In Vitro Impact Testing to Simulate Implant-Supported Prosthesis Retrievability in Clinical Practice: Influence of Cement and Abutment Geometry.

ABSTRACT: Cement-retained implant-supported prosthetics are gaining popularity compared to the alternative screw-retained type, a rise that serves to highlight the importance of retrievability. The aim of the present investigation is to determine the influence of luting agent, abutment height and taper angle on the retrievability of abutment-coping cementations. Abutments with different heights and tapers were screwed onto an implant and their cobalt-chrome copings were cemented on the abutments using three different luting agents. The removals were performed by means of Coronaflex®. The number of impulses and the forces were recorded and analyzed with a Kruskal-Wallis test. Harvard cement needed the highest number of impulses for retrieval, followed by Telio CS and Temp Bond. However, abutment height and taper showed a greater influence on the cap's retrievability (p < 0.05). Long and tapered abutments provided the highest percentage of good retrievability. The influence of the luting agent and the abutment geometry on the cap's retrieval performed by Coronaflex® reflects data from literature about the influence of the same factor on the maximum force reached during uniaxial tensile tests. The impulse force was slightly affected by the same factors.

SUBMITTER: Lugas AT

PROVIDER: S-EPMC7178674 | biostudies-literature | 2020 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

In Vitro Impact Testing to Simulate Implant-Supported Prosthesis Retrievability in Clinical Practice: Influence of Cement and Abutment Geometry.

Lugas Andrea T AT Terzini Mara M Zanetti Elisabetta M EM Schierano Gianmario G Manzella Carlo C Baldi Domenico D Bignardi Cristina C Audenino Alberto L AL

Materials (Basel, Switzerland) 20200409 7

Cement-retained implant-supported prosthetics are gaining popularity compared to the alternative screw-retained type, a rise that serves to highlight the importance of retrievability. The aim of the present investigation is to determine the influence of luting agent, abutment height and taper angle on the retrievability of abutment-coping cementations. Abutments with different heights and tapers were screwed onto an implant and their cobalt-chrome copings were cemented on the abutments using thr ...[more]

PMID: 32283615

Similar Datasets

Project description:BackgroundThe association between peri-implant diseases and the periodontal, implant, and prosthesis characteristics has been characterized in various ways.PurposeThe aim of this study was to evaluate the link between the peri-implant and periodontal status and the influence of implant and prosthesis parameters during implant follow-up.Materials and methodsOne hundred and seven patients with a total of 310 implants that had at least one year of function who were attending periodontal and implant maintenance at a university clinic setting were included in this cross-sectional study. The demographic, periodontal, peri-implant tissue, implant, and prosthesis parameters were recorded. A pocket depth > 4 mm with bleeding on probing defined periodontal/peri-implant soft tissue diseased sites. Analyses were performed at the patient and implant levels using univariable and multivariable mixed regression analysis.ResultsThe mean implant follow-up was 7.22 years. At the patient level, the bleeding on probing and pocket depth measurements were more pronounced around the implant than around the teeth. The opposite was observed for plaque and the clinical attachment levels. At the implant level, multivariable analysis showed that the periodontal and corresponding peri-implant tissue parameters, such as diseased sites, were closely related. The implant location, bone level, and number were selectively associated with the implant bone level, while cemented retention and emergence restoration profile influenced the implant pocket depth.ConclusionsThe present study suggested that clinical peri-implant and periodontal soft tissue statuses were different, which could be a consequence of the initial implant and prosthesis healing process. However, during implant follow-up, the peri-implant parameters were predominantly associated with their corresponding periodontal parameters regardless of an association with the implant and prosthesis characteristics. This trial is registered with ClinicalTrials.gov ID: NCT03841656.

Project description:The purpose of this paper was to determine the effect of anodization on the in vitro proliferation and adhesion of immortalized human keratinocytes (HaCats) and mouse bone marrow-derived mesenchymal stem cells (BM-MSCs) in Titanium Grade 23 (Ti6Al4V ELI) discs and to describe the surface topography, roughness, and composition of dental implants (body and collar) and abutments submitted to an area-specific anodization process. HaCat cells and BM-MSCs were seeded onto discs with three different surface treatments: machined, area-specific anodization for abutments, and area-specific anodization for implant collars. Cell proliferation was assessed using a resazurin-based fluorescent dye on days 1, 3, and 7, while cell adhesion was examined using scanning electron microscopy (SEM). Surface topography, roughness, and composition were evaluated for six implant bodies with an anodized rough surface, six anodized implant smooth collars, and six anodized prosthetic abutments. Both HaCats and BM-MSCs showed increased viability over time (p < 0.001) with no statistically significant differences among the different surfaces (p = 0.447 HaCats and p = 0.631 BM-MSCs). SEM analysis revealed an enhanced presence and adhesion of HaCat cells on the anodized surface for the implant collars and an increased adhesion of BM-MSCs on both the anodized and machined surface abutments. The topography characteristics of the treated implants and abutments varied depending on the specific implant region. Chemical analysis confirmed the presence of oxygen, calcium, phosphorus, and sodium on the anodized surfaces. The area-specific anodization process can be utilized to create variable topography, increase the specific surface area, and introduce oxygen, calcium, phosphorus, and sodium to dental implants and abutments. While BM-MSCs and HaCat cells showed similar adhesion and proliferation on anodized and machined surfaces, a positive interaction between anodized Ti6Al4V ELI surfaces and these two cell lines present in the peri-implant mucosa was observed. Due to the limitations of the present study, further research is necessary to confirm these findings.

Dataset Information

In Vitro Impact Testing to Simulate Implant-Supported Prosthesis Retrievability in Clinical Practice: Influence of Cement and Abutment Geometry.

Publications

In Vitro Impact Testing to Simulate Implant-Supported Prosthesis Retrievability in Clinical Practice: Influence of Cement and Abutment Geometry.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets