Direct Visualization of Crystalline Domains in Carboxylated Nanocellulose Fibers.

ABSTRACT: Direct visualization of soft organic molecules like cellulose is extremely challenging under a high-energy electron beam. Herein, we adopt two ionization damage extenuation strategies to visualize the lattice arrangements of the β-(1→4)-d-glucan chains in carboxylated nanocellulose fibers (C-NCFs) having cellulose II crystalline phase using high-resolution transmission electron microscopy. Direct imaging of individual nanocellulose fibrils with high-resolution and least damage under high-energy electron beam is achieved by employing reduced graphene oxide, a conducting material with high electron transmittance and Ag⁺ ions, with high electron density, eliminating the use of sample-specific, toxic staining agents, or other advanced add-on techniques. Furthermore, the imaging of cellulose lattices in a C-NCF/TiO₂ nanohybrid system is accomplished in the presence of Ag⁺ ions in a medium revealing the mode of association of C-NCFs in the system, which validates the feasibility of the presented strategy. The methods adopted here can provide further understanding of the fine structures of carboxylated nanocellulose fibrils for studying their structure-property relationship for various applications.

SUBMITTER: Nabeela K

PROVIDER: S-EPMC7271348 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Nanocellulose, as a biobased versatile nanomaterial that can be derived with tailorable surface functionalities, dimensions, and morphologies, has considerable implications for modifying the rheology, mechanical reinforcement, and influencing the carbonization efficiency in the production of polyacrylonitrile (PAN)-based carbon fibers. Herein, we report the influence of three different nanocellulose types, varying in the derivatization method, source, and aspect ratio, on the mechanical properties and thermal transformations of solution-spun PAN/nanocellulose nanocomposite fibers into carbon fibers. The incorporation of 0.1 wt % nanocellulose into solution-spun PAN fibers led to a 7-19% increase in tensile modulus and 0-27% increase in tensile strength in the solution-spun fibers, compared to a control PAN fiber. These improvements varied depending on the nanocellulose type. After low-temperature carbonization at 1200 °C, improvements in the mechanical properties of the nanocellulose-reinforced carbon fibers, compared with a PAN fiber, were also observed. In contrast to the precursor fibers, the improvement % in the carbonized fibers was found to be dependent on the nanocellulose morphology and was linearly correlated with increasing aspect ratio of nanocellulose. For example, in carbon fibers with a cotton-derived low-aspect-ratio cellulose nanocrystal and spinifex-derived high-aspect-ratio CNC and nanofiber, up to 4, 87, and 172% improvements in tensile moduli were observed, respectively. Due to the processing methods used, the nanocellulose aspect ratio and crystallinity are inversely related, and as such, the increase in the carbon fiber mechanical properties was also related to a decrease in crystallinity of the nanocellulose reinforcers. Raman spectra and electron microscopy analysis suggest that mechanical improvement after carbonization is due to internal reinforcement by highly ordered regions surrounding the carbonized nanocellulose, within the turbostratic carbon fibers.

Dataset Information

Direct Visualization of Crystalline Domains in Carboxylated Nanocellulose Fibers.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets