Direct resin composite restoration of endodontically-treated permanent molars in adolescents: bite force and patient-specific finite element analysis.

ABSTRACT: Objective To evaluate the influence of three levels of dental structure loss on stress distribution and bite load in root canal-treated young molar teeth that were filled with bulk-fill resin composite, using finite element analysis (FEA) to predict clinical failure. Methodology Three first mandibular molars with extensive caries lesions were selected in teenager patients. The habitual occlusion bite force was measured using gnathodynamometer before and after endodontic/restoration procedures. The recorded bite forces were used as input for patient-specific FEA models, generated from cone-beam computed tomographic (CT) scans of the teeth before and after treatment. Loads were simulated using the contact loading of the antagonist molars selected based on the CT scans and clinical evaluation. Pre and post treatment bite forces (N) in the 3 patients were 30.1/136.6, 34.3/133.4, and 47.9/124.1. Results Bite force increased 260% (from 36.7±11.6 to 131.9±17.8 N) after endodontic and direct restoration. Before endodontic intervention, the stress concentration was located in coronal tooth structure; after rehabilitation, the stresses were located in root dentin, regardless of the level of tooth structure loss. The bite force used on molar teeth after pulp removal during endodontic treatment resulted in high stress concentrations in weakened tooth areas and at the furcation. Conclusion Extensive caries negatively affected the bite force. After pulp removal and endodontic treatment, stress and strain concentrations were higher in the weakened dental structure. Root canal treatment associated with direct resin composite restorative procedure could restore the stress-strain conditions in permanent young molar teeth.

SUBMITTER: Rodrigues MP

PROVIDER: S-EPMC7185981 | biostudies-literature | 2020

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Direct resin composite restoration of endodontically-treated permanent molars in adolescents: bite force and patient-specific finite element analysis.

Rodrigues Monise de Paula MP Soares Priscilla Barbosa Ferreira PBF Gomes Márcio Alex Barros MAB Pereira Renata Afonso RA Tantbirojn Daranee D Versluis Antheunis A Soares Carlos Jose CJ

Journal of applied oral science : revista FOB 20200427

Objective To evaluate the influence of three levels of dental structure loss on stress distribution and bite load in root canal-treated young molar teeth that were filled with bulk-fill resin composite, using finite element analysis (FEA) to predict clinical failure. Methodology Three first mandibular molars with extensive caries lesions were selected in teenager patients. The habitual occlusion bite force was measured using gnathodynamometer before and after endodontic/restoration procedures. T ...[more]

PMID: 32348440

Similar Datasets

Project description:BackgroundMolar-incisor hypomineralization (MIH) is a common condition among children that significantly increases the risk of caries. The objective of this research was to evaluate the clinical success of giomer- and conventional resin-based sealants applied on first permanent molars (FPMs) affected by MIH.MethodsOne-hundred FPMs with MIH which were indicated for non-invasive fissure sealant were selected in 39 children, aged 6-12 years. Using a split mouth design, the FPMs were randomized into two groups; Group 1. Resin sealant (etch-and-rinse + Conceal F) and Group 2. Giomer sealant (self-etch primer + BeautiSealant). Clinical evaluation was performed using the modified United States Public Health Service (USPHS) criteria at 1, 3, 6 and 12 months. The Log-rank, Fisher's exact test and Kaplan-Meier analysis were used for statistical analysis.ResultsAt 12 months, the retention rates in Group 1 and Group 2 were 68% and %8, respectively (p = 0.000). The cumulative survival rates of conventional resin sealants were significantly higher than giomer sealants for all follow-up visits (p < 0.05). In Groups 1 and 2, the distribution of unsuccessful sealants on mandibular vs maxillary FPMs were 32.1% vs 31.8% (p = 0.612) and 91.7% vs 92.3% (p = 0.664), respectively. Although the success rate was higher for teeth with white opacities or lesions with less extension in Group 1, no significant difference was found. The average survival time was found as 10.46 ± 3.21 months in Group 1 and 4.02 ± 4.43 months in Group 2.ConclusionsThe conventional resin-based sealants yielded a better clinical performance over the 12-month evaluation period than the giomer sealants which were applied with self-etch primer. The high failure rate observed in giomer sealants could be explained by the possible deficiency in the etching capacity of self-etch primer on MIH-affected teeth. Trial registration ClinicalTrials.gov, NCT04929782. Registered 10 June 2021-Retrospectively registered, https://clinicaltrials.gov/ct2/show/NCT04929782 .

Dataset Information

Direct resin composite restoration of endodontically-treated permanent molars in adolescents: bite force and patient-specific finite element analysis.

Publications

Direct resin composite restoration of endodontically-treated permanent molars in adolescents: bite force and patient-specific finite element analysis.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets