The Effect of the Bioactive Glass and the Er:YAG Laser on the Remineralization of the Affected Dentin: A Comparative In Vitro Study.

ABSTRACT: Introduction: The purpose of this study was to compare the effect of the bioactive glass, the glass ionomer, and the Erbium YAG laser as liners on the remineralization of the affected dentin. Methods: The present study was conducted on 64 healthy extracted human molars divided into 4 groups, 1 control group and 3 experimental groups. After artificially inducing dentinal caries lesions, each of the experimental groups was applied to the cavity floor and then restored with a composite. The samples were stored after thermocycling in an incubator for two months. Finally, the hardness of the cavity floor was measured at 3 depths of 20, 50 and 100 ?m by the Vickers microhardness tester. The dentin conditions underneath the liners were also evaluated with FESEM. Statistical analysis was performed by two-way ANOVA and the post-hoc Games-Howell test (P<0.05). Results: Among the groups, the lowest microhardness value was in the control group (P<0.05) except at a depth of 100 ?m; therefore, there was no significant difference between the control group and the bioactive glass (P>0.05). The laser group had the highest microhardness value, which was significantly different from the control group (P<0.05). There was a significant difference between the laser and bioactive glass (P<0.05), except at a depth of 20 ?m. The laser and glass ionomer had only a significant difference at a depth of 100 ?m (P<0.05). The microhardness value induced by glass ionomer was higher than bioactive glass, which in no depth was significant (P>0.05). Partial dentinal tubule occlusion was observed with FESEM in each of the experimental groups as compared to the control group. Conclusion: The microhardness values were higher in all groups than in the control group. The laser might be more successful in remineralization than the other ones.

SUBMITTER: Moghaddas MJ

PROVIDER: S-EPMC7118508 | biostudies-literature | 2020

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

The Effect of the Bioactive Glass and the Er:YAG Laser on the Remineralization of the Affected Dentin: A Comparative In Vitro Study.

Moghaddas Mohammad Javad MJ Moosavi Horieh H Yaghoubirad Sara S Chiniforush Nasim N

Journal of lasers in medical sciences 20200315 2

<b>Introduction:</b> The purpose of this study was to compare the effect of the bioactive glass, the glass ionomer, and the Erbium YAG laser as liners on the remineralization of the affected dentin. <b>Methods:</b> The present study was conducted on 64 healthy extracted human molars divided into 4 groups, 1 control group and 3 experimental groups. After artificially inducing dentinal caries lesions, each of the experimental groups was applied to the cavity floor and then restored with a composit ...[more]

PMID: 32273957

Similar Datasets

Project description:BackgroundGlaucoma is a leading cause of global blindness, especially preventable blindness. The increased prevalence of glaucoma has led to a growing demand for newer, safer, more rapid, and simpler treatments for the reduction of intraocular pressure (IOP). In this study, we evaluated the safety and feasibility of performing filtration glaucoma surgery with an Ab-Interno Er:YAG laser in rabbits.MethodsNine New Zealand White rabbits age 16 weeks were studied. After subconjunctival injection of mitomycin C (MMC), a novel Ab-Interno Er:YAG laser probe was inserted into the anterior chamber (AC) through a clear corneal 1 mm paracentesis and directed at the trabecular meshwork adjacent to the MMC injection area. A pulsed laser beam was applied to create a patent sclerostomy connecting the AC to the subconjuctival space, resulting in a filtering bleb. The laser system used was the Er:YAG laser system - LAS25-FCU, (Pantec Biosolutions AG, Liechtenstein). Parameters used: Wave lengh: 2940 nm, Pulse length: 100-400 μsec,frequency: 250 Hz. Average laser power in accordance to the fiber tip diameter: 0.85 W(range 0.8-0.92 W). Complete ocular exams, including IOP measurements, were performed on 1, 7, 14, and 23 days postoperatively. Three rabbits were sacrificed on days 1, 14, and 23, and histological examinations were performed on all nine eyes.ResultsAll procedures resulted in a functional medium-large superior bleb without significant complications. The bleb was sustained in all rabbits by day 14 and in one of the three rabbits that reached the last follow-up at 23 days. No cases of postoperative hypotony were observed. There was a transient significant reduction in mean IOP on postoperative days 5 and 7 (P = 0.028). Histopathological analysis revealed a patent full-thickness scleral tunnel with only a minor degree of surrounding coagulation necrosis.ConclusionsThe Ab-Interno laser sclerostomy procedure is potentially safe and effective based on initial experience in an in-vivo rabbit animal model.

Project description:BACKGROUND:When implants are restored with cement-retained restorations, prosthetic retrievability can be difficult and often requires sectioning using rotary instruments. Sometimes repeated removals of a cement-retained implant crown are needed such as for treatment of peri-implantitis or immediate implant provisionalization. The purpose of this study was to evaluate the effect of erbium-doped yttrium aluminum garnet (Er:YAG) laser as a non-invasive treatment modality to remove lithium disilicate crowns from zirconia implant abutments following long-term cementation, repetitive debonding and re-cementation, and short-term retrieval. MATERIAL AND METHODS:Twenty identical lithium disilicate crowns were cemented onto zirconia prefabricated abutments using composite resin cement. Ten cemented crowns were removed at 48 hours after cementation as a short-term group (ST), while another 10 were removed 6 months after cementation as a long-term group (LT). To mimicking repetitive recementation and retrieval, the LT crowns were then recemented and removed after 48 hours as a long-term recemention (LTR) group. The LTR crowns were then again recemented and removed after 48 hours as a long-term repeated recemention (LTRR) group. Er:YAG laser was used to facilitate the retrieval of these crowns. recorded and analyzed using ANOVA and t-test. The surfaces of the crown and the abutment were further examined using light microscopy and scanning electron microscopy (SEM). Temperature changes of the abutment and crown upto 10 minutes were also measured and statistically analyzed (paired t-test). RESULTS:The average times of crown removal from zirconia abutments were 4 minutes (min) and 42 second (sec) in LT to 3 min 24 sec in LTR, and 3 min 12 sec in LTRR and ST groups. LTR took the longest time to remove, statistically (ANOVA and t-test, p < .001). No statistical differences were observed among the removal times of LTR, LTRR, and ST groups (t-test, p = .246, .246 and 1). SEM examination of the material surface showed no visual surface damaging from treatment with Er:YAG laser. The temperatures during irradiation ranged from 18.4°C to 20°C and 22.2°C to 24.5°C (Paired t-test, p < .0001) for the abutment and the crown during irradiation from 1 min to 10 mins. CONCLUSIONS:Long-term cementation can increase time in lithium disilicate crown removal from zirconia abutment using Er:YAG. Er:YAG laser is a non-invasive tool to remove cement-retained implant prostheses and should be considered as a viable alternative to rotary instruments.

Dataset Information

The Effect of the Bioactive Glass and the Er:YAG Laser on the Remineralization of the Affected Dentin: A Comparative In Vitro Study.

Publications

The Effect of the Bioactive Glass and the Er:YAG Laser on the Remineralization of the Affected Dentin: A Comparative In Vitro Study.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets