Reactive Comb Polymer Compatibilized Immiscible PVDF/PLLA Blends: Effects of the Main Chain Structure of Compatibilizer.

ABSTRACT: The compatibilizer with double comb structure has a superior compatibilizing effect for immiscible polymer blends due to the symmetrical structure on both sides of main chains. Extensive study related to the architectural effects of compatibilizer on the compatibilization has mainly focused on the side chains. We investigated the influence of the compatibilizer-main-chain structure on the compatibilizing effect for immiscible poly(vinylidene fluoride)/poly(L-lactic acid) (PVDF/PLLA) blends. Two reactive-comb compatibilizers with polystyrene (PS) and polymethylmethacrylate (PMMA) as main chains and PMMA as the side chains have been synthesized. PS is immiscible with both PLLA and PVDF, while PMMA is miscible with PVDF. It was found that both compatibilizers can improve the compatibility between the PLLA and PVDF, with different compatibilization effects. In the PVDF/PLLA (50/50) blends, 1 wt.% poly(styrene-co-glycidyl methacrylate)-graft-poly(methyl methacrylate) (RC-SG) tuned the morphology from the droplet-in-matrix structure to the co-continuous structure, while the blends with poly(methyl methacrylate-co-glycidyl methacrylate)-graft-poly(methyl methacrylate) (RC-MMG) kept the sea-island structure with even 3 wt.% loading. Moreover, RC-SG induces a wider co-continuous interval range than RC-MMG. The co-continuous structure obtained by RC-SG was also more stable than that by RC-MMG. It was further found that RC-SG-compatibilized PVDF/PLLA blends exhibit higher mechanical properties than the RC-MMG-compatibilized blends.

SUBMITTER: Yang X

PROVIDER: S-EPMC7182944 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Compatibilized Immiscible Polymer Blends for Gas Separations.

Project description:Membrane-based gas separation has attracted a great deal of attention recently due to the requirement for high purity gasses in industrial applications like fuel cells, and because of environment concerns, such as global warming. The current methods of cryogenic distillation and pressure swing adsorption are energy intensive and costly. Therefore, polymer membranes have emerged as a less energy intensive and cost effective candidate to separate gas mixtures. However, the use of polymeric membranes has a drawback known as the permeability-selectivity tradeoff. Many approaches have been used to overcome this limitation including the use of polymer blends. Polymer blending technology synergistically combines the favorable properties of different polymers like high gas permeability and high selectivity, which are difficult to attain with a single polymer. During polymer mixing, polymers tend to uncontrollably phase separate due to unfavorable thermodynamics, which limits the number of completely miscible polymer combinations for gas separations. Therefore, compatibilizers are used to control the phase separation and to obtain stable membrane morphologies, while improving the mechanical properties. In this review, we focus on immiscible polymer blends and the use of compatibilizers for gas separation applications.

| S-EPMC5509093 | biostudies-literature

Role of Plasticizers on PHB/bio-TPE Blends Compatibilized by Reactive Extrusion.

Project description:Poly(hydroxybutyrate) (PHB) is a biopolymer biologically synthesized by controlled bacterial fermentation from a wide variety of microorganisms. PHB is proposed as a potential green alternative to commonly used plastics in packaging, due to its biodegradability and biocompatibility. However, if PHB is to replace commodities, it has some limitations regarding its thermo-mechanical performance to overcome. Among them are its critically the low toughness values at room temperature and poor thermoforming ability. With the aim of overcoming these weaknesses, in this work, blends of PHB with the addition of a biodegradable thermoplastic elastomer (bio-TPE) were prepared and evaluated. Films of such compounds were made by cast extrusion. In order to enhance the compatibility of both polymers during the extrusion process, three different reactive agents (poly-hexametylene diisocianate, triglycidyl isocyanurate, and Joncryl® ADR-4368) were assessed. The morphology and mechanical- and thermal properties of the films obtained were analyzed. In addition, the thermoforming ability of the produced films was evaluated. The results show that the plasticizers present in the bio-TPE interacted with the reactive agents, making them chemical competitors and altering the outcome of the blends.

| S-EPMC8840646 | biostudies-literature

Rheological and Crystallization Properties of ABS/PA6-Compatibilized Blends via In Situ Reactive Extrusion.

Project description:ABS/PA6-compatibilized blends were prepared by in situ reactive extrusion method. The main objective was to evaluate the influences of the morphology and blend composition on the rheological and nonisothermal crystallization properties. The morphology of submicron-sized ABS droplets evenly dispersed in PA6 led to dilatant fluid behavior and a transition from elastic to viscous behavior in the low-frequency region. The crystallization results indicated that reactive blends had elevated crystallization temperatures and crystallization rates, which were due to the heterogeneous nucleation of the submicron-sized ABS particles. In addition, it was observed that the theory by Mo suitably described the nonisothermal crystallization process. The activation energy slightly decreased for ABS contents of 5 and 15 wt % and then increased for a content of 25 wt %, indicating that the ABS promoted the crystallization of the blends at appropriate contents.

| S-EPMC7331037 | biostudies-literature

Electrospun Porous Nanofibers with Imprinted Patterns Induced by Phase Separation of Immiscible Polymer Blends.

Project description:Nanofibrous nonwoven fabrics have attracted attention as porous adsorbents with high specific surface areas for the safe and efficient treatment of spilled organic dyes and petroleum. For this purpose, a method of fabricating porous nanofibers with high specific surface areas would be highly beneficial. In this study, the phase separation in nanofibers electrospun from blended solutions of immiscible polymers [poly(styrene) (PS) and poly(vinylpyrrolidone) (PVP)] was investigated. The removal of PVP as a sacrificial polymer afforded the imprinting of mesopores (40-70 nm) in the PS nanofibers. The effects of solution composition (PS/PVP in N,N-dimethylformamide) on the structure formation in the fibers were investigated. The nanofibers thus obtained could selectively adsorb low-molecular-weight hydrophobic dyes, such as Nile Red and Oil Red O. Thus, it is expected that the combined approach of electrospinning of immiscible polymer blends and phase separation-induced patterning can be applied to the fabrication of functional nanofibers for diverse applications.

| S-EPMC9202247 | biostudies-literature

Green Processes for Green Products: The Use of Supercritical CO₂ as Green Solvent for Compatibilized Polymer Blends.

Project description:Polycaprolactone-g-glycidyl methacrylate (PCL-g-GMA), a reactive interfacial agent for PCL-starch blends, is synthesized using supercritical carbon dioxide (scCO₂) as reaction medium and relatively high molecular weight PCL (Mw = 50,000). Higher GMA and radical initiator intakes lead to higher functionalization degrees (FD) for PCL-g-GMA samples. A mathematical model is developed to describe the correlation between monomer and initiator intake and FD values. The model shows an excellent R²-value (0.978), which implies a good fit of the experimental data. Comparison of this model with a similar one for the reaction in the melt clearly indicates a better reaction efficiency in scCO₂. Furthermore, GPC results show that less degradation occurred for samples made in scCO₂. Finally, the use of the PCL-g-GMA made in scCO₂ (as interfacial agent) in ternary blend of PCL/starch/PCL-g-GMA results in better mechanical properties with respect to those obtained by using the same graft-copolymer as prepared in the melt.

| S-EPMC6401873 | biostudies-literature

Investigation of PLLA/PCL blends and paclitaxel release profiles.

Project description:Blends of poly (L-lactide) (PLLA) and poly (?-caprolactone) (PCL) with and without paclitaxel were prepared via solution casting. DSC analysis as well as SEM analysis of the PLLA/PCL blend solution cast films showed that these blends are all phase separated.%PLLA crystallinity was found to increase with increasing PCL content (up till 15 wt.%). The PCL phase is found to homogeneously disperse in the PLLA matrix as spherical domains where the pore diameters of the PCL domains significantly increased with increasing PCL content. The degradation profiles matched with the slower degrading component PCL rather than PLLA and also increasing PCL content of the blends increased the degradation rate relatively. The increased crystallinity of the PLLA phase with increasing PCL contents confirmed that the degradation occurred through PCL phase. Cell proliferation on PLLA/PCL blends showed that all these blends were suitable for the support of cellular growth. Apoptosis assay with the paclitaxel-loaded PLLA/PCL blends showed an increase in cell death throughout 7 days of incubation where the cell death was increased with increasing PCL contents. This was attributed to the faster release of paclitaxel which was at least partially affected by the faster degradation rate at increasing PCL contents. The paclitaxel release was shown to be degradation controlled in the initial stages followed by a faster diffusion-controlled release in the later stages. These polymer blends were found to be very suitable paclitaxel release agents for which the paclitaxel release times can be altered with the composition of the blend and the film thickness.

| S-EPMC3225542 | biostudies-literature

Mechanical Upcycling Immiscible Polyethylene Terephthalate-Polypropylene Blends with Carbon Fiber Reinforcement.

