Toughening of Biodegradable Poly(3-hydroxybutyrate-co-3-hydroxyvalerate)/Poly(?-caprolactone) Blends by In Situ Reactive Compatibilization.

ABSTRACT: Reactive extrusion of poly(3-hydroxybutyrate-co-3-hydroxyvalerate)/poly(?-caprolactone) (PHBV/PCL) blends was performed in the presence of cross-linker 1,3,5-tri-2-propenyl-1,3,5-triazine-2,4,6(1H,3H,5H)-trione (TAIC) and peroxide. The compatibility between the two biodegradable polymers was significantly improved only when TAIC and peroxide work together, as evidenced by the decreased PCL particle size and blurred interfacial gap between the PHBV and PCL. The mechanical, thermal, morphological, and rheological properties of the compatibilized blends were studied and compared to the blends without TAIC and peroxide. At the optimal TAIC content (1 phr), the elongation at break of the compatibilized blends was 380% that of the PHBV/PCL blend without any additives and 700% that of neat PHBV. The improved interfacial compatibility, decreased PCL particle size, and uniform PHBV crystals are all factors that contribute to improving the toughness of the blend. Through Fourier transform infrared (FTIR) and rheological studies, the reaction mechanism is discussed. The study shows that PHBV and PCL are cross-linked by TAIC, resulting in the formation of a PHBV–PCL co-polymer, which improves the compatibility of the blend. The biodegradable polymer blends with high crystallinity and improved toughness prepared in this study are proposed to be used in sustainable packaging or other applications.

SUBMITTER: Zytner P

PROVIDER: S-EPMC7330898 | biostudies-literature | 2020 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Toughening Poly(l-lactide) Blends: Effectiveness of Sequence-Controlled Six-Arm Star-Branched Block Copolymers of Poly(l-lactide) and Poly(ε-caprolactone).

Project description:Well-defined six-arm star-branched bio-degradable block copolymers of l-lactide and ε-caprolactone were prepared using controlled ring-opening polymerization and a sequential monomer addition method using dipentaerythritol as the initiator core and organocatalysts at low temperatures in solution. Sequence of enchainment was changed by reversing the order of monomer addition giving, either, a crystalline PLA block or an amorphous PCL block as the outer segment. Well-defined six-arm poly(ε-caprolactone-b-l-lactide, 6s-PCL-b-PLA) block copolymers were obtained with a range of segment molecular weights. However, in the case of six-arm poly(l-lactide-b-ε-caprolactone, 6s-PLA-b-PCL), disruption of the block structure was observed on account of competing transesterification reactions accompanying a chain-growth reaction. Such sequence-controlled block copolymers showed interesting phase morphologies, as evidenced by differential scanning calorimetry (DSC) studies. 6s-PCL-b-PLA showed two glass-transition temperatures and two melting temperatures characteristic of the amorphous and crystalline blocks. 6s-PCL-b-PLA and 6s-PLA-b-PCL with different segment chain lengths were solution blended (10 wt %) with a commercially sourced PLA. All the blends were highly transparent. The structure and properties of the blend were examined by DSC, measurement of mechanical properties, and scanning electron microscopy. The results show that a phase-separated 6s-PCL-b-PLA copolymer results in two- to three-fold improvement in tensile toughness without the loss of modulus. A possible hypothesis for the mechanism of tensile toughness in the blend has been proposed.

| S-EPMC8945082 | biostudies-literature

Blends of Poly(3-Hydroxybutyrate-co-3-Hydroxyvalerate) with Fruit Pulp Biowaste Derived Poly(3-Hydroxybutyrate-co-3-Hydroxyvalerate-co-3-Hydroxyhexanoate) for Organic Recycling Food Packaging.

Project description:In the present study, a new poly(3-hydroxybutyrate-co-3-hydroxyvalerate-co-3-hydroxyhexanoate) [P(3HB-co-3HV-co-3HHx)] terpolyester with approximately 68 mol% of 3-hydroxybutyrate (3HB), 17 mol% of 3-hydroxyvalerate (3HV), and 15 mol% of 3-hydroxyhexanoate (3HHx) was obtained via the mixed microbial culture (MMC) technology using fruit pulps as feedstock, a processing by-product of the juice industry. After extraction and purification performed in a single step, the P(3HB-co-3HV-co-3HHx) powder was melt-mixed, for the first time, in contents of 10, 25, and 50 wt% with commercial poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV). Thereafter, the resultant doughs were thermo-compressed to obtain highly miscible films with good optical properties, which can be of interest in rigid and semirigid organic recyclable food packaging applications. The results showed that the developed blends exhibited a progressively lower melting enthalpy with increasing the incorporation of P(3HB-co-3HV-co-3HHx), but retained the PHB crystalline morphology, albeit with an inferred lower crystalline density. Moreover, all the melt-mixed blends were thermally stable up to nearly 240 °C. As the content of terpolymer increased in the blends, the mechanical response of their films showed a brittle-to-ductile transition. On the other hand, the permeabilities to water vapor, oxygen, and, more notably, limonene were seen to increase. On the overall, this study demonstrates the value of using industrial biowaste derived P(3HB-co-3HV-co-3HHx) terpolyesters as potentially cost-effective and sustainable plasticizing additives to balance the physical properties of organic recyclable polyhydroxyalkanoate (PHA)-based food packaging materials.

| S-EPMC8038484 | biostudies-literature

Fibrous Materials Made of Poly(ε-caprolactone)/Poly(ethylene oxide)-b-Poly(ε-caprolactone) Blends Support Neural Stem Cells Differentiation.

Project description:In this work, we design and produce micron-sized fiber mats by blending poly(ε-caprolactone) (PCL) with small amounts of block copolymers poly(ethylene oxide)m-block-poly(ε-caprolactone)n (PEOm-b-PCLn) using electrospinning. Three different PEOm-b-PCLn block copolymers, with different molecular weights of PEO and PCL, were synthesized by ring opening polymerization of ε-caprolactone using PEO as initiator and stannous octoate as catalyst. The polymer blends were prepared by homogenous solvent mixing using dichloromethane for further electrospinning procedures. After electrospinning, it was found that the addition to PCL of the different block copolymers produced micron-fibers with smaller width, equal or higher hydrophilicity, lower Young modulus, and rougher surfaces, as compared with micron-fibers obtained only with PCL. Neural stem progenitor cells (NSPC), isolated from rat brains and grown as neurospheres, were cultured on the fibrous materials. Immunofluorescence assays showed that the NSPC are able to survive and even differentiate into astrocytes and neurons on the synthetic fibrous materials without any growth factor and using the fibers as guidance. Disassembling of the cells from the NSPC and acquisition of cell specific molecular markers and morphology progressed faster in the presence of the block copolymers, which suggests the role of the hydrophilic character and porous topology of the fiber mats.

| S-EPMC6835932 | biostudies-literature

Crystallization of Poly(ε-caprolactone) in Poly(vinylidene fluoride)/Poly(ε-caprolactone) Blend.

Project description:The crystallization behavior of poly(ε-caprolactone) (PCL) in a poly(vinylidene fluoride) (PVDF)/PCL blend as well as on a highly orientated PVDF substrate was studied by means of POM, DSC and TEM. The results show that the miscibility of the PVDF/PCL blend and the spherulitic morphology of PVDF varies with the blend ratio. For all the compositions, the pre-existing PVDF crystals accelerated the crystallization of PCL because the PVDF exhibits very strong nucleation ability toward PCL as reflected by the occurrence of heteroepitaxy and the transcrystallization of PBA on the PVDF substrate. This is associated with the perfect lattice matching between the PBA and PVDF crystals.

| S-EPMC6432374 | biostudies-literature

Toughening Biosourced Poly(lactic acid) and Poly(3-hydroxybutyrate-co-4-hydroxybutyrate) Blends by a Renewable Poly(epichlorohydrin-co-ethylene oxide) Elastomer.

Project description:A series of sustainable polymer blends from renewable poly(lactic acid) (PLA), poly(3-hydroxybutyrate-co-4-hydroxybutyrate) (P3,4HB), and poly(epichlorohydrin-co-ethylene oxide) (ECO) elastomer were fabricated via a melt blending method to gain balanced physical performance. The interplay of the composition, mutual miscibility, and viscosity ratio of the pristine PLA, P3,4HB, and ECO elastomer resulted in diverse phase structures of the ternary blends. An excellent flexibility at an elongation of 270% was achieved for the PLA/P3,4HB/ECO (70/20/10) blend with a core-shell structure. The PLA/P3,4HB/ECO (70/10/20) blend with a phase-separated structure exhibited a high impact strength of 54 KJ/m2, which is 25 times over that of the neat PLA. The relationship between the phase structure and physical performance of the blend was analyzed based on the compositions, surface tension, and physical characteristics of the neat components. Combining the compatibilization of the P3,4HB phase and ECO elastomer toughening played a crucial role in enhancing the mechanical properties of the blends.

| S-EPMC6882108 | biostudies-literature

Nucleation of Poly(lactide) Partially Wet Droplets in Ternary Blends with Poly(butylene succinate) and Poly(ε-caprolactone).

Project description:This work presents the first investigation on the crystallization behavior of partially wet droplets in immiscible ternary blends. Poly(lactide), poly(ε-caprolactone), and poly(butylene succinate) (PLA, PCL, and PBS, respectively) were melt blended in a 10/45/45 weight ratio to produce a "partial wetting" morphology with droplets of the PLA minor phase located at the interface between the other two major components. The crystallization process of the higher melting PLA droplets was studied by polarized light optical microscopy, while the other components remain in the molten state. We found that neighboring partially wet droplets nucleate in close sequence. This is unexpected since partially wet droplets display points of three-phase contact and, hence, should not touch each other. Moreover, the onset of poly(lactide) crystallization is frequently observed at the interface with molten PCL or PBS, with a significant preference for the former polymer. The observed sequential droplet-to-droplet crystallization is attributed to the weak partial wetting behavior of the PCL/PLA/PBS ternary system. In fact, the contact between the interfacially confined droplets during crystallization due to their mobility can lead to a transition from a partial to a completely wet state, with the formation of thin continuous layers bridging larger partially wet droplets. This allows crystallization to spread sequentially between neighboring domains. Using a simple heterogeneous nucleation model, it is shown that the nucleation of PLA on either PCL or PBS melts is energetically feasible. This study establishes a clear relationship between the unique partial wetting morphology of ternary blends and the nucleation of the minor component, paving the way to the understanding and control of crystallization in multiphasic polymer blends for advanced applications.

| S-EPMC8016171 | biostudies-literature

Properties and Degradation Performances of Biodegradable Poly(lactic acid)/Poly(3-hydroxybutyrate) Blends and Keratin Composites.

Project description:From environmental aspects, the recovery of keratin waste is one of the important needs and therefore also one of the current topics of many research groups. Here, the keratin hydrolysate after basic hydrolysis was used as a filler in plasticized polylactic acid/poly(3-hydroxybutyrate) blend under loading in the range of 1-20 wt%. The composites were characterized by infrared spectroscopy, and the effect of keratin on changes in molar masses of matrices during processing was investigated using gel permeation chromatography (GPC). Thermal properties of the composites were investigated using thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The effect of keratin loading on the mechanical properties of composite was investigated by tensile test and dynamic mechanical thermal analysis. Hydrolytic degradation of matrices and composites was investigated by the determination of extractable product amounts, GPC, DSC and NMR. Finally, microbial growth and degradation were investigated. It was found that incorporation of keratin in plasticized PLA/PHB blend provides material with good thermal and mechanical properties and improved degradation under common environmental conditions, indicating its possible application in agriculture and/or packaging.

| S-EPMC8399615 | biostudies-literature

Evaluation of the Hemocompatibility and Anticancer Potential of Poly(ε-Caprolactone) and Poly(3-Hydroxybutyrate) Microcarriers with Encapsulated Chrysin.

Project description:In this work, novel chrysin-loaded poly(ε-caprolactone) and poly(3-hydroxybutyrate) microcarriers were synthesized according to a modified oil-in-water single emulsion/solvent evaporation method, utilizing poly(vinyl alcohol) surfactant as stabilizer and dispersing agent for the emulsification, and were evaluated for their physico-chemical and morphological properties, loading capacity and entrapment efficiency and in vitro release of their load. The findings suggest that the novel micro-formulations possess a spherical and relatively wrinkled structure with sizes ranging between 2.4 and 24.7 µm and a highly negative surface charge with z-potential values between (-18.1)-(-14.1) mV. The entrapment efficiency of chrysin in the poly(ε-caprolactone) and poly(3-hydroxybutyrate) microcarriers was estimated to be 58.10% and 43.63%, whereas the loading capacity was found to be 3.79% and 15.85%, respectively. The average release percentage of chrysin was estimated to be 23.10% and 18.01%, respectively. The novel micromaterials were further biologically evaluated for their hemolytic activity through hemocompatibility studies over a range of hematological parameters and cytoxicity against the epithelial human breast cancer cell line MDA-MB 231. The poly(ε-caprolactone) and poly(3-hydroxybutyrate) microcarriers reached an IC50 value with an encapsulated chrysin content of 149.19 µM and 312.18 µM, respectively, and showed sufficient blood compatibility displaying significantly low (up to 2%) hemolytic percentages at concentrations between 5 and 500 µg·mL-1.

| S-EPMC7831015 | biostudies-literature

Study on the 3D printability of poly(3-hydroxybutyrate-co-3-hydroxyvalerate)/poly(lactic acid) blends with chain extender using fused filament fabrication.

Project description:In this study, the 3D printability of a series of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV)/poly(lactic acid) (PLA) blends were investigated using fused filament fabrication (FFF). The studied blends suffered from poor 3D printability due to differences in compatibility and low thermal resistance. These shortcomings were addressed by incorporating a functionalized styrene-acrylate copolymer with oxirane moieties as a chain extender (CE). To enhance mechanical properties, the synergistic effect of 3D printing parameters such as printing temperature and speed, layer thickness and bed temperature were explored. Rheological analysis showed improvement in the 3D printability of PHBV:PLA:CE blend by allowing a higher printing temperature (220 °C) and sufficient printing speed (45 mm s-1). The surface morphology of fractured tensile specimens showed good bonding between layers when a bed temperature of 60 °C was used and a layer thickness of 0.25 mm was designed. The optimized printing samples shown higher storage modulus and strength, resulting in stiffer and stronger parts. The crystallinity, morphology and performance of the 3D printed products were correlated to share key methods to improve the 3D printability of PHBV:PLA based blends which may be implemented in other biopolymer blends, and further highlight how process parameters enhance the mechanical performance of 3D printed products.

| S-EPMC7367353 | biostudies-literature

Microstructural Evolution of Poly(ε-Caprolactone), Its Immiscible Blend, and In Situ Generated Nanocomposites.

Project description:Polymer-polymer systems with special phase morphology were prepared, leading to an exceptional combination of strength, modulus, and ductility. Two immiscible polymers: poly(ε-caprolactone) (PCL) and polyhydroxyalkanoate (PHA) were used as components for manufacturing a nanoblend and a nanocomposite characterized by nanodroplet-matrix and nanofibril-matrix morphologies, respectively. Nanofibrils were formed by high shear of nanodroplets at sufficiently low temperature to stabilize their fibrillar shape by shear-induced crystallization. The effects of nanodroplet vs. nanofiber morphology on the tensile mechanical behavior of the nanocomposites were elucidated with the help of in situ 2D small-angle X-ray scattering, microcalorimetry and 2D wide-angle X-ray diffraction. For neat PCL and a PCL/PHA blend, the evolution of the structure under uniaxial tension was accompanied by extensive fragmentation of crystalline lamellae with the onset at strain e = 0.1. Limited lamellae fragmentation in the PCL/PHA composite occurred continuously over a wide range of deformations (e = 0.1-1.1) and facilitated plastic flow of the composite and was associated with the presence of a PHA nanofiber network that transferred local stress to the PCL lamellae, enforcing their local deformation. The PHA nanofibers acted as crystallization nuclei for PCL during their strain-induced melting-recrystallization.

| S-EPMC7694185 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data