Effect-Based Approach to Assess Nanostructured Cellulose Sponge Removal Efficacy of Zinc Ions from Seawater to Prevent Ecological Risks.

ABSTRACT: To encourage the applicability of nano-adsorbent materials for heavy metal ion removal from seawater and limit any potential side effects for marine organisms, an ecotoxicological evaluation based on a biological effect-based approach is presented. ZnCl2 (10 mg L-1) contaminated artificial seawater (ASW) was treated with newly developed eco-friendly cellulose-based nanosponges (CNS) (1.25 g L-1 for 2 h), and the cellular and tissue responses of marine mussel Mytilus galloprovincialis were measured before and after CNS treatment. A control group (ASW only) and a negative control group (CNS in ASW) were also tested. Methods: A significant recovery of Zn-induced damages in circulating immune and gill cells and mantle edges was observed in mussels exposed after CNS treatment. Genetic and chromosomal damages reversed to control levels in mussels' gill cells (DNA integrity level, nuclear abnormalities and apoptotic cells) and hemocytes (micronuclei), in which a recovery of lysosomal membrane stability (LMS) was also observed. Damage to syphons, loss of cilia by mantle edge epithelial cells and an increase in mucous cells in ZnCl2-exposed mussels were absent in specimens after CNS treatment, in which the mantle histology resembled that of the controls. No effects were observed in mussels exposed to CNS alone. As further proof of CNS' ability to remove Zn(II) from ASW, a significant reduction of >90% of Zn levels in ASW after CNS treatment was observed (from 6.006 to 0.510 mg L-1). Ecotoxicological evaluation confirmed the ability of CNS to remove Zn from ASW by showing a full recovery of Zn-induced toxicological responses to the levels of mussels exposed to ASW only (controls). An effect-based approach was thus proven to be useful in order to further support the environmentally safe (ecosafety) application of CNS for heavy metal removal from seawater.

SUBMITTER: Liberatori G

PROVIDER: S-EPMC7407410 | biostudies-literature | 2020 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Effect-Based Approach to Assess Nanostructured Cellulose Sponge Removal Efficacy of Zinc Ions from Seawater to Prevent Ecological Risks.

Liberatori Giulia G Grassi Giacomo G Guidi Patrizia P Bernardeschi Margherita M Fiorati Andrea A Scarcelli Vittoria V Genovese Massimo M Faleri Claudia C Protano Giuseppe G Frenzilli Giada G Punta Carlo C Corsi Ilaria I

Nanomaterials (Basel, Switzerland) 20200630 7

To encourage the applicability of nano-adsorbent materials for heavy metal ion removal from seawater and limit any potential side effects for marine organisms, an ecotoxicological evaluation based on a biological effect-based approach is presented. ZnCl2 (10 mg L-1) contaminated artificial seawater (ASW) was treated with newly developed eco-friendly cellulose-based nanosponges (CNS) (1.25 g L-1 for 2 h), and the cellular and tissue responses of marine mussel M ...[more]

PMID: 32629917

Similar Datasets

Project description:In this research article, wood based microfibrillated cellulose (MFC) was studied to gain a better understanding of the process of dependent network formation. Networking potential and obtained properties of the produced dimensional structures could be controlled using opted processing routes. The fabricated dimensional structure, using freeze-drying (FD) is a highly open and porous network (98% porosity) compared to slightly tight, dense and less porous network produced after pressing at 200kN (96% porosity), followed by vacuum-filtered (VF) networks (33% porosity). The porosity (17%) was further decreased when the casting (CS) method was used, further producing a highly dense and compressed network. High water flux (180.8?±?11?L/m2h) of pressed freeze-dried (PFD) followed by vacuum-filtered (VF) (11.4?±?1.9?L/m2h) and casting CS (0.7?±?0.01?L/m2h) were calculated using device. Furthermore, increased water flux (1.4 fold) of Experimental Paper Machine (XPM) based structures was reported in comparison with CS structures. Pore-sized distribution and surface area were measured using Hg porosimetry; they showed an average pore size of 16.5 ?m for FD, followed by PFD (8.2 ?m) structures. A 27-fold decrease in average pore-size was observed for CS structure in comparison with the FD structures. Highest tensile strength (87?±?21?MPa) was recorded for CS structures, indicating a more highly compacted network formation compared to VF (82?±?19?MPa) and PFD (1.6?±?0.06?MPa). Furthermore, an attempt was made to upscale the VF structures using traditional paper making approach on XMP. Improved tensile strength (73?±?11?MPa) in machine produced structures is due to alignment of fibers towards machine direction compared to cross directional (43?±?9?MPa) fractured structures as shown in our Scanning Electron Microscopy (SEM) analysis. Surface functionalization of MFC using enzyme (hexokinase) was performed to increase the adsorption efficiency towards ferric ions removal. All fabricated structures were further evaluated for Fe(iii) removal and it was summarized that charge densities of functional groups, produced ?-potential and networking potential were dominating influential factors for adsorption fluctuation of ferric ions.

Project description:Sponges are efficient filter feeders, removing significant portions of particulate and dissolved organic matter (POM, DOM) from the water column. While the assimilation and respiration of POM and DOM by sponges and their abundant microbial symbiont communities have received much attention, there is virtually no information on the impact of sponge holobiont metabolism on the composition of DOM at a molecular-level. We applied untargeted and targeted metabolomics techniques to characterize DOM in seawater samples prior to entering the sponge (inhalant reef water), in samples exiting the sponge (exhalent seawater), and in samples collected just outside the reef area (off reef seawater). Samples were collected from two sponge species, Ircinia campana and Spheciospongia vesparium, on a near-shore hard bottom reef in the Florida Keys. Metabolic profiles generated from untargeted metabolomics analysis indicated that many more compounds were enhanced in the exhalent samples than in the inhalant samples. Targeted metabolomics analysis revealed differences in diversity and concentration of metabolites between exhalent and off reef seawater. For example, most of the nucleosides were enriched in the exhalent seawater, while the aromatic amino acids, caffeine and the nucleoside xanthosine were elevated in the off reef water samples. Although the metabolic profile of the exhalent seawater was unique, the impact of sponge metabolism on the overall reef DOM profile was spatially limited in our study. There were also no significant differences in the metabolic profiles of exhalent water between the two sponge species, potentially indicating that there is a characteristic DOM profile in the exhalent seawater of Caribbean sponges. Additional work is needed to determine whether the impact of sponge DOM is greater in habitats with higher sponge cover and diversity. This work provides the first insight into the molecular-level impact of sponge holobiont metabolism on reef DOM and establishes a foundation for future experimental studies addressing the influence of sponge-derived DOM on chemical and ecological processes in coral reef ecosystems.

Dataset Information

Effect-Based Approach to Assess Nanostructured Cellulose Sponge Removal Efficacy of Zinc Ions from Seawater to Prevent Ecological Risks.

Publications

Effect-Based Approach to Assess Nanostructured Cellulose Sponge Removal Efficacy of Zinc Ions from Seawater to Prevent Ecological Risks.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets