Production and Characterization of Chitosan-Polyanion Nanoparticles by Polyelectrolyte Complexation Assisted by High-Intensity Sonication for the Modified Release of Methotrexate.

ABSTRACT: A promising strategy to improve the effectivity of anticancer treatment and decrease its side effects is to modulate drug release by using nanoparticulates (NPs) as carriers. In this study, methotrexate-loaded chitosan-polyanion nanoparticles were produced by polyelectrolyte complexation assisted by high-intensity sonication, using several anionic polymers, such as the sodium and potassium salts of poly(maleic acid-alt-ethylene) and poly(maleic acid-alt-octadecene), here named PAM-2 and PAM-18, respectively. Such NPs were analyzed and characterized according to particle size, polydispersity index, zeta potential and encapsulation efficiency. Likewise, their physical stability was tested at 4 °C and 40 °C in order to evaluate any change in the previously mentioned particle parameters. The in vitro methotrexate release was assessed at a pH of 7.4, which simulated physiological conditions, and the data were fitted to the heuristic models of order one, Higuchi, Peppas-Sahlin and Korsmeyer-Peppas. The results revealed that most of the MTX-chitosan-polyanion NPs have positive zeta potential values, sizes <280 nm and monodisperse populations, except for the NPs formed with PAM-18 polyanions. Further, the NPs showed adequate physical stability, preventing NP-NP aggregation. Likewise, these carriers modified the MTX release by an anomalous mechanism, where the NPs formed with PAM-2 polymer led to a release mechanism controlled by diffusion and relaxation, whereas the NPs formed with PAM-18 led to a mainly diffusion-controlled release mechanism.

SUBMITTER: Ciro Y

PROVIDER: S-EPMC7168905 | biostudies-literature | 2020 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Production and Characterization of Chitosan-Polyanion Nanoparticles by Polyelectrolyte Complexation Assisted by High-Intensity Sonication for the Modified Release of Methotrexate.

Ciro Yhors Y Rojas John J Rojas John J Alhajj Maria J MJ Carabali Gustavo A GA Salamanca Constain H CH

Pharmaceuticals (Basel, Switzerland) 20200108 1

A promising strategy to improve the effectivity of anticancer treatment and decrease its side effects is to modulate drug release by using nanoparticulates (NPs) as carriers. In this study, methotrexate-loaded chitosan-polyanion nanoparticles were produced by polyelectrolyte complexation assisted by high-intensity sonication, using several anionic polymers, such as the sodium and potassium salts of poly(maleic acid-<i>alt</i>-ethylene) and poly(maleic acid-<i>alt</i>-octadecene), here named PAM- ...[more]

PMID: 31936208

Similar Datasets

Project description:Smart hydrogels that can respond to external stimuli such as temperature and pH have attracted tremendous interest for biological and biomedical applications. In this work, we synthesized two alginate-graft-poly(N-isopropylacrylamide) (Alg-g-PNIPAAm) copolymers and aimed to prepare smart hydrogels through formation of polyelectrolyte complex (PEC) between the negatively charged Alg-g-PNIPAAm copolymers and the positively charged chitosan (Cts) in aqueous solutions. The hydrogels were expected to be able to respond to both temperature and pH changes due to the nature of Alg-g-PNIPAAm and chitosan. The hydrogel formation was determined by a test tube inverting method and confirmed by the rheological measurements. The rheological measurements showed that the PEC hydrogels formed at room temperature could be further enhanced by increasing temperature over the lower critical solution temperature (LCST) of PNIPAAm, because PNIPAAm would change from hydrophilic to hydrophobic upon increasing temperature over its LCST, and the hydrophobic interaction between the PNIPAAm segments may act as additional physical crosslinking. The controlled release properties of the hydrogels were studied by using the organic dye rhodamine B (RB) as a model drug at different pH. The PEC hydrogels could sustain the RB release more efficiently at neutral pH. Both low pH and high pH weakened the PEC hydrogels, and resulted in less sustained release profiles. The release kinetics data were found to fit well to the Krosmyer-Peppas power law model. The analysis of the release kinetic parameters obtained by the modelling indicates that the release of RB from the PEC hydrogels followed mechanisms combining diffusion and dissolution of the hydrogels, but the release was mainly governed by diffusion with less dissolution at pH 7.4 when the PEC hydrogels were stronger and stabler than those at pH 5.0 and 10.0. Therefore, the PEC hydrogels are a kind of smart hydrogels holding great potential for drug delivery applications.

Project description:We present here a modified, sonication-assisted transient transformation assay for rapid analysis of cis-regulatory elements. We tested promoter elements from MIR159B locus of Brassica juncea by generating stable transgenic lines and compared the transcriptional activity of GUS reporter with that of the transient assay method. To obtain reliable and repeatable results, and to omit false-positive data, we optimized several parameters including sonication duration and cycle and concentration of Agrobacterium tumefaciens measured as optical density (O.D.) at 600 nm. To the best of our knowledge, this is the first report of promoter characterization of MIR159B from Brassica juncea, and comparative analysis of stable and transient lines. Our analysis shows that the protocol described herein allows understanding promoter activity/transcriptional control in tissues other than leaf or protoplast which have remained the mainstay for transient analysis thus far. We tested reporter gene GUS under the control of constitutive promoter, CaMV 35S, and MIR159b from Brassica juncea. We optimized the duration of sonication (5-, 10- and 15-min cycle), bacterial density (measured as O.D at 600 nm?=?0.6/0.8/1.0) and Agro-infection time (5, 10, 15 min), and co-cultivation (12-, and 24-h). Sonication cycle of 10-min, followed by Agro-infection and co-cultivation with Agrobacterium tumefaciens with O.D. 600 nm?=?0.8 and for 12 h was found to be optimum. We could successfully express reporter genes in deep-seated tissues such as floral organs and pollen grains where it was previously not possible to perform transient assay. Constitutive GUS activity was observed when reporter was placed under control of the constitutive promoter of CaMV 35S. Reporter GUS when placed under transcriptional control of MIR159b promoter from Brassica juncea showed reporter activity in floral tissues, in mature pollen grains. Comparative analysis of reporter activity from stable transgenic lines at T2 generation with that of transient assay system reveals identical to near-identical reporter activity. Transient assay could be successfully performed in tissues collected not only from Arabidopsis thaliana, but also from Brassica juncea and Brassica nigra to demonstrate its wide applicability. Our modified method thus has the potential of quick and rapid analysis of promoter activity and allows us to record the developmental dynamics and spatio-temporal expression pattern driven by specific promoters. Suitable modification and controls should also allow analysis of hormonal regulation and identification of trans-factors via DNA-protein interactions. Furthermore, this method can also be extended to study promoters under various environmental conditions that otherwise do not allow growth and complete life cycle of healthy plants and can be modified to test reporter activity in other non-model plants or plants with long life cycle.

Project description:Chitosan nanofibrous membranes have immense potential in tissue engineering and drug delivery applications because of their increased surface area, high degree of biocompatibility, and their ability to mimic the extracellular matrix. However, their use is often limited due to their extreme hydrophilic nature causing them to lose their nanofibrous structure in vivo. In the present study, chitosan membranes were modified either by acylation reactions using fatty acids of different chain lengths or tert-butyloxycarbonyl (tBOC) protecting groups to increase the hydrophobicity of the membranes and protect the nanofibrous structure. The modified membranes were characterized using scanning electron microscopy, attenuated total reflectance Fourier transform infrared spectroscopy, water contact angle and elemental analysis to confirm the addition of the modification groups. These membranes were then evaluated to control the release of a hydrophobic osteogenic drug-simvastatin (SMV). The interaction between SMV and the polymer was determined using molecular modeling. Pure SMV and SMV loaded membranes were examined for their in vitro cytotoxicity and osteogenic potential using preosteoblast mouse bone marrow stromal cells. From results, it was evident that as the fatty acid chain length increased from two to six methylene groups, the hydrophobicity of the membranes increased (59.2 ± 8.2° to 94.3 ± 8.5° water contact angle). The amount of drug released from the membranes could be controlled by changing the amount of initial drug loaded and/or the type of modifications. After 4 weeks, for a 500 μg loading, the short chain fatty acid modified membranes released 17.8 ± 3.2% of the drug whereas a long chain fatty acid released only 4.8 ± 0.8%. Similarly, for a 50 μg loading, short chain modified membranes released more (73.3 ± 33.3%) of the loaded drug as compared to the long chain membranes (43.0 ± 3.5%). The long chain fatty acid membranes released SMV for extended time periods of up to 90 days. This data was further supported by molecular modeling, which revealed that SMV was more compatible with more hydrophobic membranes. Cell studies showed that pure SMV from 75 to 600 ng/ml range possessed osteogenic potential in a dose dependent manner and the amount of SMV released from the most hydrophobic FA treated membranes was not cytotoxic and supported osteogenic differentiation. Therefore, this study demonstrates our ability to control the release of a hydrophobic drug from modified chitosan membranes as per the clinical need.

Dataset Information

Production and Characterization of Chitosan-Polyanion Nanoparticles by Polyelectrolyte Complexation Assisted by High-Intensity Sonication for the Modified Release of Methotrexate.

Publications

Production and Characterization of Chitosan-Polyanion Nanoparticles by Polyelectrolyte Complexation Assisted by High-Intensity Sonication for the Modified Release of Methotrexate.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets