Fracture Resistance of Zirconia-Reinforced Lithium Silicate Ceramic Crowns Cemented with Conventional or Adhesive Systems: An In Vitro Study.

ABSTRACT: In recent years, Zirconia-reinforced Lithium Silicate ceramic (ZLS), combining lithium-silicate and zirconia features, has shown to have excellent mechanical and aesthetic characteristics. Thus, the aim of this study was to compare the fracture strength of ZLS single crowns cemented with two different cementation techniques. Twenty crowns were realised and cemented on teeth replicas achieved from an extracted premolar human tooth. The samples were divided into two groups of 10 specimens each, Glass-ionomeric cement (GIC) group and Self-Adhesive Resin Cement (ARC) group. The mechanical test was performed using a universal testing machine. The specimens were then evaluated with a scanning electron microscope (SEM) to identify for all crowns and related abutments the pattern of fracture after the breaking point. The data obtained were statistically analysed. The mean fracture toughness values and standard deviations (±SD) were 2227 ± 382 N and 3712 ± 319 N respectively for GIC and ARC groups. In fact, t-test showed a statistically significant difference between the two groups (p < 0.001). Moreover, the SEM results demonstrated portions of abutments still attached to the crown fragments in the ARC group, whilst these were not present in the GIC group. Within the limitations of this study, these results suggest the use of adhesive cementation for ZLS crowns, which significantly increase the compressive strength of ZLS restorations compared to GIC.

SUBMITTER: D'Addazio G

PROVIDER: S-EPMC7254201 | biostudies-literature | 2020 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Fracture Resistance of Zirconia-Reinforced Lithium Silicate Ceramic Crowns Cemented with Conventional or Adhesive Systems: An In Vitro Study.

D'Addazio Gianmaria G Santilli Manlio M Rollo Marco Lorenzo ML Cardelli Paolo P Rexhepi Imena I Murmura Giovanna G Al-Haj Husain Nadin N Sinjari Bruna B Traini Tonino T Özcan Mutlu M Caputi Sergio S

Materials (Basel, Switzerland) 20200425 9

In recent years, Zirconia-reinforced Lithium Silicate ceramic (ZLS), combining lithium-silicate and zirconia features, has shown to have excellent mechanical and aesthetic characteristics. Thus, the aim of this study was to compare the fracture strength of ZLS single crowns cemented with two different cementation techniques. Twenty crowns were realised and cemented on teeth replicas achieved from an extracted premolar human tooth. The samples were divided into two groups of 10 specimens each, Gl ...[more]

PMID: 32344894

Similar Datasets

Project description:BACKGROUND:Clinical studies regarding zirconia implant abutments reported good survival rates in the short-term observation period. The purpose of this study was to assess the six-year clinical performance of zirconia abutments supporting all-ceramic crowns in anterior and premolar regions. METHODS:The patients received zirconia implant abutments to support all-ceramic crowns in Chang-Gung Medical Center during the period August 2010 to August 2011 were enrolled. In the following six years of observation period after the implant-crown had finished, the clinical parameters of all of the included patients were registered on a special form. The records regarding the following variables: age, gender, implant location, the condition of edentulous site before implant placement, esthetic performance at baseline, presence or absence of technical complications, and biological outcomes were registered and scrutinized for evaluation. RESULTS:Out of the 32 zirconia implant abutments and 32 all-ceramic crowns that were followed for six years. Neither abutments nor crowns were lost, yielding 100% survival rates for both zirconia abutments and crowns. The esthetic outcomes were excellent except that a score of 2 was given to two restorations. With regard to technical complications, there was one instance of abutment screw loosening, two cases of veneering ceramic chipping, one restoration with occlusal roughness, and three instances of crowns loosening. Overall, the success rates were 96.8% and 81.2% for abutments and crowns respectively. In biological performance, only 1 implant was classified in group II (satisfactory survival) in the Misch classification, while all the others were classified in group I (excellent). CONCLUSIONS:Zirconia abutments supporting all-ceramic crowns demonstrated high survival rate, good biological and esthetic results. While some technical complications were frequently observed, the complication-free rates were 96.8% for abutments and 81.2% for crowns in the medium-term observation period.

Project description:BACKGROUND:When implants are restored with cement-retained restorations, prosthetic retrievability can be difficult and often requires sectioning using rotary instruments. Sometimes repeated removals of a cement-retained implant crown are needed such as for treatment of peri-implantitis or immediate implant provisionalization. The purpose of this study was to evaluate the effect of erbium-doped yttrium aluminum garnet (Er:YAG) laser as a non-invasive treatment modality to remove lithium disilicate crowns from zirconia implant abutments following long-term cementation, repetitive debonding and re-cementation, and short-term retrieval. MATERIAL AND METHODS:Twenty identical lithium disilicate crowns were cemented onto zirconia prefabricated abutments using composite resin cement. Ten cemented crowns were removed at 48 hours after cementation as a short-term group (ST), while another 10 were removed 6 months after cementation as a long-term group (LT). To mimicking repetitive recementation and retrieval, the LT crowns were then recemented and removed after 48 hours as a long-term recemention (LTR) group. The LTR crowns were then again recemented and removed after 48 hours as a long-term repeated recemention (LTRR) group. Er:YAG laser was used to facilitate the retrieval of these crowns. recorded and analyzed using ANOVA and t-test. The surfaces of the crown and the abutment were further examined using light microscopy and scanning electron microscopy (SEM). Temperature changes of the abutment and crown upto 10 minutes were also measured and statistically analyzed (paired t-test). RESULTS:The average times of crown removal from zirconia abutments were 4 minutes (min) and 42 second (sec) in LT to 3 min 24 sec in LTR, and 3 min 12 sec in LTRR and ST groups. LTR took the longest time to remove, statistically (ANOVA and t-test, p < .001). No statistical differences were observed among the removal times of LTR, LTRR, and ST groups (t-test, p = .246, .246 and 1). SEM examination of the material surface showed no visual surface damaging from treatment with Er:YAG laser. The temperatures during irradiation ranged from 18.4°C to 20°C and 22.2°C to 24.5°C (Paired t-test, p < .0001) for the abutment and the crown during irradiation from 1 min to 10 mins. CONCLUSIONS:Long-term cementation can increase time in lithium disilicate crown removal from zirconia abutment using Er:YAG. Er:YAG laser is a non-invasive tool to remove cement-retained implant prostheses and should be considered as a viable alternative to rotary instruments.

Dataset Information

Fracture Resistance of Zirconia-Reinforced Lithium Silicate Ceramic Crowns Cemented with Conventional or Adhesive Systems: An In Vitro Study.

Publications

Fracture Resistance of Zirconia-Reinforced Lithium Silicate Ceramic Crowns Cemented with Conventional or Adhesive Systems: An In Vitro Study.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets