New Resin-Based Bulk-Fill Composites: in vitro Evaluation of Micro-Hardness and Depth of Cure as Infection Risk Indexes.

ABSTRACT: The current in vitro study evaluated the Vickers hardness number (VHN) and hardness ratio of four bulk-fill composites (VisCalor bulk; Admira Fusion x-tra; x-tra fil; and GrandioSO x-tra-Voco, Cuxhaven, Germany) to assess the risk of bacterial colonization in comparison with standard composite materials. Thirty samples were prepared for each group. The VHN of both the external (top) and internal surface (bottom) was determined with a micro-hardness tester (200 g load for 15 s), and the hardness ratio was also calculated for each sample. Subsequently, storage in an acidic soft drink (Coca-Cola, Coca-Cola Company, Milano, Italy) was performed; for each group, 10 samples were stored for 1 day, while another 10 were stored for 7 days and the remaining 10 were kept in water as controls. A significant reduction in VHN was shown for all the groups when comparing the external versus internal side (P < 0.05), although the hardness ratio was greater than 0.80, resulting in an adequate polymerization. Regarding the acid storage, all the groups showed a significant decrease of VHN when compared with the controls, both after 1 day (P < 0.05) and after 7 days (P < 0.001). All the products showed adequate depth of cure without further risk of bacterial colonization. However, acid exposure negatively affected micro-hardness values, which might promote subsequent colonization.

SUBMITTER: Colombo M

PROVIDER: S-EPMC7143874 | biostudies-literature | 2020 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

New Resin-Based Bulk-Fill Composites: <i>in vitro</i> Evaluation of Micro-Hardness and Depth of Cure as Infection Risk Indexes.

Colombo Marco M Gallo Simone S Poggio Claudio C Ricaldone Vittorio V Arciola Carla Renata CR Scribante Andrea A

Materials (Basel, Switzerland) 20200313 6

The current <i>in vitro</i> study evaluated the Vickers hardness number (VHN) and hardness ratio of four bulk-fill composites (VisCalor bulk; Admira Fusion x-tra; x-tra fil; and GrandioSO x-tra-Voco, Cuxhaven, Germany) to assess the risk of bacterial colonization in comparison with standard composite materials. Thirty samples were prepared for each group. The VHN of both the external (top) and internal surface (bottom) was determined with a micro-hardness tester (200 g load for 15 s), and the ha ...[more]

PMID: 32183115

Similar Datasets

Project description:Background It has been demonstrated that dental restorations with rough surfaces can have several disadvantages such as pigment retention or plaque accumulation, which can facilitate caries formation, color variation, loss of brightness, degradation of restoration, among others. The present study aimed to assess surface roughness in bulk fill and conventional nanohybrid resins with and without polishing, controlling the oxygen inhibited layer. Methods This in vitro and longitudinal experimental study consisted of 120 resin blocks of 6 mm diameter and 4 mm depth, divided into two groups: Bulk Fill (Tetric® N-Ceram Bulk-fill, Opus Bulk Fill APS, Filtek™ Bulk Fill) and conventional nanohybrid (Tetric® N-Ceram, Opallis EA2, Filtek™ Z250 XT). Each resin group was divided into two equal parts, placing glycerin only on one of them, in order to control the oxygen inhibited layer. Subsequently, the surface roughness was measured before and after the polishing procedure with Sof-Lex discs. The data were analyzed with the T-test for related measures, and for comparison between groups before and after polishing, the non-parametric Kruskal Wallis test with the Bonferroni post hoc was used, considering a significance level of p < 0.05. Results Before polishing, the resin composites with the lowest surface roughness were Opus Bulk Fill APS (0.383 ± 0.186 µm) and Opallis EA2 (0.430 ± 0. 177 µm) with and without oxygen inhibited layer control, respectively; while after polishing, those with the lowest surface roughness were Opus Bulk Fill APS (0.213 ± 0.214 µm) and Tetric N-Ceram (0.097 ± 0.099 µm), with and without oxygen inhibited layer control, respectively. Furthermore, before and after polishing, all resins significantly decreased their surface roughness (p < 0.05) except Opus Bulk Fill APS resin with oxygen inhibited layer control (p = 0.125). However, when comparing this decrease among all groups, no significant differences were observed (p < 0.05). Conclusion The Opus Bulk Fill APS resin with oxygen inhibited layer control presented lower surface roughness both before and after polishing, being these values similar at both times. However, after polishing the other bulk fill and conventional nanohybrid resins with and without oxygen inhibited layer control, the surface roughness decreased significantly in all groups, being this decrease similar in all of them. Supplementary Information The online version contains supplementary material available at 10.1186/s12903-022-02297-w.

Project description:BackgroundDespite recent advances in restorative dentistry adhesive restorations may cause postoperative sensitivity which leads to restoration failure.AimThis study aimed to compare and evaluate the incremental and bulk fill resin Composite postoperative sensitivity in class II posterior restorations bonded with two adhesive systems (self-etch and etch-and-rinse).MethodsSixty patients were randomly selected, their age range from twenty-five to forty years old, divided into two groups according to the packing technique of resin composite material; incremental Tetric Evoceram and Tetric Evoceram bulk-fill resin composite. Thirty patients (n = 30) for incremental Tetric Evoceram resin composite restorations and according to the adhesive systems used they were equally divided (n = 15 teeth).Thirty patients (n = 30) for Tetric Evoceram bulk-fill resin composite restorations and according to the adhesive systems used (etch and rinse or self-etch), they were equally divided (n = 15 teeth). Post-operative pain assessed at 24 hours, 1 week and 1 month using the Visual Analog Scale Score (VAS). Each patient was instructed to put a mark on the VAS line at home to point out the intensity of pain at each assessment period. The problem of measuring the pain that pain tolerance of individuals may be different from the others. This may be due to different reasons, and it is not always because of a problem in the restoration.ResultsAfter 1 day, 1 week as well as 1 month, no statistically significant disagreement between the two resin composite types using self-etch adhesive strategy and total-etch adhesive strategy. Also, when the two adhesive systems were compared using Bulk Fill resin composite and incremental Nano resin composite no statistically significant disagreement between the two adhesive systems after 1 day, 1 week as well as 1 month.ConclusionThe post-operative hypersensitivity is related to many factors as the procedure of cavity preparation, adhesive approach, and type of resin composite used and placement technique of the resin composite.

Dataset Information

New Resin-Based Bulk-Fill Composites: in vitro Evaluation of Micro-Hardness and Depth of Cure as Infection Risk Indexes.

Publications

New Resin-Based Bulk-Fill Composites: <i>in vitro</i> Evaluation of Micro-Hardness and Depth of Cure as Infection Risk Indexes.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets