Effect of Low-Concentration Hydrofluoric Acid Etching on Shear Bond Strength and Biaxial Flexural Strength after Thermocycling.

ABSTRACT: This study evaluated the shear bond strength (SBS) and biaxial flexural strength (BFS) of resin cements according to the surface treatment method using low-temperature hot etching with hydrofluoric acid (HF) on a yttrium-stabilized tetragonal zirconia (Y-TZP) surface; 96 discs and 72 cubes for BFS and SBS tests for Y-TZP were randomly divided into four groups of BFS and three groups of SBS. Specimens were subjected to the following surface treatments: (1) no treatment (C), (2) air abrasion with 50 ?m Al2O3 particles (A), (3) hot etching with HF at 100 °C for 10 min (E), and (4) air abrasion + hot etching (AE). After treatments, the specimens were coated with primer, and resin cement was applied with molds. The specimens were evaluated for roughness (Ra) via scanning electron microscopy and x-ray diffraction, and the data were analyzed by an analysis of variance (ANOVA) and Kruskal-Wallis tests. Group E produced significantly higher SBS compared to group A and AE before and after thermocycling. The BFSs of all groups showed no significant differences before thermocycling; however, after thermocycling, C and E treatment groups were significantly higher compared to group A and AE. All groups showed phase transformation. Group E was observed lower monoclinic phase transformation compared to other groups.

SUBMITTER: Kang YJ

PROVIDER: S-EPMC7143885 | biostudies-literature | 2020 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Effect of Low-Concentration Hydrofluoric Acid Etching on Shear Bond Strength and Biaxial Flexural Strength after Thermocycling.

Kang You-Jung YJ Shin Yooseok Y Kim Jee-Hwan JH

Materials (Basel, Switzerland) 20200320 6

This study evaluated the shear bond strength (SBS) and biaxial flexural strength (BFS) of resin cements according to the surface treatment method using low-temperature hot etching with hydrofluoric acid (HF) on a yttrium-stabilized tetragonal zirconia (Y-TZP) surface; 96 discs and 72 cubes for BFS and SBS tests for Y-TZP were randomly divided into four groups of BFS and three groups of SBS. Specimens were subjected to the following surface treatments: (1) no treatment (C), (2) air abrasion with ...[more]

PMID: 32244878

Similar Datasets

Project description:One therapeutical alternative in the treatment of functional disorders is the use of printed oral splints. The mechanical properties of these materials are highly essential to their clinical effectiveness, and their performance may vary depending on factors such as cleaning, post-polymerization, or their orientation during construction. The objective of this in vitro investigation is to evaluate the effectiveness of the selected materials in terms of their biaxial flexural strength in relation to the criteria listed above. Splint materials were used in the printing of 720 discs. The printing process was carried out in different orientations in relation to the building platform. Either an automatic or manual cleaning process was performed on the samples. For post-polymerization, either an LED or Xenon light was utilized. A piston-on-three-ball test was used to measure the biaxial flexural strength (BFS) of the materials after they were stored in water for either 24 h or 60 days. The homogeneity of the data was controlled by employing the Levene method, and the differences between the groups were analyzed using the ANOVA and Bonferroni methods. After being stored for twenty-four hours, the mean BFS ranged anywhere from 79 MPa to 157 MPa. Following a period of sixty hours, the BFS exhibited a substantial drop and revealed values that ranged from 72 to 127 MPa. There was no significant difference that could be identified between the materials or between the various cleaning processes. The results of post-polymerization showed that the LED light produced higher means than the Xenon light did. In terms of position, the mean values varied greatly, with 0°'s mean value being 101 MPa, 45°'s mean value being 102 MPa, and 90°'s mean value being 115 MPa. The use of a build orientation of 90° and post-polymerization with LED light resulted in significantly increased biaxial flexural strength. According to this study, this design should be implemented in order to ensure that splint materials have the highest possible strength.

Dataset Information

Effect of Low-Concentration Hydrofluoric Acid Etching on Shear Bond Strength and Biaxial Flexural Strength after Thermocycling.

Publications

Effect of Low-Concentration Hydrofluoric Acid Etching on Shear Bond Strength and Biaxial Flexural Strength after Thermocycling.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets