluorescein, lactate dehydrogenase, and comet assays, respectively. Our toxicological observations suggest that the functional groups and sizes of SPIONs are critical determinants of cellular responses, degrees of cytotoxicity and genotoxicity, and potential mechanisms of toxicity. Nanoparticles with various surface modifications and of different sizes induced slight, but possibly meaningful, changes in cell cytotoxicity and genotoxicity, which would be significantly valuable in further studies of bioconjugation and cell interaction for drug delivery, cell culture, and cancer-targeting applications.

Dataset Information

Hydrophobically Coated Superparamagnetic Iron Oxides Nanoparticles Incorporated into Polymer-Based Nanocapsules Dispersed in Water.

Publications

Hydrophobically Coated Superparamagnetic Iron Oxides Nanoparticles Incorporated into Polymer-Based Nanocapsules Dispersed in Water.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets