Molecular Structure, Chemical Exchange, and Conductivity Mechanism of High Concentration LiTFSI Electrolytes.

ABSTRACT: High concentration lithium electrolytes have been found to be good candidates for high energy density and high voltage lithium batteries. Recent studies have shown that limiting the free solvent molecules in the electrolytes prevents the degradation of the battery electrodes. However, the molecular level knowledge of the structure and dynamics of such an electrolyte system is limited, especially for electrolytes based on typical organic carbonates. In this article, the interactions and motions involved in lithium bis(trifluoromethanesulfonyl)imide in carbonyl-containing solvents are investigated using linear and time-resolved vibrational spectroscopies and computational methods. Our results suggest that the overall structure and the speciation of the three high concentration electrolytes are similar. However, the cyclic carbonate-based electrolyte presents an additional interaction as a result of dimer formation. Time-resolved studies reveal similar and fast dynamics for the structural motions of solvent molecules in electrolytes composed of linear molecules, while the electrolyte made of cyclic solvent molecules shows slower structural changes as a result of the dimer formation. Additionally, a picosecond time scale process is observed and assigned to the coordination and decoordination of solvent molecules from a lithium-ion solvation shell. This process of solvent exchange is found to be directly correlated to the making and breaking of structures between the lithium-ion and the anion and, consequently, to the conduction mechanism. Overall, our data show that the molecular structure of the solvent does not significantly affect the speciation and distribution of the lithium-ion solvation shells. However, the presence of dimerization between solvent molecules of two neighboring lithium-ions appears to produce a microscopic ordering that it is manifested macroscopically in properties of the electrolyte, such as its viscosity.

SUBMITTER: Galle Kankanamge SR

PROVIDER: S-EPMC7307920 | biostudies-literature | 2020 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Molecular Structure, Chemical Exchange, and Conductivity Mechanism of High Concentration LiTFSI Electrolytes.

Galle Kankanamge Susith R SR Kuroda Daniel G DG

The journal of physical chemistry. B 20200227 10

High concentration lithium electrolytes have been found to be good candidates for high energy density and high voltage lithium batteries. Recent studies have shown that limiting the free solvent molecules in the electrolytes prevents the degradation of the battery electrodes. However, the molecular level knowledge of the structure and dynamics of such an electrolyte system is limited, especially for electrolytes based on typical organic carbonates. In this article, the interactions and motions i ...[more]

PMID: 32069048

Similar Datasets

Project description:Composite polymer electrolytes (CPEs) strike an effective balance between ionic conductivity and mechanical flexibility for lithium-ion solid-state batteries. Long-term performance, however, is limited by capacity fading after hundreds of charge and discharge cycles. The causes of performance degradation include multiple contributing factors such as dendrite formation, physicochemical changes in electrolytes, and structural remodeling of porous electrodes. Among the many factors that contribute to performance degradation, the effect of stress specifically on the composite electrolyte is not well understood. This study examines the mechanical changes in a poly(ethylene oxide) electrolyte with bis(trifluoromethane) sulfonimide. Two different sizes of Li6.4La3Zr1.4Ta0.6O12 particles (500 nm and 5 μm) are compared to evaluate the effect of the surface-to-volume ratio of the ion-conducting fillers within the composite. Cyclic compression was applied to mimic stress cycling in the electrolyte, which would be caused by asymmetric volume changes that occur during charging and discharging cycles. The electrolytes exhibited fatigue softening, whereby the compressive modulus gradually decreased with an increase in the number of cycles. When the electrolyte was tested for 500 cycles at 30% compressive strain, the compressive modulus of the electrolyte was reduced to approximately 80% of the modulus before cycling. While the extent of softening was similar regardless of particle size, CPEs with 500 nm particles exhibited a significant reduction in ionic conductivity after cyclic compression (1.4 × 10-7 ± 2.3 × 10-8 vs 1.1 × 10-7 ± 2.0 × 10-8 S/cm, mean ± standard deviation, n = 4), whereas there was no significant change in ionic conductivity for CPEs with 5 μm particles. These observations -performed deliberately in the absence of charge-discharge cycles -show that repetitive mechanical stresses can play a significant role in altering the performance of CPEs, thereby revealing another possible mechanism for performance degradation in all-solid-state batteries.

Dataset Information

Molecular Structure, Chemical Exchange, and Conductivity Mechanism of High Concentration LiTFSI Electrolytes.

Publications

Molecular Structure, Chemical Exchange, and Conductivity Mechanism of High Concentration LiTFSI Electrolytes.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets