Na-Montmorillonite vs. Organically Modified Montmorillonite as Essential Oil Nanocarriers for Melt-Extruded Low-Density Poly-Ethylene Nanocomposite Active Packaging Films with a Controllable and Long-Life Antioxidant Activity.

ABSTRACT: Nowadays, active packaging is becoming significant for the extension of the shelf life of food products via the incorporation of raw nanomaterials such as nanoclays and bioactive compounds such as essential oils (EO). This study aims to study the performance of the sodium montmorillonite (NaMt) and organically modified montmorillonite (OrgMt) as thyme (TO), oregano (OO), and basil (BO) essential oil (EO) control release nanocarriers in low-density poly-ethylene (LDPE) active films. NaMt and OrgMt nanofillers are modified with low (20 wt.%), medium (40 wt.%), and high (80 wt.%) nominal contents of TO, OO, and BO. The novel active packaging films were tested using the X-ray diffraction method (XRD), tensile, water, and oxygen barrier properties, and antioxidant activity tests. For the two most active packaging films, the lipid oxidation of chicken breast fillets estimated by the thiobarbituric-acid-reacting substances (TBARS) method. Overall study shows that both NaMtEO-based and OrgMt-based films exhibited controllable and sustained antioxidant activity. All films retained up to 50-70% of their antioxidant activity after six months of incubation. OrgMtEO-based LDPE films showed more significance applied as active packaging films than NaMtEO-based LDPE films because of their highest tensile and barrier properties.

SUBMITTER: Giannakas A

PROVIDER: S-EPMC7352687 | biostudies-literature | 2020 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Na-Montmorillonite vs. Organically Modified Montmorillonite as Essential Oil Nanocarriers for Melt-Extruded Low-Density Poly-Ethylene Nanocomposite Active Packaging Films with a Controllable and Long-Life Antioxidant Activity.

Giannakas Aris A

Nanomaterials (Basel, Switzerland) 20200527 6

Nowadays, active packaging is becoming significant for the extension of the shelf life of food products via the incorporation of raw nanomaterials such as nanoclays and bioactive compounds such as essential oils (EO). This study aims to study the performance of the sodium montmorillonite (NaMt) and organically modified montmorillonite (OrgMt) as thyme (TO), oregano (OO), and basil (BO) essential oil (EO) control release nanocarriers in low-density poly-ethylene (LDPE) active films. NaMt and OrgM ...[more]

PMID: 32471304

Similar Datasets

Project description:Nanocomposite hydrogels have found a wide scope in regenerative medicine, tissue engineering, and smart drug delivery applications. The present study reports the formulations of biocompatible nanocomposite hydrogel films using carboxymethyl cellulose-hydroxyethyl cellulose-acrylonitrile-linseed oil polyol (CHAP) plain hydrogel and Na-montmorillonite (NaMMT) dispersed CHAP nanocomposite hydrogel films (NaCHAP) using solution blending technique. The structural, morphological, and mechanical properties of resultant nanocomposite hydrogel films were further investigated to analyze the effects of polyol and NaMMT on the characteristic properties. The synergistic effect of polyol and nanofillers on the mechanical strength and sustained drug-release behavior of the resultant hydrogel films was studied, which revealed that the increased cross-link density of hydrogels enhanced the elastic modulus (up to 99%) and improved the drug retention time (up to 72 h at both pHs 7.4 and 4.0). The release rate of cisplatin in nanocomposite hydrogel films was found to be higher in CHAP-1 (83 and 69%) and CHAP-3 (79 and 64%) than NaCHAP-3 (77 and 57%) and NaCHAP-4 (73 and 54%) at both pHs 4.0 and 7.4, respectively. These data confirmed that the release rate of cisplatin in nanocomposite hydrogel films was pH-responsive and increased with decrease of pH. All nanocomposite hydrogel films have exhibited excellent pH sensitivity under buffer solution of various pHs (1.0, 4.0, 7.4, and 9.0). The in vitro biocompatibility and cytotoxicity tests of these films were also conducted using 3-(4,5-dimethylthiazole-2-yl-2,5-diphenyl tetrazolium bromide) assay of human embryonic kidney (HEK-293) and human breast cancer (MCF-7) cell lines up to 48 h, which shows their biocompatible nature. However, cisplatin-loaded nanocomposite hydrogel films effectively inhibited the growth of human breast MCF-7 cancer cells. These studies suggested that the proposed nanocomposite hydrogel films have shown promising application in therapeutics, especially for anticancer-targeted drug delivery.

Project description:Infections in nonhealing wounds remain one of the major challenges. Recently, nanomedicine approach seems a valid option to overcome the antibiotic resistance mechanisms. The aim of this study was the development of three types of polysaccharide-based scaffolds (chitosan-based (CH), chitosan/chondroitin sulfate-based (CH/CS), chitosan/hyaluronic acid-based (CH/HA)), as dermal substitutes, to be loaded with norfloxacin, intended for the treatment of infected wounds. The scaffolds have been loaded with norfloxacin as a free drug (N scaffolds) or in montmorillonite nanocomposite (H-hybrid-scaffolds). Chitosan/glycosaminoglycan (chondroitin sulfate or hyaluronic acid) scaffolds were prepared by means of electrospinning with a simple, one-step process. The scaffolds were characterized by 500 nm diameter fibers with homogeneous structures when norfloxacin was loaded as a free drug. On the contrary, the presence of nanocomposite caused a certain degree of surface roughness, with fibers having 1000 nm diameters. The presence of norfloxacin-montmorillonite nanocomposite (1%) caused higher deformability (90%-120%) and lower elasticity (5-10 mN/cm2), decreasing the mechanical resistance of the systems. All the scaffolds were proven to be degraded via lysozyme (this should ensure scaffold resorption) and this sustained the drug release (from 50% to 100% in 3 days, depending on system composition), especially when the drug was loaded in the scaffolds as a nanocomposite. Moreover, the scaffolds were able to decrease the bioburden at least 100-fold, proving that drug loading in the scaffolds did not impair the antimicrobial activity of norfloxacin. Chondroitin sulfate and montmorillonite in the scaffolds are proven to possess a synergic performance, enhancing the fibroblast proliferation without impairing norfloxacin's antimicrobial properties. The scaffold based on chondroitin sulfate, containing 1% norfloxacin in the nanocomposite, demonstrated adequate stiffness to sustain fibroblast proliferation and the capability to sustain antimicrobial properties to prevent/treat nonhealing wound infection during the healing process.

Dataset Information

Na-Montmorillonite vs. Organically Modified Montmorillonite as Essential Oil Nanocarriers for Melt-Extruded Low-Density Poly-Ethylene Nanocomposite Active Packaging Films with a Controllable and Long-Life Antioxidant Activity.

Publications

Na-Montmorillonite vs. Organically Modified Montmorillonite as Essential Oil Nanocarriers for Melt-Extruded Low-Density Poly-Ethylene Nanocomposite Active Packaging Films with a Controllable and Long-Life Antioxidant Activity.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets