Irreversible Structural Changes of Copper Hexacyanoferrate Used as a Cathode in Zn-Ion Batteries.

ABSTRACT: The structural changes of copper hexacyanoferrate (CuHCF), a Prussian blue analogue, which occur when used as a cathode in an aqueous Zn-ion battery, are investigated using electron microscopy techniques. The evolution of Znx Cu1-x HCF phases possessing wire and cubic morphologies from initial CuHCF nanoparticles are monitored after hundreds of cycles. Irreversible introduction of Zn ions to CuHCF is revealed locally using scanning transmission electron microscopy. A substitution mechanism is proposed to explain the increasing Zn content within the cathode material while simultaneously the Cu content is lowered during Zn-ion battery cycling. The present study demonstrates that the irreversible introduction of Zn ions is responsible for the decreasing Zn ion capacity of the CuHCF cathode in high electrolyte concentration.

SUBMITTER: Lim J

PROVIDER: S-EPMC7187350 | biostudies-literature | 2020 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Irreversible Structural Changes of Copper Hexacyanoferrate Used as a Cathode in Zn-Ion Batteries.

Lim Joohyun J Kasiri Ghoncheh G Sahu Rajib R Schweinar Kevin K Hengge Katharina K Raabe Dierk D La Mantia Fabio F Scheu Christina C

Chemistry (Weinheim an der Bergstrasse, Germany) 20200225 22

The structural changes of copper hexacyanoferrate (CuHCF), a Prussian blue analogue, which occur when used as a cathode in an aqueous Zn-ion battery, are investigated using electron microscopy techniques. The evolution of Zn<sub>x</sub> Cu<sub>1-x</sub> HCF phases possessing wire and cubic morphologies from initial CuHCF nanoparticles are monitored after hundreds of cycles. Irreversible introduction of Zn ions to CuHCF is revealed locally using scanning transmission electron microscopy. A substi ...[more]

PMID: 31782839

Similar Datasets

Project description:Dual-ion batteries (DIBs) generally operate beyond 4.7 V vs Li+/Li0 and rely on the intercalation of both cations and anions in graphite electrodes. Major challenges facing the development of DIBs are linked to electrolyte decomposition at the cathode-electrolyte interface (CEI), graphite exfoliation, and corrosion of Al current collectors. In this work, X-ray photoelectron spectroscopy (XPS) is employed to gain a broad understanding of the nature and dynamics of the CEI built on anion-intercalated graphite cycled both in highly concentrated electrolytes (HCEs) of common lithium salts (LiPF6, LiFSI, and LiTFSI) in carbonate solvents and in a typical ionic liquid. Though Al metal current collectors were adequately stable in all HCEs, the Coulombic efficiency was substantially higher for HCEs based on LiFSI and LiTFSI salts. Specific capacities ranging from 80 to 100 mAh g-1 were achieved with a Coulombic efficiency above 90% over extended cycling, but cells with LiPF6-based electrolytes were characterized by <70% Coulombic efficiency and specific capacities of merely ca. 60 mAh g-1. The poor performance in LiPF6-containing electrolytes is indicative of the continual buildup of decomposition products at the interface due to oxidation, forming a thick interfacial layer rich in LixPFy, POxFy, LixPOyFz, and organic carbonates as evidenced by XPS. In contrast, insights from XPS analyses suggested that anion intercalation and deintercalation processes in the range from 3 to 5.1 V give rise to scant or extremely thin surface layers on graphite electrodes cycled in LiFSI- and LiTFSI-containing HCEs, even allowing for probing anions intercalated in the near-surface bulk. In addition, ex situ Raman, SEM and TEM characterizations revealed the presence of a thick coating on graphite particles cycled in LiPF6-based electrolytes regardless of salt concentration, while hardly any surface film was observed in the case of concentrated LiFSI and LiTFSI electrolytes.

Dataset Information

Irreversible Structural Changes of Copper Hexacyanoferrate Used as a Cathode in Zn-Ion Batteries.

Publications

Irreversible Structural Changes of Copper Hexacyanoferrate Used as a Cathode in Zn-Ion Batteries.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets