Large magnetoelectric coupling in multiferroic oxide heterostructures assembled via epitaxial lift-off.

ABSTRACT: Epitaxial films may be released from growth substrates and transferred to structurally and chemically incompatible substrates, but epitaxial films of transition metal perovskite oxides have not been transferred to electroactive substrates for voltage control of their myriad functional properties. Here we demonstrate good strain transmission at the incoherent interface between a strain-released film of epitaxially grown ferromagnetic La_0.7Sr_0.3MnO₃ and an electroactive substrate of ferroelectric 0.68Pb(Mg_1/3Nb_2/3)O₃-0.32PbTiO₃ in a different crystallographic orientation. Our strain-mediated magnetoelectric coupling compares well with respect to epitaxial heterostructures, where the epitaxy responsible for strong coupling can degrade film magnetization via strain and dislocations. Moreover, the electrical switching of magnetic anisotropy is repeatable and non-volatile. High-resolution magnetic vector maps reveal that micromagnetic behaviour is governed by electrically controlled strain and cracks in the film. Our demonstration should inspire others to control the physical/chemical properties in strain-released epitaxial oxide films by using electroactive substrates to impart strain via non-epitaxial interfaces.

SUBMITTER: Pesquera D

PROVIDER: S-EPMC7314756 | biostudies-literature | 2020 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Large magnetoelectric coupling in multiferroic oxide heterostructures assembled via epitaxial lift-off.

Pesquera D D Khestanova E E Ghidini M M Zhang S S Rooney A P AP Maccherozzi F F Riego P P Farokhipoor S S Kim J J Moya X X Vickers M E ME Stelmashenko N A NA Haigh S J SJ Dhesi S S SS Mathur N D ND

Nature communications 20200624 1

Epitaxial films may be released from growth substrates and transferred to structurally and chemically incompatible substrates, but epitaxial films of transition metal perovskite oxides have not been transferred to electroactive substrates for voltage control of their myriad functional properties. Here we demonstrate good strain transmission at the incoherent interface between a strain-released film of epitaxially grown ferromagnetic La0.7Sr0.3MnO3 and an electroa ...[more]

PMID: 32581280

Similar Datasets

Project description:HighlightsThe (001)-oriented ferromagnetic La0.67Sr0.33MnO3 films are stuck onto the (011)-oriented ferroelectric single-crystal 0.7Pb(Mg1/3Nb2/3)O3-0.3PbTiO3 substrate with 0° and 45° twist angle. By applying a 7.2 kV cm-1 electric field, the coexistence of uniaxial and fourfold in-plane magnetic anisotropy is observed in 45° Sample, while a typical uniaxial anisotropy is found in 0° Sample. Manipulating strain mode and degree that can be applied to epitaxial complex oxide thin films have been a cornerstone of strain engineering. In recent years, lift-off and transfer technology of the epitaxial oxide thin films have been developed that enabled the integration of heterostructures without the limitation of material types and crystal orientations. Moreover, twisted integration would provide a more interesting strategy in artificial magnetoelectric heterostructures. A specific twist angle between the ferroelectric and ferromagnetic oxide layers corresponds to the distinct strain regulation modes in the magnetoelectric coupling process, which could provide some insight in to the physical phenomena. In this work, the La0.67Sr0.33MnO3 (001)/0.7Pb(Mg1/3Nb2/3)O3-0.3PbTiO3 (011) (LSMO/PMN-PT) heterostructures with 45º and 0º twist angles were assembled via water-etching and transfer process. The transferred LSMO films exhibit a fourfold magnetic anisotropy with easy axis along LSMO < 110 >. A coexistence of uniaxial and fourfold magnetic anisotropy with LSMO [110] easy axis is observed for the 45° Sample by applying a 7.2 kV cm-1 electrical field, significantly different from a uniaxial anisotropy with LSMO [100] easy axis for the 0° Sample. The fitting of the ferromagnetic resonance field reveals that the strain coupling generated by the 45° twist angle causes different lattice distortion of LSMO, thereby enhancing both the fourfold and uniaxial anisotropy. This work confirms the twisting degrees of freedom for magnetoelectric coupling and opens opportunities for fabricating artificial magnetoelectric heterostructures.

Dataset Information

Large magnetoelectric coupling in multiferroic oxide heterostructures assembled via epitaxial lift-off.

Publications

Large magnetoelectric coupling in multiferroic oxide heterostructures assembled via epitaxial lift-off.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets