Alternately Dipping Method to Prepare Graphene Fiber Electrodes for Ultra-high-Capacitance Fiber Supercapacitors.

ABSTRACT: Flexible fiber supercapacitors are promising candidate for power supply of wearable electronics. Fabrication of high-performance fibers is in progress yet challenging. The currently available graphene fibers made from wet-spinning or electro-deposition technologies are far away from practical applications due to their unsatisfactory capacitance. Here we report a facile alternately dipping (AD) method to coat graphene on wire-like substrates. The excellent mechanical properties of the substrate with greatly diverse choices can be carried over to the fiber supercapacitors. Under such guideline, the graphene fiber with a titanium core made by our AD method (AD:Ti@RGO) shows an ultra-high specific capacitance of up to 1,722.1 mF cm^-2, which is ∼1,000 times that of wet-spinning- and electro-deposition-fabricated neat graphene fibers and presents the highest specific capacitance to date. With excellent mechanical properties and striking electrochemical performances, the AD:Ti@RGO-based supercapacitors light the path to the next-generation technologies for wearable devices.

SUBMITTER: Qu G

PROVIDER: S-EPMC7416342 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Ultra-Fine Ruthenium Oxide Quantum Dots/Reduced Graphene Oxide Composite as Electrodes for High-Performance Supercapacitors.

Project description:This study synthesized ultra-fine nanometer-scaled ruthenium oxide (RuO2) quantum dots (QDs) on reduced graphene oxide (rGO) surface by a facile and rapid microwave-assisted hydrothermal approach. Benefiting from the synergistic effect of RuO2 and rGO, RuO2/rGO nanocomposite electrodes showed ultra-high capacitive performance. The impact of different RuO2 loadings in RuO2/rGO nanocomposite on their electrochemical performance was investigated by various characterizations. The composite RG-2 with 38 wt.% RuO2 loadings exhibited a specific capacitance of 1120 F g-1 at 1 A g-1. In addition, it has an excellent capacity retention rate of 84 % from 1A g-1 to 10 A g-1, and excellent cycling stability of 89% retention after 10,000 cycles, indicating fast ion-involved redox reactions on the nanocomposite surfaces. These results illustrate that RuO2/rGO composites prepared by this facile process can be an ideal candidate electrode for high-performance supercapacitors.

| S-EPMC9000793 | biostudies-literature

An Ultra-microporous Carbon Material Boosting Integrated Capacitance for Cellulose-Based Supercapacitors.

Project description:A breakthrough in advancing power density and stability of carbon-based supercapacitors is trapped by inefficient pore structures of electrode materials. Herein, an ultra-microporous carbon with ultrahigh integrated capacitance fabricated via one-step carbonization/activation of dense bacterial cellulose (BC) precursor followed by nitrogen/sulfur dual doping is reported. The microporous carbon possesses highly concentrated micropores (~ 2 nm) and a considerable amount of sub-micropores (< 1 nm). The unique porous structure provides high specific surface area (1554 m2 g-1) and packing density (1.18 g cm-3). The synergistic effects from the particular porous structure and optimal doping effectively enhance ion storage and ion/electron transport. As a result, the remarkable specific capacitances, including ultrahigh gravimetric and volumetric capacitances (430 F g-1 and 507 F cm-3 at 0.5 A g-1), and excellent cycling and rate stability even at a high current density of 10 A g-1 (327 F g-1 and 385 F cm-3) are realized. Via compositing the porous carbon and BC skeleton, a robust all-solid-state cellulose-based supercapacitor presents super high areal energy density (~ 0.77 mWh cm-2), volumetric energy density (~ 17.8 W L-1), and excellent cyclic stability.

| S-EPMC7770663 | biostudies-literature

Towards ultrahigh volumetric capacitance: graphene derived highly dense but porous carbons for supercapacitors.

Project description:A small volumetric capacitance resulting from a low packing density is one of the major limitations for novel nanocarbons finding real applications in commercial electrochemical energy storage devices. Here we report a carbon with a density of 1.58 g cm(-3), 70% of the density of graphite, constructed of compactly interlinked graphene nanosheets, which is produced by an evaporation-induced drying of a graphene hydrogel. Such a carbon balances two seemingly incompatible characteristics: a porous microstructure and a high density, and therefore has a volumetric capacitance for electrochemical capacitors (ECs) up to 376 F cm(-3), which is the highest value so far reported for carbon materials in an aqueous electrolyte. More promising, the carbon is conductive and moldable, and thus could be used directly as a well-shaped electrode sheet for the assembly of a supercapacitor device free of any additives, resulting in device-level high energy density ECs.

| S-EPMC3797987 | biostudies-literature

Systematic Design of Polypyrrole/Carbon Fiber Electrodes for Efficient Flexible Fiber-Type Solid-State Supercapacitors.

Project description:Fiber-type supercapacitors (FSC) have attracted much attention as efficient energy storage devices for soft electronics. This study proposes the synthesis of polypyrrole (PPy) on carbon fiber (CF) using electropolymerization as the energy storage electrode for FSC. Effects of the electrolyte, applied current, and time of electropolymerization for synthesizing PPy on CF are investigated. The configuration of the electrochemical system is also studied to better understand the electropolymerization of PPy. The highest specific capacitance (CM) of 308.2 F/g are obtained for the PPy electrode prepared using 0.5 M pyrrole and 0.3 M NaClO4 as the electrolyte at 40 mA for 20 min. The FSC assembled with PPy electrodes and the polyvinyl alcohol/H3PO4 gel electrolyte shows a CM value of 30 F/g and the energy density of 5.87 Wh/kg at the power density of 60.0 W/kg. Excellent cycling stability with CM retention of 70% and Coulombic efficiency higher than 98% in 3000 times charge/discharge process, and the good bending capability with CM retention of 153% and 148%, respectively, under the bending angle of 180° and the bending times of 600 are achieved. This work gives deeper understanding of electropolymerization and provides recipes for fabricating an efficient PPy electrode for soft energy storage devices.

| S-EPMC7075248 | biostudies-literature

Hydrothermal synthesis of nanostructured graphene/polyaniline composites as high-capacitance electrode materials for supercapacitors.

Project description:As known to all, hydrothermal synthesis is a powerful technique for preparing inorganic and organic materials or composites with different architectures. In this reports, by controlling hydrothermal conditions, nanostructured polyaniline (PANi) in different morphologies were composited with graphene sheets (GNS) and used as electrode materials of supercapacitors. Specifically, ultrathin PANi layers with total thickness of 10-20 nm are uniformly composited with GNS by a two-step hydrothermal-assistant chemical oxidation polymerization process; while PANi nanofibers with diameter of 50~100 nm are obtained by a one-step direct hydrothermal process. Benefitting from the ultrathin layer and porous structure, the sheet-like GNS/PANi composites can deliver specific capacitances of 532.3 to 304.9 F/g at scan rates of 2 to 50 mV/s. And also, this active material showed very good stability with capacitance retention as high as ~99.6% at scan rate of 50 mV/s, indicating a great potential for using in supercapacitors. Furthermore, the effects of hydrothermal temperatures on the electrochemical performances were systematically studied and discussed.

| S-EPMC5349513 | biostudies-literature

All-lignin converted graphene quantum dot/graphene nanosheet hetero-junction for high-rate and boosted specific capacitance supercapacitors.

Project description:The high value-added conversion of biomass lignin has been paramount in the field of lignin utilization, especially for high performance energy conversion and storage devices. A majority of lignin-based supercapacitors generally exhibit inferior electrochemical performance with low capacitance and slow diffusion kinetics due to the poor interfacial compatibility, low conductivity, and uncontrollable morphology. Herein, we designed all-lignin converted graphene quantum dot and graphene sheet (GQD/Gr) hetero-junction for simultaneous fast charging and boosted specific capacitance. The conversion from lignin to GQDs and then refusion into graphene allows the in situ growth of GQDs on graphene, endowing good interfacial compatibility with the GQD/Gr hetero-junction. Furthermore, both GQDs and graphene sheets exhibit highly crystalline structure with obvious graphene lattice, giving GQDs/Gr good conductivity. GQDs play an additive role for avoiding stacks and agglomerates between graphene layers, which endow the assembled GQDs/Gr with massive electron capacitive sites and more hierarchical channels. Therefore, the GQD/Gr hetero-junction gives rise to a high specific capacitance of 404.6 F g-1 and a short charging time constant (τ 0) of 0.3 s, 2.5 times higher and 7.5 times faster than that of the unmodified lignin electrode with 162 F g-1 and 2.3 s, respectively. This proposed strategy could offer the opportunity to unblock the critical roadblocks for a superior electrochemical performance lignin-based supercapacitor by composing a 0D/2D GQD/Gr hetero-junction system and also paves a bright way for the high-value industrial lignin conversion into cheap, scalable, and high-performance electrochemical energy devices.

| S-EPMC9418623 | biostudies-literature

Electrochemical Method To Prepare Graphene Quantum Dots and Graphene Oxide Quantum Dots.

Project description:In this study, we present the preparation of graphene quantum dots (GQDs) and graphene oxide quantum dots (GOQDs). GQDs/GOQDs are prepared by an easy electrochemical exfoliation method, in which two graphite rods are used as electrodes. The electrolyte used is a combination of citric acid and alkali hydroxide in water. Four types of quantum dots, GQD1-GQD4, are prepared by varying alkali hydroxide concentration in the electrolyte, while keeping the citric acid concentration fixed. Variation of alkali hydroxide concentration in the electrolyte results in the production of GOQDs. Balanced reaction of citric acid and alkali hydroxide results in the production of GQDs (GQD3). However, three variations in alkali hydroxide concentration result in GOQDs (GQD1, GQD2, and GQD4). GOQDs show tunable oxygen functional groups, which are confirmed by X-ray photoelectron spectroscopy. GQDs/GOQDs show absorption in the UV region and show excitation-dependent photoluminescence behavior. The obtained average size is 2-3 nm, as revealed by transmission electron microscopy. X-ray diffraction peak at around 10° and broad D band peak at 1350 cm-1 in Raman spectra confirm the presence of oxygen-rich functional groups on the surface of GOQDs. These GQDs and GOQDs show blue to green luminescence under 365 nm UV irradiation.

| S-EPMC6645081 | biostudies-literature

Platinized graphene fiber electrodes uncover direct spleen-vagus communication.

Project description:Neural interfacing nerve fascicles along the splenic neurovascular plexus (SNVP) is needed to better understand the spleen physiology, and for selective neuromodulation of this major organ. However, their small size and anatomical location have proven to be a significant challenge. Here, we use a reduced liquid crystalline graphene oxide (rGO) fiber coated with platinum (Pt) as a super-flexible suture-like electrode to interface multiple SNVP. The Pt-rGO fibers work as a handover knot electrodes over the small SNVP, allowing sensitive recording from four splenic nerve terminal branches (SN 1-4), to uncover differential activity and axon composition among them. Here, the asymmetric defasciculation of the SN branches is revealed by electron microscopy, and the functional compartmentalization in spleen innervation is evidenced in response to hypoxia and pharmacological modulation of mean arterial pressure. We demonstrate that electrical stimulation of cervical and sub-diaphragmatic vagus nerve (VN), evokes activity in a subset of SN terminal branches, providing evidence for a direct VN control over the spleen. This notion is supported by adenoviral tract-tracing of SN branches, revealing an unconventional direct brain-spleen projection. High-performance Pt-rGO fiber electrodes, may be used for the fine neural modulation of other small neurovascular plexus at the point of entry of major organs as a bioelectronic medical alternative.

| S-EPMC8448843 | biostudies-literature

Facile preparation of flexible binder-free graphene electrodes for high-performance supercapacitors.

Project description:A facile two-step strategy to prepare flexible graphene electrodes has been developed for supercapacitors using thermal reduction of graphene oxide (GO) and thermally reduced graphene oxide (TRGO) composite films. The tunable porous structure of the GO/TRGO film provided channels to release the high pressure generated by CO2 gas. The graphene electrode obtained from reduced-GO/TRGO (1 : 1 in mass ratio) film showed great flexibility and high film density (0.52 g cm-3). Using the EMI-BF4 electrolyte with a working voltage of 3.7 V, the as-fabricated free-standing reduced-GO/TRGO (1 : 1) film achieved a great gravimetric capacitance of 180 F g-1 (delivering a gravimetric energy density of 85.6 W h kg-1), a volumetric capacitance of 94 F cm-3 (delivering a volumetric energy density of 44.7 W h L-1), and a 92% retention after 10 000 charge/discharge cycles. In addition, the solid state flexible supercapacitor with the free-standing reduced-GO/TRGO (1 : 1) film as the electrodes and the EMI-BF4/poly (vinylidene fluoride hexafluopropylene) (PVDF-HFP) gel as the electrolyte also demonstrated a high gravimetric capacitance of 146 F g-1 with excellent mechanical flexibility, bending stability, and electrochemical stability. The strategy developed in this study provides great potentials for the synthesis of flexible graphene electrodes for supercapacitors.

| S-EPMC9039804 | biostudies-literature

N/O Co-doped Porous Carbons Derived from Coal Tar Pitch for Ultra-high Specific Capacitance Supercapacitors

Project description:In this paper, a

| S-EPMC9281300 | biostudies-literature