Size Effect in Compressive Strength Tests of Cored Specimens of Lightweight Aggregate Concrete.

ABSTRACT: The aim of this paper is to discuss the unrecognized problem of the scale effect in compressive strength tests determined for cored specimens of lightweight aggregate concrete (LWAC) against the background of available data on the effect for normal-weight concrete (NWAC). The scale effect was analyzed taking into consideration the influence of slenderness (? = 1.0, 1.5, 2.0) and diameter (d = 80, 100, 125, and 150 mm) of cored specimens, as well as the type of lightweight aggregate (expanded clay and sintered fly ash) and the type of cement matrix (w/c = 0.55 and 0.37). The analysis of the results for four lightweight aggregate concretes revealed no scale effect in compressive strength tests determined on cored specimens. Neither the slenderness, nor the core diameter seemed to affect the strength results. This fact should be explained by the considerably better structural homogeneity of the tested lightweight concretes in comparison to normal-weight ones. Nevertheless, there were clear differences between the results obtained on molded and cored specimens of the same shape and size.

SUBMITTER: Domagala L

PROVIDER: S-EPMC7085069 | biostudies-literature | 2020 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Size Effect in Compressive Strength Tests of Cored Specimens of Lightweight Aggregate Concrete.

Domagała Lucyna L

Materials (Basel, Switzerland) 20200306 5

The aim of this paper is to discuss the unrecognized problem of the scale effect in compressive strength tests determined for cored specimens of lightweight aggregate concrete (LWAC) against the background of available data on the effect for normal-weight concrete (NWAC). The scale effect was analyzed taking into consideration the influence of slenderness (<i>λ</i> = 1.0, 1.5, 2.0) and diameter (d = 80, 100, 125, and 150 mm) of cored specimens, as well as the type of lightweight aggregate (expan ...[more]

PMID: 32155815

Similar Datasets

Project description:At present, many modification methods have been proposed to improve the performance of recycled aggregate concrete (RAC). In this study, tests on the compressive strength and damping properties of modified RAC with the addition of different proportions of recycled coarse aggregate (RCA) (0, 50, 100%), rubber powder (10, 15, 20%), steel fibre (5, 7.5, 10%) and fly ash (15, 20, 5%) are carried out. To elucidate the effect of the modification method on the interfacial transition zone (ITZ) performance of RAC, model ITZ specimens are used for push-out tests. The results show that when the replacement rate of RCA reaches 100%, the loss factor of the RAC is 6.0% higher than that of natural aggregate concrete; however, the compressive strength of the RAC decreases by 22.6%. With the addition of 20% rubber powder, the damping capacity of the modified RAC increases by 213.7%, while the compressive strength of the modified RAC decreases by 47.5%. However, with the addition of steel fibre and fly ash, both the compressive strength and loss factor of the RAC specimens increase. With a steel fibre content of 10 wt%, the compressive strength and loss factor of the RAC increase by 21.9% and 15.2%, respectively. With a fly ash content of 25 wt%, the compressive strength and loss factor of the RAC increase by 8.6% and 6.9%, respectively. This demonstrates that steel fibre and fly ash are effective in improving both the damping properties and compressive strength of RAC, and steel fibre is more effective than fly ash. Two methods were used for modification of the RAC: reinforcing the RCA through impregnation with a 0.5% polyvinyl alcohol (PVA) emulsion and nano-SiO2 solution, and strengthening the RAC integrally through the addition of fly ash as an admixture. Both of these techniques can improve the ITZ bond strength between the RAC and new mortar. Replacing 10% of the cement with fly ash in the new mortar is shown to be the best method to improve the ITZ strength.

Dataset Information

Size Effect in Compressive Strength Tests of Cored Specimens of Lightweight Aggregate Concrete.

Publications

Size Effect in Compressive Strength Tests of Cored Specimens of Lightweight Aggregate Concrete.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets