Chloride Diffusion in Concrete Protected with a Silane-Based Corrosion Inhibitor.

ABSTRACT: One of the most important parameters concerning durability is undoubtedly represented by cement matrix resistance to chloride diffusion in environments where reinforced concrete structures are exposed to the corrosion risk induced by marine environment or de-icing salts. This paper deals with protection from chloride ingress by a silane-based surface-applied corrosion inhibitor. Results indicated that the corrosion inhibitor (CI) allows to reduce the penetration of chloride significantly compared to untreated specimens, independently of w/c, cement type, and dosage. Reduction of chloride diffusion coefficient (Dnssn) measured by an accelerated test in treated concrete was in the range 30-60%. Natural chloride diffusion test values indicate a sharp decrease in apparent diffusion coefficient (Dapp) equal to about 75% when concrete is protected by CI. Mechanism of action of CI in slowing down the chloride penetration inside the cement matrix is basically due to the water repellent effect as confirmed by data of concrete bulk electrical resistivity.

SUBMITTER: Coppola L

PROVIDER: S-EPMC7216148 | biostudies-literature | 2020 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Chloride Diffusion in Concrete Protected with a Silane-Based Corrosion Inhibitor.

Coppola Luigi L Coffetti Denny D Crotti Elena E Gazzaniga Gabriele G Pastore Tommaso T

Materials (Basel, Switzerland) 20200424 8

One of the most important parameters concerning durability is undoubtedly represented by cement matrix resistance to chloride diffusion in environments where reinforced concrete structures are exposed to the corrosion risk induced by marine environment or de-icing salts. This paper deals with protection from chloride ingress by a silane-based surface-applied corrosion inhibitor. Results indicated that the corrosion inhibitor (CI) allows to reduce the penetration of chloride significantly compare ...[more]

PMID: 32344730

Similar Datasets

Project description:Corrosion-induced damage to concrete reinforced with bars is a serious problem regarding technical and economic aspects and strongly depends on used materials, corrosion environment, and service life. Tests described in this paper refer to a two-year evaluation of the effectiveness of protection provided by zinc-coated low-carbon reinforcing steel of grade B500SP in concrete against chloride corrosion. Performed tests were comparative and included measurements conducted on four groups of concrete test elements with dimensions of 40 mm × 40 mm × 140 mm reinforced with a bar having a diameter of ?8 mm. Particular groups were a combination of different types of concrete with or without chloride additives, with galvanized or black steel. Chlorides as CaCl2 were added to the concrete mix in the amount of 3% of cement weight in concrete. Reinforced concrete specimens were periodically monitored within two years using the following techniques: linear polarization resistance (LPR) and electrochemical impedance spectroscopy (EIS). Polarization measurements were conducted in a three-electrode arrangement, in which a rebar in concrete served as a working electrode, stainless steel sheet was used as an auxiliary electrode, and Cl-/AgCl,Ag was a reference electrode. Comparative tests of changes in the density of corrosion current in concrete specimens without chloride additives basically demonstrated no development of corrosion, and possible passivation was expected in case of black steel. Higher densities of corrosion current were observed for galvanized steel during first days of testing. The reason was the dissolution of zinc after the contact with initially high pH of concrete pore solution. Six-month measurements demonstrated a higher density of corrosion current in concrete specimens with high concentration of chlorides, which unambiguously indicated corrosion in concrete reinforced with galvanized or black steel. Densities of corrosion current determined for selected specimens dramatically decreased after an 18-month interval in measurements. Corrosion was even inhibited on black steel as an insulating barrier of corrosion products was formed. The above observations were confirmed with structural studies using scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) techniques. Results obtained from corrosion (LPR, EIS) and structural (SEM, EDS) tests on specimens of concrete reinforced with steel B500SP demonstrated a very favorable impact of zinc coating on steel by providing two-year protection against corrosion in the environment with very high chloride content.

Dataset Information

Chloride Diffusion in Concrete Protected with a Silane-Based Corrosion Inhibitor.

Publications

Chloride Diffusion in Concrete Protected with a Silane-Based Corrosion Inhibitor.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets