Color Shift, Color Stability, and Post-Polishing Surface Roughness of Esthetic Resin Composites.

ABSTRACT: The aim of this study was to compare color shift, color stability, and post-polishing surface roughness of esthetic restorative materials. Twenty-five disc-shaped specimens (10 mm in diameter and 2 mm in thickness) from five esthetic resin materials (Z250XT, IPS Empress-Direct, G-ænial, Vit-l-escence, and Ceram.X) were fabricated. Color shift before and immediately after light-curing (?E0) then color stability after immersion in tea, coffee, berry juice, and distilled water were measured using a spectrophotometer. Color changes were measured after 2 (?E2), 4 (?E4), 6 (?E6), and 8 weeks (?E8). Surface roughness values (Rq) were determined using an optical profilometer after polishing using a rotary polishing system. Data were analyzed using ANOVA and multiple comparison methods at 0.05 significance level. There were no significant differences between the tested materials regarding color shift except between Vit-l-escence and Ceram.X (p = 0.033). There was no significant difference between coffee and tea solutions (p = 1.0) and between berry juice and distilled water (p = 0.15). There was no difference between the tested materials regarding Rq (p = 0.057). Ceram.X was associated with the lowest ?E8 values overall. Tested materials were comparable regarding color shift and post-polishing surface roughness. Susceptibility to staining was dependent on the material.

SUBMITTER: Alkhadim YK

PROVIDER: S-EPMC7143460 | biostudies-literature | 2020 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Color Shift, Color Stability, and Post-Polishing Surface Roughness of Esthetic Resin Composites.

Alkhadim Yara Khalid YK Hulbah Malak Jameel MJ Nassar Hani Mohammad HM

Materials (Basel, Switzerland) 20200318 6

The aim of this study was to compare color shift, color stability, and post-polishing surface roughness of esthetic restorative materials. Twenty-five disc-shaped specimens (10 mm in diameter and 2 mm in thickness) from five esthetic resin materials (Z250XT, IPS Empress-Direct, G-ænial, Vit-l-escence, and Ceram.X) were fabricated. Color shift before and immediately after light-curing (∆E<sub>0</sub>) then color stability after immersion in tea, coffee, berry juice, and distilled water were measu ...[more]

PMID: 32197532

Similar Datasets

Project description:Background It has been demonstrated that dental restorations with rough surfaces can have several disadvantages such as pigment retention or plaque accumulation, which can facilitate caries formation, color variation, loss of brightness, degradation of restoration, among others. The present study aimed to assess surface roughness in bulk fill and conventional nanohybrid resins with and without polishing, controlling the oxygen inhibited layer. Methods This in vitro and longitudinal experimental study consisted of 120 resin blocks of 6 mm diameter and 4 mm depth, divided into two groups: Bulk Fill (Tetric® N-Ceram Bulk-fill, Opus Bulk Fill APS, Filtek™ Bulk Fill) and conventional nanohybrid (Tetric® N-Ceram, Opallis EA2, Filtek™ Z250 XT). Each resin group was divided into two equal parts, placing glycerin only on one of them, in order to control the oxygen inhibited layer. Subsequently, the surface roughness was measured before and after the polishing procedure with Sof-Lex discs. The data were analyzed with the T-test for related measures, and for comparison between groups before and after polishing, the non-parametric Kruskal Wallis test with the Bonferroni post hoc was used, considering a significance level of p < 0.05. Results Before polishing, the resin composites with the lowest surface roughness were Opus Bulk Fill APS (0.383 ± 0.186 µm) and Opallis EA2 (0.430 ± 0. 177 µm) with and without oxygen inhibited layer control, respectively; while after polishing, those with the lowest surface roughness were Opus Bulk Fill APS (0.213 ± 0.214 µm) and Tetric N-Ceram (0.097 ± 0.099 µm), with and without oxygen inhibited layer control, respectively. Furthermore, before and after polishing, all resins significantly decreased their surface roughness (p < 0.05) except Opus Bulk Fill APS resin with oxygen inhibited layer control (p = 0.125). However, when comparing this decrease among all groups, no significant differences were observed (p < 0.05). Conclusion The Opus Bulk Fill APS resin with oxygen inhibited layer control presented lower surface roughness both before and after polishing, being these values similar at both times. However, after polishing the other bulk fill and conventional nanohybrid resins with and without oxygen inhibited layer control, the surface roughness decreased significantly in all groups, being this decrease similar in all of them. Supplementary Information The online version contains supplementary material available at 10.1186/s12903-022-02297-w.

Project description:BACKGROUND:Increased composite roughness enhances bacterial adhesion and discoloration, thus increasing the risk of gingival inflammation and secondary caries. Concerns about detrimental effects of sodium bicarbonate on surface roughness influenced the development of less abrasive powders: a glycine-based powder and an erythritol-based powder, additionally - sodium bicarbonate-based powder of reduced grain size. However, there is limited evidence on effects of these materials on the surface of dental fillings. The aim of the present study was to compare the effects of three air-polishing powders (of a reduced abrasiveness) on surface roughness of microhybrid restorative composite material. MATERIAL AND METHODS:Microhybrid light-cure resin composite samples were placed on 64 plaster cubes and light-cured through polyester strips. Surface roughness was measured using laser confocal microscope (magnification 2160x). The specimens were randomly divided into three groups (n = 20, 20 and 24) and air-polished with: sodium bicarbonate (40 μm), glycine (25 μm) and erythritol (14 μm), respectively. Then surface roughness was remeasured, keeping the same field of observation. Specialized 3D analysis software was used for data processing. Parameters according to ISO 25178: Sa, Sq, Sku, Sp, Sv, Sz, Ssk were used to describe surface roughness. RESULTS:Sa, Sq, Sp, Sv, Sz increased significantly following air polishing. Ssk was significantly higher, whereas Sku was significantly lower in sodium bicarbonate and erythritol groups than before air polishing. Comparison between the three powders revealed that Sa was significantly higher in sodium bicarbonate group than in glycine group. Sku was significantly higher in glycine and erythritol groups than in sodium bicarbonate group. CONCLUSIONS:Sodium bicarbonate has a stronger detrimental effect on composite surface than glycine or erythritol. No advantage of erythritol comparing to glycine could be found.

Project description:This ex vivo study aimed to investigate surface roughness and substance loss after treatment with different professional cleaning methods and to determine whether subsequent polishing with a rubber cup and polishing paste is necessary. Samples (flat and natural surfaces) of human enamel and dentin were prepared (baseline) and treated with either a curette, air-polishing with erythritol, a rubber cup and polishing paste, or a combination thereof (treatment). Subsequently, all samples were immersed in an ultrasonic bath (ultrasonic) to remove residues from the treatment procedures. The surface roughness values sRa and sRz as well as tissue loss were measured profilometrically. Linear regression models were used to compare group differences (roughness and loss) considering the corresponding baseline value. The significance level was set at p<0.05. sRa increased significantly after treatment with curettes or air-polishing with erythritol in both enamel (p<0.001) and dentin (p<0.001) of flat samples. The same effect was observed for sRz in dentin (p<0.001) but not for enamel compared to negative control. Polishing with a rubber cup and paste alone had no significant effect on roughness values. When combined with other treatments, the effect of curette or air-polishing with erythritol dominated the effect. In enamel, none of the tested methods led to measurable tissue loss. In dentin, air-polishing with erythritol caused ≤50% tissue loss compared to the curette. Conclusively, for enamel, treatment effects on roughness were measurable but of limited clinical relevance. For dentin, air-polishing resulted in a smaller but insignificant roughness increase and less tissue loss compared to the curette. Polishing with a rubber cup and paste did not affect surface roughness. Regarding the clinical application, the use of air-polishing seems to be a less invasive procedure than using a curette; polishing with rubber cup and paste offers no advantage in terms of reducing roughness as a final procedure.

Dataset Information

Color Shift, Color Stability, and Post-Polishing Surface Roughness of Esthetic Resin Composites.

Publications

Color Shift, Color Stability, and Post-Polishing Surface Roughness of Esthetic Resin Composites.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets