Early failure of a modern moderately cross-linked polyethylene acetabular liner.

ABSTRACT: Modern polyethylene components for total hip arthroplasty have shown excellent long-term wear properties. However, among 204 primary total hip arthroplasty procedures performed by one surgeon using the Exactech Connexion GXL Liner, we identified 5 cases of severe polyethylene wear and osteolysis which occurred within 5 years of the index surgery. Among the 5 cases, all patients had a size 36 head with an acetabular component from size 52 to 56 mm. All patients had a UCLA activity scale score of at least 6 at the time that the osteolysis was detected. The average wear rate was 0.265 mm ± 0.207 mm per year. This review of 5 cases of catastrophic early polyethylene wear demonstrates a concerning trend with the use of the Exactech Connexion GXL liner. Further investigation is warranted to evaluate material characteristics which may have caused this accelerated wear and to prevent recurrences of this complication in the future.

SUBMITTER: Kahlenberg CA

PROVIDER: S-EPMC7303480 | biostudies-literature | 2020 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Early failure of a modern moderately cross-linked polyethylene acetabular liner.

Kahlenberg Cynthia A CA Menken Luke L Ranawat Amar S AS Rodriguez Jose A JA

Arthroplasty today 20200307 2

Modern polyethylene components for total hip arthroplasty have shown excellent long-term wear properties. However, among 204 primary total hip arthroplasty procedures performed by one surgeon using the Exactech Connexion GXL Liner, we identified 5 cases of severe polyethylene wear and osteolysis which occurred within 5 years of the index surgery. Among the 5 cases, all patients had a size 36 head with an acetabular component from size 52 to 56 mm. All patients had a UCLA activity scale score of ...[more]

PMID: 32577467

Similar Datasets

Polyethylene liner dissociation with the Pinnacle acetabular component: should we be concerned?

Project description:Between 2007 and 2018, 535 total hip arthroplasties using the uncemented Pinnacle acetabular component (DePuy Synthes, Warsaw, IN) and polyethylene liner were implanted in our unit. Of these, 6 patients presented acutely with liner polyethylene dissociation, giving a rate of liner dissociation of 1.11%. All dissociations were atraumatic. Failure occurred at mean 37 months (range 4.5 to 130 months). Radiologically, all acetabular components were within safe zone of abduction and mean anteversion was 10 degrees (range 2-20). In one case, there was posterior impingement against the femoral neck due to femoral malalignment. All patients underwent head and liner exchange with no repeat failures. Despite excellent long-term results, the frequency of dissociated polyethylene liners is a cause of concern with the Pinnacle acetabular component.

| S-EPMC7083726 | biostudies-literature

Superior rim fracture of a vitamin E-infused highly cross-linked polyethylene (HXLPE) liner leading to total hip arthroplasty revision.

Project description:This case report looks at the failure of a vitamin E-infused highly cross-linked polyethylene acetabular liner that fractured at the superior rim of the locking mechanism. This calls to question whether there is a problem with the vitamin E-infused product or a flaw in the design of the liner or possibly a combination of the 2. Although there has been discussion of a possible minimum rim polyethylene thickness, there has not been a minimum thickness established. In addition, in the case of offset liners, indentations which are a part of a locking mechanism can cause the minimum rim dimension to be much less than the specified nominal thickness. This case serves as an interesting observation and contributes to the discussion of rim liner polyethylene thickness and minimum rim thickness.

| S-EPMC6123179 | biostudies-literature

Acetabular Liner Dissociation: A Comparative Study of Two Contemporary Uncemented Acetabular Components.

Project description:Background:There are a number of reports of polyethylene liner dissociation of third-generation modular acetabular components. This study compares our experience with 2 contemporary systems to determine whether this is an implant- or class-specific problem. Methods:This is a single-center retrospective study of 961 primary total hip arthroplasties using 2 third-generation modular cementless acetabular shells: Pinnacle (535) and R3 (426) with a polyethylene liner. Details of all revisions were obtained from local databases and the New Zealand Joint Registry. Kaplan-Meier survival curves were calculated for all-cause revision, acetabular reoperation (including liner exchange), and liner dissociation. Results:There were 17 revisions in group 1 (Pinnacle; DePuy Synthes): 17 for recurrent dislocation, 6 for liner dissociations (1.12%), 3 for femoral loosening, and one for deep infection. In group 2 (R3; Smith and Nephew), there were 4 revision procedures: one for infection, 2 for dislocation, and one femoral revision for periprosthetic fracture. There were significantly higher proportions revised in group 1 for all-cause revision, acetabular reoperation, and dissociation (P = .024 to 0.038). The 7-year survival for all-cause revision was 96.1% for Pinnacle and 99.0% for R3 (P = .022), and that in the acetabular reoperation group was 96.9% for Pinnacle and 99.3% for R3 (P = .035). Conclusions:There was a higher revision rate for the Pinnacle acetabular component than for the R3 at 7 years. This was mainly due to polyethylene liner dissociation that can occur early or late. It appears to be a problem specific to the Pinnacle cup design rather than a feature of similar third-generation acetabular components.

| S-EPMC7298534 | biostudies-literature

Precision of radiostereometric analysis (RSA) of acetabular cup stability and polyethylene wear improved by adding tantalum beads to the liner.

Project description:Background and purposeIn traditional radiostereometric analysis (RSA), 1 segment defines both the acetabular shell and the polyethylene liner. However, inserting beads into the polyethylene liner permits employment of the shell and liner as 2 separate segments, enabling distinct analysis of the precision of 3 measurement methods in determining femoral head penetration and shell migration.Patients and methodsThe UmRSA program was used to analyze the double examinations of 51 hips to determine if there was a difference in using the shell-only segment, the liner-only segment, or the shell + liner segment to measure wear and acetabular cup stability. The standard deviation multiplied by the critical value (from a t distribution) established the precision of each method.ResultsDue to the imprecision of the automated edge detection, the shell-only method was least desirable. The shell + liner and liner-only methods had a precision of 0.115 mm and 0.086 mm, respectively, when measuring head penetration. For shell migration, the shell + liner had a precision of 0.108 mm, which was better than the precision of the shell-only method. In both the penetration and migration analyses, the shell + liner condition number was statistically significantly lower and the bead count was significantly higher than for the other methods.InterpretationInsertion of beads in the polyethylene improves the precision of femoral head penetration and shell migration measurements. A greater dispersion and number of beads when combining the liner with the shell generated more reliable results in both analyses, by engaging a larger portion of the radiograph.

| S-EPMC4564778 | biostudies-literature

Long-term results of uncemented acetabular cups with an ACS polyethylene liner. a 14-16-year follow-up study.

Project description:We assessed the clinical and radiographic results of 40 porous-coated acetabular cups with an Acetabular Cup System polyethylene liner over a minimum 14-year follow-up. Femoral head penetration was estimated using a software package. Fifteen cups were revised, 11 due to polyethylene liner rupture. All cups but two were radiographically stable, and 11 hips showed acetabular osteolysis. The overall femoral head penetration rate in hips without liner fracture with reference to the early penetration point was 0.1188+/-0.070 mm per year. Polyethylene liner fractures were associated with higher early femoral head penetration (P<0.0001) and a vertical cup position (P=0.0016). The 14-year survival without cup revision for any reason was 63.9%, 71.8% with no ACS polyethylene liner fracture and 65.3% with no acetabular osteolysis. Most cups showed a good clinical outcome in general, but major Acetabular Cup System liner failure and osteolysis were frequent. Patients with the ACS cups still in place should be monitored closely.

| S-EPMC2267555 | biostudies-other

Pinnacle polyethylene liner dissociation: a report of 3 cases.

Project description:We describe 3 cases of DePuy Pinnacle polyethylene dissociations, their presentations, and treatment. A 34-year-old female with arthritis secondary to dysplasia, a 51-year-old male with avascular necrosis of the femoral head, and a 57-year-old female with osteoarthritis were treated with total hip arthroplasty. Acute nontraumatic polyethylene liner dissociations occurred at 31, 42, and 2 months postoperatively. They were treated with component retention and modular femoral head and liner revision. The 51-year-old male subsequently developed a prosthetic joint infection requiring explant of his components. Although dissociation of polyethylene liners from the DePuy Pinnacle acetabular components is an uncommon complication, this problem may increase in prevalence with longer term follow-up, and vigilance is recommended.

| S-EPMC6287959 | biostudies-literature

2-year results of an RCT of 2 uncemented isoelastic monoblock acetabular components: lower wear rate with vitamin E blended highly cross-linked polyethylene compared to ultra-high molecular weight polyethylene.

Project description:Background and purpose - The long-term survival of arthroplasty components may be limited by polyethylene wear-related problems such as periprosthetic osteolysis and aseptic loosening. Highly cross-linked polyethylene (HXLPE) blended with vitamin E was introduced to improve oxidative stability and to avoid long-term embrittlement. This study clinically compares the tribological behavior and clinical outcome of vitamin E blended HXLPE with ultra-high molecular weight polyethylene (UHMWPE) in an isoelastic monoblock cup for uncemented total hip arthroplasty.Patients and methods - In this randomized controlled trial (RCT), 199 patients were included: 102 patients received the vitamin E blended HXLPE cup, 97 patients the UHMWPE cup. Clinical and radiographic parameters were obtained preoperatively, directly postoperative and at 3, 12, and 24 months. Wear rates were compared using the mean linear femoral head penetration (FHP) rate.Results - 188 patients (94%) completed the 2-year follow-up. Mean patient satisfaction was higher in the vitamin E blended HXLPE group (8.9 [1]) than in in the control group (8.5 [2], p = 0.03). The Harris Hip Score (HHS) was higher in the vitamin E blended HXLPE group (95 [8]) than in the control group (92 [11], p = 0.3). The FHP rate was lower in the vitamin E blended HXLPE group: 0.046 mm/year compared with 0.056 mm/year in the control group (p = 0.05). No adverse reactions associated with the clinical application of vitamin E blended HXLPE were observed during follow-up, with an excellent 2-year survival to revision rate of 98% for both cups.Interpretation - This study shows the superior performance of the HXLPE blended with vitamin E acetabular cup with lower linear femoral head penetration rates and better clinical results compared with the UHMWPE acetabular cup after 2 years.

| S-EPMC8023900 | biostudies-literature

Study of the Failure Mechanism of a High-Density Polyethylene Liner in a Type IV High-Pressure Storage Tank.

Project description:The use of Type IV cylinders for gas storage is becoming more widespread in various sectors, especially in transportation, owing to the lightweight nature of this type of cylinder, which is composed of a polymeric liner that exerts a barrier effect and an outer composite material shell that primarily imparts mechanical strength. In this work, the failure analysis of an HDPE liner in a Type IV cylinder for high-pressure storage was carried out. The breakdown occurred during a cyclic pressure test at room temperature and manifested in the hemispherical head area, as cracks perpendicular to the liner pinch-off line. The failed sample was thoroughly investigated and its characteristics were compared with those of other liners at different stages of production of a Type IV cylinder (blow molding, curing of the composite material). An examination of the liner showed that no significant chemical and morphological changes occurred during the production cycle of a Type IV cylinder that could justify the liner rupture, and that the most likely cause of failure was a design-related fatigue phenomenon.

| S-EPMC10975935 | biostudies-literature

A vitamin E blended highly cross-linked polyethylene acetabular cup results in less wear: 6-year results of a randomized controlled trial in 199 patients.

Project description:Background and purpose - Survivorship of total hip arthroplasty (THA) with the ultra-high molecular weight polyethylene (UHMWPE) monoblock cup has been limited due to periprosthetic osteolysis and aseptic loosening, secondary to wear of the UHMWPE. In response, a vitamin E blended highly cross-linked polyethylene (HXLPE) cup was developed. This study set out to compare the wear and clinical 6-year outcomes of vitamin E blended HXLPE with UHMWPE in an isoelastic monoblock cup in patients with hip osteoarthritis who underwent uncemented THA. The 2-year results have been reported previously. Patients and methods - For this randomized controlled trial 199 patients were included. 102 patients received the vitamin E blended HXLPE uncemented acetabular cup and 97 patients the uncemented UHMWPE monoblock cup. Clinical and radiographic parameters were obtained preoperatively, directly postoperatively, and at 3, 12, 24, and 72 months. Wear rates were compared using the femoral head penetration (FHP) rate. Results - 173 patients (87%) completed the 6-year follow-up. The mean NRS scores for rest pain, load pain, and patient satisfaction were 0.3 (SD 1), 0.6 (SD 1), and 8.6 (SD 1) respectively. The mean Harris Hip Score was 93 (SD 12). The FHP rate was lower in the vitamin E blended HXLPE cup (0.028 mm/year) compared with the UHMWPE cup (0.035 mm/year) (p = 0.002). No adverse reactions associated with the clinical application of vitamin E blended HXLPE were observed. 15 complications occurred, equally distributed between the two cups. The 6-year survival to revision rate was 98% for both cups. There was no aseptic loosening. Interpretation - This study shows the superior performance of the HXLPE blended with vitamin E acetabular cup with clinical and radiographic results similar to the UHMWPE acetabular cup.

| S-EPMC8023918 | biostudies-literature

Acetabular polyethylene wear and acetabular inclination and femoral offset.

Project description:UNLABELLED: Restoration of femoral offset and acetabular inclination may have an effect on polyethylene (PE) wear in THA. We therefore assessed the effect of femoral offset and acetabular inclination (angle) on acetabular conventional (not highly cross-linked) PE wear in uncemented THA. We prospectively followed 43 uncemented THAs for a minimum of 49 months (mean, 64 months; range, 49-88 months). Radiographs were assessed for femoral offset, acetabular inclination, and conventional PE wear. The mean (+/- standard deviation) linear wear rate in all THAs was 0.14 mm/year (+/- 0.01 mm/year) and the mean volumetric wear rate was 53.1 mm(3)/year (+/- 5.5 mm(3)/year). In THAs with an acetabular angle less than 45 degrees , the mean wear was 0.12 mm/year (+/- 0.01 mm/year) compared with 0.18 mm/year (+/- 0.02 mm/year) in those with a reconstructed acetabular angle greater than 45 degrees . Reproduction of a reconstructed femoral offset to within 5 mm of the native femoral offset was associated with a reduction in conventional PE wear (0.12 mm/year versus 0.16 mm/year). Careful placement of the acetabular component to ensure an acetabular angle less than 45 degrees in the reconstructed hip allows for reduced conventional PE wear. LEVEL OF EVIDENCE: Level II, prospective study. See Guidelines for Authors for a complete description of levels of evidence.

| S-EPMC2758973 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data