Influence of the Infill Orientation on the Properties of Zirconia Parts Produced by Fused Filament Fabrication.

ABSTRACT: The fused filament fabrication (FFF) of ceramics enables the additive manufacturing of components with complex geometries for many applications like tooling or prototyping. Nevertheless, due to the many factors involved in the process, it is difficult to separate the effect of the different parameters on the final properties of the FFF parts, which hinders the expansion of the technology. In this paper, the effect of the fill pattern used during FFF on the defects and the mechanical properties of zirconia components is evaluated. The zirconia-filled filaments were produced from scratch, characterized by different methods and used in the FFF of bending bars with infill orientations of 0°, ±45° and 90° with respect to the longest dimension of the specimens. Three-point bending tests were conducted on the specimens with the side in contact with the build platform under tensile loads. Next, the defects were identified with cuts in different sections. During the shaping by FFF, pores appeared inside the extruded roads due to binder degradation and or moisture evaporation. The changes in the fill pattern resulted in different types of porosity and defects in the first layer, with the latter leading to earlier fracture of the components. Due to these variations, the specimens with the 0° infill orientation had the lowest porosity and the highest bending strength, followed by the specimens with ±45° infill orientation and finally by those with 90° infill orientation.

SUBMITTER: Cano S

PROVIDER: S-EPMC7411807 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Temperature Analyses in Fused Filament Fabrication: From Filament Entering the Hot-End to the Printed Parts.

Project description:This article analyzes temperature fields and their variations in fused filament fabrication (FFF) from the filament entering the hot-end to the printed parts, aiming at a deeper understanding of the thermal process of this additive manufacturing technology. A standard E3D print head assembly was mounted on a robot arm for printing. A stable filament feeding region was determined with an upper limit in the volume flow rate at different nozzle temperatures. Within the limit, the steady-state temperature fields inside the hot-end were studied by a computational fluid dynamics model. Simulations indicated that the temperature became less homogeneous at higher flow rates, leading to a lower extrudate temperature at the nozzle outlet. These outlet temperatures were analyzed, validated, and used as input to simulate temperature variations in printed parts with a self-developed open-access numerical model. An interlayer time similarity rule was found in printing single-walled geometries, which specifies temperature similarities at the same interlayer time. The findings provide new insights into FFF processes, pointing out opportunities for improved production efficiency and scalability to large-scale manufacturing.

| S-EPMC9831539 | biostudies-literature

Optimization of the 3D Printing Parameters for Tensile Properties of Specimens Produced by Fused Filament Fabrication of 17-4PH Stainless Steel.

Project description:Fused filament fabrication (FFF) combined with debinding and sintering could be an economical process for three-dimensional (3D) printing of metal parts. In this paper, compounding, filament making, and FFF processing of feedstock material with 55% vol. of 17-4PH stainless steel powder in a multicomponent binder system are presented. The experimental part of the paper encompasses central composite design for optimization of the most significant 3D printing parameters (extrusion temperature, flow rate multiplier, and layer thickness) to obtain maximum tensile strength of the 3D-printed specimens. Here, only green specimens were examined in order to be able to determine the optimal parameters for 3D printing. The results show that the factor with the biggest influence on the tensile properties was flow rate multiplier, followed by the layer thickness and finally the extrusion temperature. Maximizing all three parameters led to the highest tensile properties of the green parts.

| S-EPMC7040736 | biostudies-literature

Graphene/Carbon Nanotube Hybrid Nanocomposites: Effect of Compression Molding and Fused Filament Fabrication on Properties.

Project description:The present work reports on the production and characterization of acrylonitrile butadiene styrene (ABS) hybrid nanocomposite filaments incorporating graphene nanoplatelets (GNPs) and carbon nanotubes (CNTs) suitable for fused filament fabrication (FFF). At first, nanocomposites with a total nanofiller content of GNP and/or CNT of 6 wt.% and a GNP/CNT relative percentage ratio of 0, 10, 30, 50, 70, and 100 were produced by melt compounding and compression molding. Their mechanical, electrical resistivity, and electromagnetic interference shielding effectiveness (EMI SE) properties were evaluated. The hybrid nanocomposites showed a linear increase in modulus and decrease in strength as a function of GNP content; on the other hand, the addition of CNT in hybrid nanocomposites determined a positive increase in electrical conductivity, but a potentially critical decrease of melt flow index. Due to the favorable compromise between processability and enhancement of performance (i.e., mechanical and electrical properties), the hybrid composition of 50:50 GNP/CNT was selected as the most suitable for the filament production of 6 wt.% carbonaceous nanocomposites. EMI SE of ABS-filled single CNT and hybrid GNP/CNT nanofillers obtained from compression molding reached the requirement for applications (higher than -20 dB), while slightly lower EMI SE values (in the range -12/-16 dB) were obtained for FFF parts dependent on the building conditions.

| S-EPMC7022553 | biostudies-literature

Development of Antimicrobial PLA Composites for Fused Filament Fabrication.

Project description:In addition to possessing the desirable properties of being a biodegradable and biocompatible polymer fabricated from renewable resources, poly (lactic acid) (PLA) has useful mechanical and thermal attributes that has enabled it to be one of the most widely-used plastics for medicine, manufacturing, and agriculture. Yet, PLA composites have not been heavily explored for use in 3D-printing applications, and the range of feasible materials for the technology is limited, which inhibits its potential growth and industry adoption. In this study, tunable, multifunctional antimicrobial PLA composite filaments for 3D-printing have been fabricated and tested via chemical, thermal, mechanical, and antimicrobial experiments. Thermally stable antimicrobial ceramics, ZnO and TiO2, were used as fillers up to 30 wt%, and poly (ethylene glycol) (PEG) was used as a plasticizer to tune the physical material properties. Results demonstrate that the PLA composite filaments exhibit the thermal phase behaviors and thermal stability suitable for 3D-printing. Additionally, PEG can be used to tune the mechanical properties while not affecting the antimicrobial efficacy that ZnO and TiO2 imbue.

| S-EPMC7918987 | biostudies-literature

Analysis of the Effect of the Surface Inclination Angle on the Roughness of Polymeric Parts Obtained with Fused Filament Fabrication Technology

Project description:The aim of this work was to conduct a dimensional study, in terms of microgeometry, using parts from an additive manufacturing process with fused filament fabrication (FFF) technology. As in most cases of additive manufacturing processes, curved surfaces were obtained via approximation of planes with different inclinations. The focus of this experimental study was to analyze the surface roughness of curve geometry from surface-roughness measurements of the plane surfaces that generate it. Three relevant manufacturing parameters were considered: layer height, nozzle diameter and material. Taguchi’s experimental design based on the Latin square was applied to optimize the set of specimens used. For the manufactured samples, the surface-roughness parameters Ra (roughness average), Rq (root mean square roughness) and Rz (maximum height) were obtained in eight planes of different inclinations (0° to 90°). The results were analyzed using both a graphical model and an analysis of variance study (ANOVA), demonstrating the dependency relationships among the parameters considered and surface finish. The best surface roughness was reached at 85°, with a global average Ra value of 8.66 µm, increasing the average Ra value from 6.39 µm to 11.57 µm according to the layer height increase or decreasing it slightly, from 8.91 µm to 8.41 µm, in relation to the nozzle diameter increase. On the contrary, the worst surface roughness occurred at 20°, with a global average Ra value of 19.05 µm. Additionally, the theoretical profiles and those from the surface-roughness measurement were found to coincide greatly. Eventually, the eight regression curves from the ANOVA allowed prediction of outputs from future specimens tested under different conditions.

| S-EPMC9919160 | biostudies-literature

Simple and Versatile 3D Printed Microfluidics Using Fused Filament Fabrication.

Project description:The uptake of microfluidics by the wider scientific community has been limited by the fabrication barrier created by the skills and equipment required for the production of traditional microfluidic devices. Here we present simple 3D printed microfluidic devices using an inexpensive and readily accessible printer with commercially available printer materials. We demonstrate that previously reported limitations of transparency and fidelity have been overcome, whilst devices capable of operating at pressures in excess of 2000 kPa illustrate that leakage issues have also been resolved. The utility of the 3D printed microfluidic devices is illustrated by encapsulating dental pulp stem cells within alginate droplets; cell viability assays show the vast majority of cells remain live, and device transparency is sufficient for single cell imaging. The accessibility of these devices is further enhanced through fabrication of integrated ports and by the introduction of a Lego®-like modular system facilitating rapid prototyping whilst offering the potential for novices to build microfluidic systems from a database of microfluidic components.

| S-EPMC4822857 | biostudies-literature

Fundamentals of Crystalline Evolution and Properties of Carbon Nanotube-Reinforced Polyether Ether Ketone Nanocomposites in Fused Filament Fabrication.

Project description:As fused filament fabrication (FFF) continues to gain popularity, many studies are turning to nanomaterials or optimization of printing parameters to improve the materials' properties; however, many overlook how materials formulation and additive manufacturing (AM) processes cooperatively engineer the evolution of properties across length scales. Evaluating the in-process evolution of the nanocomposite using AM will provide a fundamental understanding of the material's microstructure, which can be tailored to create unique characteristics in functionality and performance. In this study, the crystallinity behavior of polyetheretherketone (PEEK) was studied in the presence of carbon nanotubes (CNTs) as a nucleation aid for improved crystallization during FFF processing. Using various characterization techniques and molecular dynamics simulations, it was discovered that the crystallization behavior of extruded filaments is very different from that of 3D printed roads. Additionally, the printed material exhibited cold crystallization, and the CNT addition increased the crystallization of printed roads, which were amorphous without CNT addition. Tensile strength and modulus were increased by as much as 42 and 51%, respectively, due to higher crystallinity during printing. Detailed knowledge on the morphology of PEEK-CNT used in FFF allows gaining a fundamental understanding of the morphological evolution occurring during the AM process that in turn enables formulating materials for the AM process to achieve tailored mechanical and functional properties, such as crystallinity or conductivity.

| S-EPMC10853907 | biostudies-literature

Synthesis and Characterisation of ASA-PEEK Composites for Fused Filament Fabrication.

Project description:In this paper, a series of polymer composites made from acrylonitrile-styrene-acrylate (ASA) and poly (ether ether ketone) (PEEK) were manufactured. ASA acts as a polymer matrix while PEEK is loaded in the form of micro-particles that act as a reinforcing filler. The composites were compounded by single screw extrusion and then, different specimens were manufactured either via injection moulding (IM) or fused filament fabrication (FFF). Two different types of PEEK (commercial and reused) in different concentrations (3 and 6 wt.%) were tested and their influence in the mechanical, structural, and thermal properties were studied. It was observed that reused PEEK enhanced the stiffness and tensile strength and thermal stability of the composites both, for injected and printed specimens. This evidences the suitability of these composites as potential candidates as novel materials with enhanced properties following an approach of circular economy.

| S-EPMC8838854 | biostudies-literature

Fatigue Performance of ABS Specimens Obtained by Fused Filament Fabrication.

Project description:In this paper, the fatigue response of fused filament fabrication (FFF) Acrylonitrile butadiene styrene (ABS) parts is studied. Different building parameters (layer height, nozzle diameter, infill density, and printing speed) were chosen to study their influence on the lifespan of cylindrical specimens according to a design of experiments (DOE) using the Taguchi methodology. The same DOE was applied on two different specimen sets using two different infill patterns-rectilinear and honeycomb. The results show that the infill density is the most important parameter for both of the studied patterns. The specimens manufactured with the honeycomb pattern show longer lifespans. The best parameter set associated to that infill was chosen for a second experimental phase, in which the specimens were tested under different maximum bending stresses so as to construct the Wöhler curve associated with this 3D printing configuration. The results of this study are useful to design and manufacture ABS end-use parts that are expected to work under oscillating periodic loads.

| S-EPMC6317007 | biostudies-other

Fused Filament Fabrication and Computer Numerical Control Milling in Cultural Heritage Conservation.

Project description:This paper reports a comparison between the advantages and disadvantages of fused filament fabrication (FFF) and computer numerical control (CNC) milling, when applied to a specific case of conservation of cultural heritage: the reproduction of four missing columns of a 17th-century tabernacle. To make the replica prototypes, European pine wood (the original material) was used for CNC milling, while polyethylene terephthalate glycol (PETG) was used for FFF printing. Neat materials were chemically and structurally characterized (FTIR, XRD, DSC, contact angle measurement, colorimetry, and bending tests) before and after artificial aging, in order to study their durability. The comparison showed that although both materials are subject to a decrease in crystallinity (an increase in amorphous bands in XRD diffractograms) and mechanical performance with aging, these characteristics are less evident in PETG (E = 1.13 ± 0.01 GPa and σ = 60.20 ± 2.11 MPa after aging), which retains water repellent (ca = 95.96 ± 5.56°) and colorimetric (∆E = 2.6) properties. Furthermore, the increase in flexural strain (%) in pine wood, from 3.71 ± 0.03% to 4.11 ± 0.02%, makes it not suitable for purpose. Both techniques were then used to produce the same column, showing that for this specific application CNC milling is quicker than FFF, but, at the same time, it is also much more expensive and produces a huge amount of waste material compared to FFF printing. Based on these results, it was assessed that FFF is more suitable for the replication of the specific column. For this reason, only the 3D-printed PETG column was used for the subsequent conservative restoration.

| S-EPMC10141658 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data