Evaluation of the properties of Mineral Trioxide Aggregate mixed with Zinc Oxide exposed to different environmental conditions.

ABSTRACT: Addition of zinc oxide (ZnO) to Mineral Trioxide Aggregate (MTA) has been shown to rectify tooth discoloration caused by Angelus MTA. This study evaluated the microhardness, compressive strength, calcium ion release and crystalline structures of MTA mixed with ZnO in different environmental conditions. Molds with a diameter of 4 mm and a height of 6 mm were used for compressive strength, calcium ion release and X-ray diffraction (XRD) evaluations. Molds with 6 mm diameter and 4 mm height were used for surface microhardness evaluations. Cements evaluated include Angelus MTA (Angelus, Brail), Angelus MTA + ZnO, ProRoot MTA (Dentsply Tulsa Dental, OK), and ProRoot MTA + ZnO. Each group was divided into 3 subgroups according to exposure conditions: normal saline (NS), phosphate buffered saline (PBS) or blood. After 7 days incubation, surface microhardness, compressive strength and XRD analysis was performed. Calcium ion release was evaluated after 3, 24 and 168h incubation using atomic absorption spectrophotometry. Data were analyzed by One Way Anova followed by the Tukey HSD Post hoc tests and T-Test. The significance level was set at 0.05. Addition of ZnO to Angelus and ProRoot MTA significantly decreased the compressive strength of these cements regardless of the environmental conditions (P < 0.001); however, it had no significant effect on their microhardness or calcium ion release. In conclusion, adding ZnO to Angelus and ProRoot MTA can adversely affect the compressive strength of Angelus and ProRoot MTA.

SUBMITTER: Bolhari B

PROVIDER: S-EPMC7170961 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:BackgroundMineral trioxide aggregate (MTA) is a commonly used endodontic biomaterial. The physicochemical properties of MTA have a crucial role in designating clinical outcome, and different factors can affect these properties. Various methods have been used for mixing MTA, including manual, mechanical, and ultrasonic. The aim of this systematic review was to evaluate the effect of different mixing methods on the physicochemical properties of MTA.Materials and methodsElectronic databases including PubMed, Embase, Web of Science, and Scopus were searched up to May 2022. In order to cover gray literature, the ProQuest and Google Scholar databases were also searched to detect theses and conference proceedings. For quality assessment of the included studies, we used a modified version of the Cochrane risk of bias tool for randomized controlled trials (RCTs). Experimental studies which had assessed at least one property of MTA and compared at least two different mixing methods of MTA were included in this study. All animal studies, reviews, case reports, and case series were excluded.ResultsFourteen studies were included. The results showed that the ultrasonic mixing method significantly improved some MTA characteristics, including microhardness, flowability, solubility, setting time, and porosity. However, the mechanical mixing method improved other properties including flowability, solubility, push-out bond strength, and hydration. The manual mixing method showed inferior results compared to other mixing methods in terms of microhardness, flowability, solubility, setting time, push-out bond strength, porosity, and hydration. Different mixing methods had a similar effect on compressive strength, sealing ability, pH and calcium ion release, volume change, film thickness, and flexural strength of MTA.ConclusionMechanical and ultrasonic mixing methods are superior to the manual mixing method in terms of improving physicochemical properties of MTA. No report of selection bias and varieties in methodologies were limitations of evidence.

Project description:Background and objectiveMineral trioxide aggregate (MTA) is a biomaterial used in endodontic procedures as it exerts beneficial effects on regenerative processes. In this study, we evaluate the effect of MTA on healing of periodontal ligament (PDL) and surrounding tissue, following injury, in a transgenic mouse model and on the differentiation of murine mesenchymal progenitor cells in vitro.Material and methodsWe used an inducible Cre-loxP in vivo fate mapping approach to examine the effects of MTA on the contributions of descendants of cells expressing the αSMA-CreERT2 transgene (SMA9+ ) to the PDL and alveolar bone after experimental injury to the root furcation on the maxillary first molars. Col2.3GFP was used as a marker to identify mature osteoblasts, cementoblasts and PDL fibroblasts. The effects of MTA were examined 2, 17 and 30 days after injury and compared histologically with sealing using an adhesive system. The effects of two dilutions of medium conditioned with MTA on proliferation and differentiation of mesenchymal progenitor cells derived from bone marrow (BMSC) and periodontal ligament (PDLC) in vitro were examined using the PrestoBlue viability assay, alkaline phosphatase and Von Kossa staining. The expression of markers of differentiation was assessed using real-time PCR.ResultsHistological analyses showed better repair in teeth restored with MTA, as shown by greater expansion of SMA9+ progenitor cells and Col2.3GFP+ osteoblasts compared with control teeth. We also observed a positive effect on differentiation of SMA9+ progenitors into osteoblasts and cementoblasts in the apical region distant from the site of injury. The in vitro data showed that MTA-conditioned medium reduced cell viability and osteogenic differentiation in both PDLC and BMSC, indicated by reduced von Kossa staining and lower expression of osteocalcin and bone sialoprotein. In addition, cultures grown in the presence of MTA had marked decreases in SMA9+ and Col2.3GFP+ areas as compared with osteogenic medium, confirming reduced osteogenesis.ConclusionMTA promotes regeneration of injured PDL and alveolar bone, reflected as contribution of progenitors (SMA9+ cells) into osteoblasts (Col2.3GFP+ cells). In vitro, MTA-conditioned medium fails to promote osteogenic differentiation of both PDLC and BMSC.

Dataset Information

Evaluation of the properties of Mineral Trioxide Aggregate mixed with Zinc Oxide exposed to different environmental conditions.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets