Properties of wood composite plastics made from predominant Low Density Polyethylene (LDPE) plastics and their degradability in nature.

ABSTRACT: To address concerns over plastics in the global environment, this project produced three wood plastics composites (WPCs) which could divert plastics from the waste stream into new materials. The three materials made had a ratio of 85%:15%, 90%:10%, and 95%:5% low density polyethylene (LDPE) to wood powder and were produced using the dissolution method. Physical and mechanical properties of each WPC were evaluated according to Japanese Industrial Standard (JIS) A 5908:2003. Their degradation in nature was evaluated through a graveyard test and assay test conducted in Coptotermes curvignathus termites. Results showed that density, moisture content, thickness swelling and water absorption of the WPCs fulfilled the JIS standard. The mechanical properties of these composites also met the JIS standard, particularly their modulus of elasticity (MOE). Modulus of rupture (MOR) and internal bonding (IB) showed in lower values, depending on the proportion of wood filler they contained. Discoloration of the WPCs was observed after burial in the soil with spectra alteration of attenuated transmission reflectance (ATR) in the band of 500-1000 cm-1 which could be assigned to detach the interphase between wood and plastics. As termite bait, the WPCs decreased in weight, even though the mass loss was comparatively small. Micro Confocal Raman Imaging Spectrometer revealed that termite guts from insects feeding on WPCs contained small amounts of LDPE. This indicated termite can consume plastics in the form of WPCs. Thus WPCs made predominantly of plastics can be degraded in nature. While producing WPCs can assist in decreasing plastics litter in the environment, the eventual fate of the LDPE in termites is still unknown.

SUBMITTER: Nuryawan A

PROVIDER: S-EPMC7398493 | biostudies-literature | 2020

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Properties of wood composite plastics made from predominant Low Density Polyethylene (LDPE) plastics and their degradability in nature.

Nuryawan Arif A Hutauruk Nova O NO Purba Esra Yunita S EYS Masruchin Nanang N Batubara Ridwanti R Risnasari Iwan I Satrio Fatih Khusno FK Rahmawaty Basyuni Mohammad M McKay Deirdre D

PloS one 20200803 8

To address concerns over plastics in the global environment, this project produced three wood plastics composites (WPCs) which could divert plastics from the waste stream into new materials. The three materials made had a ratio of 85%:15%, 90%:10%, and 95%:5% low density polyethylene (LDPE) to wood powder and were produced using the dissolution method. Physical and mechanical properties of each WPC were evaluated according to Japanese Industrial Standard (JIS) A 5908:2003. Their degradation in n ...[more]

PMID: 32745098

Similar Datasets

Project description:Exploring the catabolic repertoire of natural bacteria for biodegradation of plastics is one of the priority areas of biotechnology research. Low Density Polyethylene (LDPE) is recalcitrant and poses serious threats to our environment. The present study explored the LDPE biodegradation potential of aerobic bacteria enriched from municipal waste dumpsite and bentonite based drilling fluids from a deep subsurface drilling operation. Considerable bacterial growth coupled with significant weight loss of the LDPE beads (∼8%), change in pH to acidic condition and biofilm cell growth around the beads (CFU count 105-106/cm2) were noted for two samples (P and DF2). The enriched microbial consortia thus obtained displayed high (65-90%) cell surface hydrophobicity, confirming their potential toward LDPE adhesion as well as biofilm formation. Two LDPE degrading bacterial strains affiliated to Stenotrophomonas sp. and Achromobacter sp. were isolated as pure culture from P and DF2 enrichments. 16S rRNA gene sequences of these isolates indicated their taxonomic novelty. Further biodegradation studies provided strong evidence toward the LDPE metabolizing ability of these two organisms. Atomic Fore Microscopy (AFM) and Scanning Electron Microscopy (SEM) revealed considerable damage (in terms of formation of cracks, grooves, etc.) on the micrometric surface of the LDPE film. Analysis of the average roughness (Ra), root mean square roughness (Rq), average height (Rz), maximum peak height (Rp), and maximum valley depth (Rv) (nano-roughness parameters) through AFM indicated 2-3 fold increase in nano-roughness of the LDPE film. FTIR analysis suggested incorporation of alkoxy (1000-1090 cm-1), acyl (1220 cm-1), nitro (1500-1600 cm-1), carbonyl (1720 cm-1) groups into the carbon backbone, formation of N-O stretching (1360 cm-1) and chain scission (905 cm-1) in the microbially treated LDPEs. Increase in carbonyl index (15-20 fold), double bond index (1.5-2 fold) and terminal double bond index (30-40 fold) confirmed that biodegraded LDPEs had undergone oxidation, vinylene formation and chain scission. The data suggested that oxidation and dehydrogenation could be the key steps allowing formation of low molecular weight products suitable for their further mineralization by the test bacteria. The study highlighted LDPE degrading ability of natural bacteria and provided the opportunity for their development in plastic remediation process.

Dataset Information

Properties of wood composite plastics made from predominant Low Density Polyethylene (LDPE) plastics and their degradability in nature.

Publications

Properties of wood composite plastics made from predominant Low Density Polyethylene (LDPE) plastics and their degradability in nature.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets