Encapsidation of Different Plasmonic Gold Nanoparticles by the CCMV CP.

ABSTRACT: Different types of gold nanoparticles have been synthesized that show great potential in medical applications such as medical imaging, bio-analytical sensing and photothermal cancer therapy. However, their stability, polydispersity and biocompatibility are major issues of concern. For example, the synthesis of gold nanorods, obtained through the elongated micelle process, produce them with a high positive surface charge that is cytotoxic, while gold nanoshells are unstable and break down in a few weeks due to the Ostwald ripening process. In this work, we report the self-assembly of the capsid protein (CP) of cowpea chlorotic mottle virus (CCMV) around spherical gold nanoparticles, gold nanorods and gold nanoshells to form virus-like particles (VLPs). All gold nanoparticles were synthesized or treated to give them a negative surface charge, so they can interact with the positive N-terminus of the CP leading to the formation of the VLPs. To induce the protein self-assembly around the negative gold nanoparticles, we use different pH and ionic strength conditions determined from a CP phase diagram. The encapsidation with the viral CP will provide the nanoparticles better biocompatibility, stability, monodispersity and a new biological substrate on which can be introduced ligands toward specific cells, broadening the possibilities for medical applications.

SUBMITTER: Duran-Meza AL

PROVIDER: S-EPMC7321416 | biostudies-literature | 2020 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Encapsidation of Different Plasmonic Gold Nanoparticles by the CCMV CP.

Durán-Meza Ana L AL Escamilla-Ruiz Martha I MI Segovia-González Xochitl F XF Villagrana-Escareño Maria V MV Vega-Acosta J Roger JR Ruiz-Garcia Jaime J

Molecules (Basel, Switzerland) 20200605 11

Different types of gold nanoparticles have been synthesized that show great potential in medical applications such as medical imaging, bio-analytical sensing and photothermal cancer therapy. However, their stability, polydispersity and biocompatibility are major issues of concern. For example, the synthesis of gold nanorods, obtained through the elongated micelle process, produce them with a high positive surface charge that is cytotoxic, while gold nanoshells are unstable and break down in a fe ...[more]

PMID: 32516956

Similar Datasets

Project description:Octahedral anatase particles (OAPs), prepared by ultrasonication-hydrothermal reaction (US-HT), were modified with 2 wt% of gold by photodeposition. Conditions of US-HT process such as durations of US and durations of HT were varied to obtain OAPs products different by physicochemical and morphological properties. Au/OAPs samples were characterized by X-ray diffraction (XRD), scanning transmission electron microscopy (STEM), X-ray photoelectron spectroscopy (XPS) and diffuse reflectance spectroscopy (DRS). The photocatalytic activity was tested under UV irradiation for decomposition of acetic acid (CO2 system) and dehydrogenation of methanol (H2 system) under aerobic and anaerobic conditions, respectively, and for oxidation of 2-propanol under visible light irradiation. Photodeposition of gold was very fast for all OAPs samples (0.5-10 min) under Ar atmosphere, and the clear correlation between the content of electron traps (ETs) and the induction period, during which nanoparticles (NPs) of gold are formed, indicates that ETs in titania samples are a key-factor for rapidity of gold photodeposition on titania surface. It was found that better morphology of titania (larger content of faceted particles) resulted in formation of larger gold NPs, while small gold NPs were deposited on structural defects. Modification of OAPs with gold NPs resulted in significant enhancement of photocatalytic activity, being e.g., 1.5 (CO2 system), 7.7 (H2 system), and even more than 40 under vis irradiation. It was found that both the properties of titania and gold are crucial for resultant photocatalytic activity, but a direct correlation between one structural/physical property and photocatalytic activity could not be obtained since all structural properties changed simultaneously when conditions of photocatalyst preparation (US-HT) were changed. Therefore, gold NPs of controlled sizes were deposited on OAPs product with the best morphology by modified photodeposition method. Clear correlation between photocatalytic activity under visible light and the size of gold NPs indicates that gold properties are decisive for visible light activity rather than titania properties. 3D-FDTD simulations confirm that an increase in the size of gold NPs results in extended surface areas with field enhancement.

Dataset Information

Encapsidation of Different Plasmonic Gold Nanoparticles by the CCMV CP.

Publications

Encapsidation of Different Plasmonic Gold Nanoparticles by the CCMV CP.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets