Green Treatment of Phosphate from Wastewater Using a Porous Bio-Templated Graphene Oxide/MgMn-Layered Double Hydroxide Composite.

ABSTRACT: Excessive phosphorus in water is the primary culprit for eutrophication, which causes approximately $2.2 billion annual economic loss in the United States. This study demonstrates a phosphate-selective sustainable method by adopting Garcinia subelliptica leaves as a natural bio-template, where MgMn-layered double hydroxide (MgMn-LDH) and graphene oxide (GO) can be grown in situ to obtain L-GO/MgMn-LDH. After calcination, the composite shows a hierarchical porous structure and selective recognition of phosphate, which achieves significantly high and recyclable selective phosphate adsorption capacity and desorption rate of 244.08 mg-P g^-1 and 85.8%, respectively. The detail variation of LDHs during calcination has been observed via in situ transmission electron microscope (TEM). Moreover, the roles in facilitating phosphate adsorption and antimicrobial ability of chemical constituents in Garcinia subelliptica leaves, biflavonoids, and triterpenoids have been investigated. These results indicate the proposed bio-templated adsorbent is practical and eco-friendly for phosphorus sustainability in commercial wastewater treatment.

SUBMITTER: Lai YT

PROVIDER: S-EPMC7195549 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Layered zinc hydroxide as an adsorbent for phosphate removal and recovery from wastewater.

Project description:At present, phosphate removal and recovery from wastewater is gaining wide attention due to the dual issues of eutrophication, caused by the increased production of algae, and universal phosphorus scarcity. In this study, a layered zinc hydroxide (LZH) was synthesized by a simple precipitation method and characterized via various techniques. Experiments investigating the effect of contact time, pH, LZH dose, initial phosphate concentration, and co-existing ions on phosphate adsorption were conducted. LZH exhibited a high phosphate adsorption capacity (135.4 mg g-1) at a neutral pH. More than 50% of phosphate was removed within the first 60 s of contact time at an initial phosphate concentration of 5 mg L-1. Phosphate removal using the as-prepared LZH adsorbent was also tested in real treated sewage effluent reducing the residual phosphate amount to levels inhibiting to the growth of algae. Furthermore, phosphate desorption from LZH was investigated using acetic acid and sodium hydroxide regenerants which showed to be very effective for phosphate recovery.

| S-EPMC9040826 | biostudies-literature

Preparation of Polystyrene Microsphere-Templated Porous Monolith for Wastewater Filtration.

Project description:Porous monoliths prepared using templates are highly sought after for filtration applications due to their good mass transport properties and high permeability. Current templates, however, often lead to the formation of dead-end pores and irregular pore distributions, which reduce the efficiency of the substrate flow across the monolith column. This study focused on the preparation of a microsphere-templated porous monolith for wastewater filtration. The optimal template/monomer ratio (50:50, 60:40, 70:30) was determined, and appropriate template removal techniques were assessed for the formation of homogenous pores. The physicochemical characteristics and pore homogeneity of the monoliths were examined. The 60:40 ratio was determined to result in monoliths with homogeneous pore distributions ranging from 1.9 μm to 2.3 μm. SEM and FTIR investigations revealed that solvent treatment was effective for removing templates from the resulting solid monolith. The water quality assessments revealed reductions in the turbidity and the total number of suspended particles in the tested wastewater of up to 96-99%. The findings of this study provide insightful knowledge regarding the fabrication of monoliths with homogenous pores that are beneficial for wastewater treatment.

| S-EPMC8658112 | biostudies-literature

Efficient Removal of Phosphate from Wastewater by a Novel Phyto-Graphene Composite Derived from Palm Byproducts.

Project description:The increased demand for clean water especially in overpopulated countries is of great concern; thus, the development of eco-friendly and cost-effective techniques and materials that can remediate polluted water for possible reuse in agricultural purposes can offer a life-saving solution to improve human welfare, especially in view of climate change impacts. In the current study, the agricultural byproducts of palm trees have been used for the first time as a carbon source to produce graphene functionalized with ferrocene in a composite form to enhance its water treatment potential. Scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy, X-ray diffraction (XRD), ultraviolet-visible, Fourier transform infrared spectroscopy, zeta potential, thermogravimetric analysis, and Raman techniques have been used to characterize the produced materials. SEM investigations confirmed the formation of multiple sheets of the graphene composite. Data collected from the zeta potential revealed that graphene was supported with a negative surface charge that maintains its stability while XRD elucidated that graphene characteristic peaks were evident at 2θ = 22.4 and 22.08° using palm leaves and fibers, respectively. Batch adsorption experiments were conducted to find out the most suitable conditions to remove PO4 3- from wastewater by applying different parameters, including pH, adsorbent dose, initial concentration, and time. Their effect on the adsorption process was also investigated. Results demonstrated that the best adsorption capacity was 58.93 mg/g (removal percentage: 78.57%) using graphene derived from palm fibers at 15 mg L-1 initial concentration, pH = 3, dose = 10 mg, and 60 min contact time. Both linear and non-linear forms of kinetic and isotherm models were investigated. The adsorption process obeyed the pseudo-second-order kinetic model and was well fitted to the Langmuir isotherm.

| S-EPMC9753538 | biostudies-literature

One-step synthesis of Nickle Iron-layered double hydroxide/reduced graphene oxide/carbon nanofibres composite as electrode materials for asymmetric supercapacitor.

Project description:A novel NiFe-LDH/RGO/CNFs composite was produced by using a facile one-step hydrothermal method as electrode for supercapacitor. Compared with NiFe-LDH/CNFs, NiFe-LDH/CNTs and NiFe-LDH/RGO, NiFe-LDH/RGO/CNFs demonstrated a high specific capacitance of 1330.2 F g-1 at 1 A g-1 and a super rate capability of 64.2% from 1 to 20 A g-1, indicating great potential for supercapacitor application. Additionally, an asymmetric supercapacitor using NiFe-LDH/RGO/CNFs composite as positive electrode material and activated carbon as negative electrode material was assembled. The asymmetric supercapacitor can work in the voltage range of 0-1.57 V. It displayed high energy density of 33.7 W h kg-1 at power density of 785.8 W kg-1 and excellent cycling stability with 97.1% of the initial capacitance after 2500 cycles at 8 A g-1. Two flexible AC//LDH-RGO-CNFs ASC devices connected in series were able to light up a red LED indicator after being fully charged. The results demonstrate that the AC//LDH-RGO-CNFs ASC has a promising potential in commercial application.

| S-EPMC5995954 | biostudies-literature

Facile synthesis approach of bifunctional Co-Ni-Fe oxyhydroxide and spinel oxide composite electrocatalysts from hydroxide and layered double hydroxide composite precursors.

Project description:Zinc-air batteries (ZABs) are promising candidates for the next-generation energy storage systems, however, their further development is severely hindered by kinetically sluggish oxygen evolution reaction (OER) and oxygen reduction reaction (ORR). Facile synthesis approaches of highly active bifunctional electrocatalysts for OER and ORR are required for their practical applications. Herein, we develop a facile synthesis procedure for composite electrocatalysts composed of OER-active metal oxyhydroxide and ORR-active spinel oxide containing Co, Ni and Fe from composite precursors consisting of metal hydroxide and layered double hydroxide (LDH). Both hydroxide and LDH are simultaneously produced by a precipitation method with a controlled molar ratio of Co2+, Ni2+ and Fe3+ in the reaction solution, and calcination of the precursor at a moderate temperature provides composite catalysts of metal oxyhydroxides and spinel oxides. The composite catalyst shows superb bifunctional performances with a small potential difference of 0.64 V between a potential of 1.51 V vs. RHE at 10 mA cm-2 for OER and a half-wave potential of 0.87 V vs. RHE for ORR. The rechargeable ZAB assembled with the composite catalyst as an air-electrode exhibits a power density of 195 mA cm-2 and excellent durability of 430 hours (1270 cycles) of a charge-discharge cycle test.

| S-EPMC10071814 | biostudies-literature

Layered double hydroxide nanocomposite for drug delivery systems; bio-distribution, toxicity and drug activity enhancement.

Project description:The production of layered double hydroxide(LDH) nanocomposite as an alternative drug delivery system against various ailments is on the increase. Their toxicity potential is usually dose and time dependent with particle sizes, shapes and surface charge playing some role both in the in vitro and in vivo studies. The reticular endothelial system of especially the liver and spleen were shown to sequestrate most of these nanocomposite, especially those with sizes greater than 50 nm. The intracellular drug delivery by these particles is mainly via endocytotic pathways aided by the surface charges in most cases. However, structural modification of these nanocomposite via coating using different types of material may lower the toxicity where present. More importantly, the coating may serve as targeting ligand hence, directing drug distribution and leading to proper drug delivery to specific area of need; it equally decreases the unwanted nanocomposite accumulation in especially the liver and spleen. These nanocomposite have the advantage of wider bio-distribution irrespective of route of administration, excellent targeted delivery potential with ease of synthetic modification including coating.

| S-EPMC4149231 | biostudies-literature

Converting Spent Cu/Fe Layered Double Hydroxide into Cr(VI) Reductant and Porous Carbon Material.

Project description:Recycling solid waste as functional materials is important for both environmental remediation and resource recycling. This study attempts to recycle spent Cu/Fe layered double hydroxide (Cu/Fe-LDH) which is generated from the adsorption of dyes by converting to Cr(VI) reductant and porous carbon material. Results showed that the obtained reductant was mainly composed of Fe0 and Cu0, and exhibited good reductive activity toward Cr(VI). The species of Fe0, Fe2+, Cu0, and Cu+ all favored the reduction of Cr(VI) according to X-ray photoelectron spectroscopy analysis. During Cr(VI) removal, solution pH could increase to neutral which caused the metal ions to precipitate near completion. On the other hand, the spent Cu/Fe-LDH could be employed to produce porous carbon materials, and the generated waste metals solution herein could be reused for LDH synthesis. Specific surface areas of the obtained carbon materials varied from 141.3-744.2?m2/g with changes in adsorbed amount of dyes on the LDH. This study illustrates that all the components of wastes can be useful resources, offering a simple recycling approach for similar organic-inorganic solid wastes. This work also enlightens us that designing a proper initial product is crucial to make waste recycling simpler.

| S-EPMC5544766 | biostudies-literature

Porous Hybrids Structure between Silver Nanoparticle and Layered Double Hydroxide for Surface-Enhanced Raman Spectroscopy.

Project description:Silver nanoparticle (AgNP), in terms of antibacterial, catalytic, electronic, and optical applications, is an attractive material. Especially, when prepared to furnish sharp edge and systematic particle orientation on the substrate, AgNPs can take advantage of surface-enhanced Raman spectroscopy (SERS). In this research, we suggested a synthetic method to immobilize the AgNP on metal oxide by utilizing Ag-thiolate and layered double hydroxide (LDH) as precursor and template, respectively. The layer-by-layer structure of LDH and Ag-thiolate transformed through reductive calcination to metal oxide and AgNP array. Physicochemical characterization, including powder X-ray diffraction, N2 adsorption-desorption, microscopies, and X-ray photoelectron spectroscopy, revealed that the AgNP with sufficient crystallinity and particle gap was obtained at relatively high calcination temperature, ~600 °C. UV-vis diffusion reflectance spectroscopy showed that the calcination temperature affected particle size and electronic structure of AgNP. The prepared materials were subjected to SERS tests toward 4-nitrothiophenol (4-NTP). The sample obtained at 600 °C exhibited 50 times higher substrate enhancement factor (SEF) than the one obtained at 400 °C, suggesting that the calcination temperature was a determining parameter to enhance SERS activity in current synthetic condition.

| S-EPMC7916476 | biostudies-literature

Development of Mesopore Structure of Mixed Metal Oxide through Albumin-Templated Coprecipitation and Reconstruction of Layered Double Hydroxide.

Project description:Mixed metal oxide (MMO) with relatively homogeneous mesopores was successfully obtained by calcination and reconstruction of albumin-templated layered double hydroxide (LDH). The aggregation degree of albumin-template was controlled by adjusting two different synthesis routes, coprecipitation and reconstruction. X-ray diffraction patterns and scanning electron microscopic images indicated that crystal growth of LDH was fairly limited during albumin-templated coprecipitation due to the aggregation. On the hand, crystal growth along the lateral direction was facilitated in albumin-templated reconstruction due to the homogeneous distribution of proteins moiety. Different state of albumin during LDH synthesis influenced the local disorder and porous structure of calcination product, MMO. The N2 adsorption-desorption isotherms demonstrated that calcination on reconstructed LDH produced MMO with large specific surface area and narrow distribution of mesopores compared with calcination of coprecipitated LDH.

| S-EPMC7999424 | biostudies-literature

Growth of NiAl-Layered Double Hydroxide on Graphene toward Excellent Anticorrosive Microwave Absorption Application.

Project description:High-performance microwave absorbers with special features are desired to meet the requirements of more complex modern service environments, especially corrosive environments. Therefore, high-efficiency microwave absorbers with corrosion resistance should be developed urgently. Herein, a 3D NiAl-layered double hydroxide/graphene (NiAl-LDH/G) composite synthesized by atomic-layer-deposition-assisted in situ growth is presented as an anticorrosive microwave absorber. The content of NiAl-LDH in the composite is optimized to achieve impedance matching. Furthermore, under the cooperative effects of the interface polarization loss, conduction loss, and 3D porous sandwich-like structure, the optimal NiAl-LDH/G shows excellent microwave absorption performance with a minimum reflection loss of -41.5 dB and a maximum effective absorption bandwidth of 4.4 GHz at a loading of only 7 wt% in epoxy. Remarkably, the encapsulation effect of NiAl-LDH can restrain the galvanic corrosion owing to graphene. The epoxy coating with the NiAl-LDH/G microwave absorber on carbon steel exhibits long-term corrosion resistance, owing to the synergetic effect of the superior impermeability of graphene and the chloridion-capture capacity of the NiAl-LDH. The NiAl-LDH/G composite is a promising anticorrosive microwave absorber, and the findings of this study may motivate the development of functional microwave absorbers that meet the demands of anticorrosive performance of coatings.

| S-EPMC7927622 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data