Project description:Ineffective sorting of post-consumer plastics remains one of the major obstacles in the recycling of plastics. Consequently, these highly heterogeneous, mixed post-consumer plastics will end up in landfill or have to be incinerated as repurposing them directly would lead to a polymer blend with inferior quality for many end-uses. In this work, we demonstrate the use of carbon fibers (CFs) to practically upgrade the mechanical properties of mixed plastics, adding value to them. This will create a stronger demand for mixed plastics to be used in various engineering applications. Using polyethylene terephthalate (PET) and polypropylene (PP) as the model immiscible polymer blend, we showed that the incorporation of CFs increased the tensile, flexural, and single-edge notched fracture toughness of the resulting CF-reinforced PET/PP composite blends. Despite the high environmental burden associated with the production of CFs, cradle-to-grave life-cycle analysis showed that CF-reinforced PET/PP composites have a lower environmental impact than the life-cycle scenarios of "doing nothing" and repurposing immiscible PET/PP blends as it is without CF reinforcement. This can be attributed to the weight saving achieved, a direct result of their higher mechanical performance. Our work opens up opportunities for the use of mixed plastics in various higher value applications such that they can be diverted away from landfill or incineration, in line with the concept of circular economy.

| S-EPMC9112279 | biostudies-literature

Novel tunable super-tough materials from biodegradable polymer blends: nano-structuring through reactive extrusion.

Project description:Structuring blends on sub-micrometer scales, especially nano-scales, has a higher potential for improving their thermomechanical properties. Here, we propose a design strategy to fabricate compatible nano-blends by manipulating the reactions between two biodegradable polymers, e.g. polybutylene succinate (PBS) and polybutylene adipate terephthalate (PBAT), with extremely low free radical contents through reactive extrusion processing. Observed by transmission electron microscopy (TEM) and atomic force microscopy (AFM), it is found that PBAT is tightly surrounded by large amounts of PBS-PBAT co-polymers and dispersed in a PBS matrix with a particle size of less than 100 nm. We show how impact strength and polymer moduli can be improved simultaneously by decreasing the small amount of dispersed phase into nano-scale (droplet or lamina structures). With 5 wt% PBAT content in the PBS-PBAT blend, the notched impact strength of PBS is increased 1200% and the Young's modulus is increased 15%. Through in situ rheological monitoring and Fourier-transform infrared spectroscopy (FTIR) studies, the reason why nano-blends can be formed in such a low amount of peroxide is illustrated. Our investigation most significantly indicates the transformation of the partially compatible PBS-PBAT micro-blend into a fully compatible PBS-PBAT through nano-structuring. This work addresses the importance of reaction rate and mechanism in favoring the formation of co-polymers rather than homo-polymer crosslinking or self-decomposition in polymer blend modification via reactive extrusion design.

| S-EPMC9060287 | biostudies-literature

Morphology Mapping of Nanoparticle-Filled Immiscible Polymer Blends in Flow: The Existence of a Critical Ratio between Nanoparticle Concentration and Droplet Concentration.

Project description:The delicate flow-induced morphology of immiscible polypropylene/polystyrene blends in the presence of silica nanoparticles (NPs) is investigated in a multiparameter space. The morphology map constructed based on in situ morphology observation reveals that a critical ratio of NP concentration to droplet concentration, which strongly depends on the NP surface chemistries and the ratio of the NP concentration to the droplet concentration, exists. Below or above the critical ratio, the NPs display diverse effects on the morphology (promote or suppress droplet coalescence). These results can be interpreted by the competition between the bridging mechanism (acceleratory effect) and the enhanced viscoelasticity (inhibitory effect) exerted by the NPs.

| S-EPMC6645428 | biostudies-literature

Main chain selective polymer degradation: controlled by the wavelength and assembly.

Project description:The advent of reversible deactivation radical polymerization (RDRP) revolutionized polymer chemistry and paved the way for accessing synthetic polymers with controlled sequences based on vinylic monomers. An inherent limitation of vinylic polymers stems from their all-carbon backbone, which limits both function and degradability. Herein, we report a synthetic strategy utilizing radical ring-opening polymerization (rROP) of complementary photoreactive cyclic monomers in combination with RDRP to embed photoresponsive functionality into desired blocks of polyvinyl polymers. Exploiting different absorbances of photoreactive cyclic monomers, it becomes possible to degrade blocks selectively by irradiation with either UVB or UVA light. Translating such primary structures of polymer sequences into higher order assemblies, the hydrophobicity of the photodegradable monomers allowed for the formation of micelles in water. Upon exposure to light, the nondegradable blocks detached yielding a significant reduction in the micelle hydrodynamic diameter. As a result of the self-assembled micellar environment, telechelic oligomers with photoreactive termini (e.g., coumarin or styrylpyrene) resulting from the photodegradation of polymers in water underwent intermolecular photocycloaddition to photopolymerize, which usually only occurs efficiently at longer wavelengths and a much higher concentration of photoresponsive groups. The reported main chain polymer degradation is thus controlled by the irradiation wavelength and the assembly of the polymers.

| S-EPMC11304539 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data