Adhesion of streptococci to titanium and zirconia.

ABSTRACT: The purpose of this study was to evaluate the adherence of streptococci to disks of titanium (commercially pure titanium: CpTi) and zirconia (tetragonal zirconia polycrystals: TZP). CpTi and yttria-stabilized TZP disks with a mirror-polished surface were used as specimens. The arithmetic mean surface roughness (Ra and Sa) and the surface wettability of the experimental specimens were measured. For analyzing the outermost layer of the experimental specimens, X-ray photoelectron spectroscopy (XPS) analysis was performed. Streptococcus sanguinis, S. gordonii, S. oralis, and S. mutans were used as streptococcal bacterial strains. These bacterial cultures were grown for 24 h on CpTi and TZP. The number of bacterial adhesions was estimated using an ATP-bioluminescent assay, and scanning electron microscope (SEM) observation of the adhered bacterial specimens was performed. No significant differences in surface roughness or wettability were found between CpTi and TZP. In XPS analyses, outermost layer of CpTi included Ti0 and Ti4+, and outermost layer of TZP included Zr4+. In the cell adhesion assay, the adherences of S. sanguinis, S. gordonii, and S. oralis to TZP were significantly lower than those to CpTi (p < 0.05); however, significant difference was not observed for S. mutans among the specimens. The adherence to CpTi and TZP of S. mutans was significantly lower than that of S. sanguinis, S. gordonii, and S. oralis. These results were confirmed by SEM. S. sanguinis, S. gordonii, and S. oralis adhered less to TZP than to CpTi, but the adherence of S. mutans was similar to both surfaces. S. mutans was less adherent compare with the other streptococci tested in those specimens.

SUBMITTER: Oda Y

PROVIDER: S-EPMC7314031 | biostudies-literature | 2020

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Adhesion of streptococci to titanium and zirconia.

Oda Yukari Y Miura Tadashi T Mori Gentaro G Sasaki Hodaka H Ito Taichi T Yoshinari Masao M Yajima Yasutomo Y

PloS one 20200624 6

The purpose of this study was to evaluate the adherence of streptococci to disks of titanium (commercially pure titanium: CpTi) and zirconia (tetragonal zirconia polycrystals: TZP). CpTi and yttria-stabilized TZP disks with a mirror-polished surface were used as specimens. The arithmetic mean surface roughness (Ra and Sa) and the surface wettability of the experimental specimens were measured. For analyzing the outermost layer of the experimental specimens, X-ray photoelectron spectroscopy (XPS) ...[more]

PMID: 32579584

Similar Datasets

Project description:Statement of problemTo separate the crown from the titanium base abutment, by using heat, caused oxidization of the titanium base abutment. The effect of this procedure on the retention of a crown is unclear.PurposeTo compare the resin bond strength and failure type between zirconia crowns and titanium base abutments utilizing four different surface treatments. Surface roughness and morphology of each surface treatment were also investigated.Material and methodsForty titanium base abutments (Variobase®) were divided into four groups, 1. Control, 2. Air abraded, 3. Oxidized, and 4. Oxidized-air abraded. Oxidized and oxidized-air abraded groups were debonded from zirconia crowns using constant dry heat at 500 ˚C. For air abraded and oxidized-air abraded groups (after oxidization), the titanium base abutments were air abraded with Al3O2. After cleaning, one specimen of each group was investigated under a non-contact profilometer (50x), then the same samples were investigated under SEM at 25,300,500,1000 magnification and EDS at 30kV of accelerated voltage. All specimens were then cemented (RelyX Ultimate). After aging, with thermocycling under 5C° to 55C°,120 seconds dwell time for 5,000 cycles, bond strength was tested and statistical differences were calculated with One-way ANOVA (p-value <0.05) follow by Tukey test. All separated crowns and titanium base abutments were investigated under a light microscope (20x), using fisher's exact test for correlation of the failure types.ResultsThere was a significant difference in the mean value of tensile bond strength among the control and test groups. Comparisons between control(237.6±46.3N) and oxidized(241.7±46.3N) showed statistically different values from air abraded(372.9±113.2N) when assembled using different surface treatments of the titanium-based abutments. (p-value<0.005) As for failure type, there were statistically significant differences between control versus air abraded, control versus oxidized-air abraded, oxidized versus air abraded, and oxidized versus oxidized-air abraded. (p-value<0.001) The titanium surface morphology shown from the profilometer and SEM was coordinated. Control (Ra 333.8nm) and oxidized (Ra 321.0nm) groups surfaces showed smooth, corrugated surfaces, meanwhile air abraded (Ra 476.0nm) and oxidized-air abraded (Ra 423.8nm) groups showed rough, rugged surfaces.ConclusionHeat oxidization of titanium-based abutments did not adversely affect tensile bond strength or the failure mode and surface roughness between titanium base abutments and zirconia crowns. However, air abrasion of the titanium surface increased surface roughness and retentive strength.Clinical implicationsThe titanium base abutments that were oxidized under heat treatment did not have an effect on crown retention. Thoroughly air abraded the titanium abutment prior to cementation can increase cement bond strength.

Project description:This study evaluates the dynamic shift in the microbiota at the peri-implant site of titanium (Ti) and zirconia (Zr) implants subjected to experimental peri-implantitis (PI) and, for the first time, of implants made of ceria-stabilized alumina-reinforced zirconia (Ce-TZP/Al), a revolutionary zirconia that is set to play a key role in modern implant dentistry. One- and two-piece (TP) implants, including Ce-TZP/AL TP/G3 glass, were placed bilaterally (six implants/side) in five beagle dogs to mimic a natural vs. ligature-induced PI following a split-mouth design. The experiment spanned 30 weeks from tooth extraction. Both PI models promoted plaque deposition at peri-implant sites. Comparatively, the PI induced by ligatures favored the deposition of anaerobes (p = 0.047 vs. natural). Regardless of the model, the plaque deposition pattern was entirely dependent on the implanted material. Ligated Ti and Zr implant sites accumulated up to 2.14 log CFU/mL unit anaerobic load (p ≤ 0.033 vs. non-ligated implant sites), predominantly comprising obligate anaerobes. Naturally occurring PI induced the deposition of co-occurring networks of obligate anaerobes and less oxygen-dependent bacteria. PI induction favored the enrichment of Ti and Zr sites with bacterial taxa belonging to the orange and red complexes (up to 28% increase naturally and up to 71% in the ligated hemiarch). Anaerobic deposition was significantly lower in ligated Ce-TZP/Al implant sites (p ≤ 0.014 vs. TI and Zr) and independent of the induction model (0.63-1 log units of increase). Facultative bacteria prevailed at Ce-TZP/AL sites. The abundance was lower in the Ce-TZP/AL TP implant. Unlike Ti and Zr sites, taxa from the orange and red complexes were negligible. Biofilms configured at the Ti and Zr sites after ligation-induced PI resemble those found in severe IP. We hypothesize that, although surface properties (surface energy and surface roughness) and physicochemical properties of the substrate play an important role in bacterial adhesion and subsequent plaque formation, Ce-TZP/Al modulates several biological activities that preserve the integrity of the gingival seal by limiting PI progression. In conclusion, biofilm progression differs in peri-implant sites according to the specific properties of the material. Ce-TZP/A, unlike titanium or zirconia, prevents dysbiosis in sites subjected to experimental PI and preserves the microbial signature of emergent obligate anaerobes related to PI development.

Project description:Streptococci from the mitis group (represented mainly by Streptococcus mitis, Streptococcus oralis, Streptococcus sanguinis, and Streptococcus gordonii) form robust biofilms with Candida albicans in different experimental models. These microorganisms have been found in polymicrobial biofilms forming on titanium biomaterial surfaces in humans with peri-implant disease. The purpose of this work was to study mutualistic interactions in biofilms forming on titanium and their effect on the adjacent mucosa, using a relevant infection model. Single and mixed biofilms of C. albicans and each Streptococcus species were grown on titanium disks. Bacterial and fungal biovolume and biomass were quantified in these biofilms. Organotypic mucosal constructs were exposed to preformed titanium surface biofilms to test their effect on secretion of proinflammatory cytokines and cell damage. C. albicans promoted bacterial biofilms of all mitis Streptococcus species on titanium surfaces. This relationship was mutualistic since all bacterial species upregulated the efg1 hypha-associated gene in C. albicans Mixed biofilms caused increased tissue damage but did not increase proinflammatory cytokine responses compared to biofilms comprising Candida alone. Interestingly, spent culture medium from tissues exposed to titanium biofilms suppressed Candida growth on titanium surfaces.IMPORTANCE Our findings provide new insights into the cross-kingdom interaction between C. albicans and Streptococcus species representative of the mitis group. These microorganisms colonize titanium-based dental implant materials, but little is known about their ability to cause inflammation and damage of the adjacent mucosal tissues. Using an in vitro biomaterial-mucosal interface infection model, we showed that mixed biofilms of each species with C. albicans enhance tissue damage. One possible mechanism for this effect is the increased fungal hypha-associated virulence gene expression we observed in mixed biofilms with these species. Interestingly, we also found that the interaction of multispecies biofilms with organotypic mucosal surfaces led to the release of growth-suppressing mediators of Candida, which may represent a homeostatic defense mechanism of the oral mucosa against fungal overgrowth. Thus, our findings provide novel insights into biofilms on biomaterials that may play an important role in the pathogenesis of mucosal infections around titanium implants.

Dataset Information

Adhesion of streptococci to titanium and zirconia.

Publications

Adhesion of streptococci to titanium and zirconia.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets